Experimental Study on Paraffin Emulsion PhaseChange Foamed Concrete

Abstract

Abstract: Aqueous dispersion emulsion of phase change paraffin was prepared and mixed into chemical foaming process to prepare phase change foamed concrete. The dry density, compressive strength, volumetric water absorption, thermal insulation property, phase change stability and microcosmic state of phase change foamed concrete were tested by experiments. The results show that the phase change paraffin emulsion has adverse effects on the chemical foaming process and compressive strength of material. Phase change foamed concrete can be stably made when the amount of phase change paraffin emulsion is less than 40% of dry powder in quality. Phase change paraffin is dispersed in foamed concrete matrix in the form of tiny particles. The compressive strength of foamed concrete decreases by 35%~47%, and the volumetric water absorption decreases by 19%~30% when the phase emulsion is 40% of dry powder. Phase change paraffin can improve the thermal insulation property of foamed concrete in a certain temperature range. The phase change stability is good, and the paraffin is difficult to leak.

Key words: foam concrete, phase change material, paraffin emulsion, chemical foaming, thermal insulation property

CLC Number:

TU55⁺1.33

CHEN Zhichun, GUO Liping, LI Yingquan, CHEN Jiayu, YANG Donglei. Experimental Study on Paraffin Emulsion PhaseChange Foamed Concrete[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(5): 1623-1629.

References

[1] 李应权, 王明轩, 扈士凯, 等. 我国泡沫混凝土行业新进展[J]. 混凝土世界, 2014(4): 10-27.
LI Y Q, WANG M X, HU S K, et al. New progress of foam concrete industry in China[J]. China Concrete, 2014(4): 10-27 (in Chinese).
[2] 陈志纯, 李应权, 扈士凯, 等. 化学发泡泡沫混凝土材料性能的影响因素[J]. 徐州工程学院学报(自然科学版), 2014, 29(2): 63-69.
CHEN Z C, LI Y Q, HU S K, et al. Research on factors influencing the material properties of chemical foamed concrete[J]. Journal of Xuzhou Institute of Technology (Natural Sciences Edition), 2014, 29(2): 63-69 (in Chinese).
[3] CABEZA L F, CASTELL A, BARRENECHE C, et al. Materials used as PCM in thermal energy storage in buildings: a review[J]. Renewable and Sustainable Energy Reviews, 2011, 15(3): 1675-1695.
[4] EHID R, FLEISCHER A S. Development and characterization of paraffin-based shape stabilized energy storage materials[J]. Energy Conversion and Management, 2012, 53(1): 84-91.
[5] 邓燕. 复合相变材料制备及建筑隔热性能研究[D]. 广州: 广州大学, 2019: 6-8.
DENG Y. Preparation composite phase change materials and study on building thermal insulation performance[D]. Guangzhou: Guangzhou University, 2019: 6-8 (in Chinese).
[6] 王晴, 吴陶俊, 丁兆洋, 等. 三元复合石蜡/玻化微珠相变储能砂浆的制备[J]. 硅酸盐通报, 2015, 34(3): 626-630.
WANG Q, WU T J, DING Z Y, et al. Preparation of ternary composite paraffin/vitrified microsphere phase change storage mortar[J]. Bulletin of the Chinese Ceramic Society, 2015, 34(3): 626-630 (in Chinese).
[7] 杨保平, 席满意, 崔锦峰, 等. 相变微胶囊的制备及其在涂料中的应用研究[J]. 当代化工, 2014, 43(1): 32-35.
YANG B P, XI M Y, CUI J F, et al. Preparation of phase change microcapsules and its application in coating[J]. Contemporary Chemical Industry, 2014, 43(1): 32-35 (in Chinese).
[8] 王磊. 改性膨润土复合相变储能墙板制备及特性研究[J]. 新型建筑材料, 2018, 45(5): 96-99+120.
WANG L. Preparation and properties of modified bentonite composite phase change energy storage wallboard[J]. New Building Materials, 2018, 45(5): 96-99+120 (in Chinese).
[9] 赵倩, 严中俊, 秦迪, 等. 相变蓄能冷暖辐射地板系统热响应特性实验研究[J]. 建筑科学, 2020, 36(8): 21-27.
ZHAO Q, YAN Z J, QIN D, et al. An experimental study on thermal response of a PCM heating and cooling radiant floor system[J]. Building Science, 2020, 36(8): 21-27 (in Chinese).
[10] 刘福战, 王宇. 建筑节能用相变混凝土的试验研究[J]. 粉煤灰综合利用, 2011, 24(3): 32-35.
LIU F Z, WANG Y. Experimental study on phase change concrete in building energy-saving[J]. Fly Ash Comprehensive Utilization, 2011, 24(3): 32-35 (in Chinese).
[11] 沈永亮, 刘淑丽, 胡鹤蓝, 等. 陶粒/石蜡定型相变材料混凝土的制备及热性能研究[J]. 中国建筑金属结构, 2020(2): 54-57.
SHEN Y L, LIU S L, HU H L, et al. Preparation and thermal properties of ceramsite/paraffin shaped phase change material concrete[J]. China Construction Metal Structure, 2020(2): 54-57 (in Chinese).
[12] 林素菊. 相变储能混凝土比热容的测定研究[J]. 山西建筑, 2012, 38(15): 98-99.
LIN S J. Research on measurement of phase-changing energy-storing concrete’s specific heat capacity[J]. Shanxi Architecture, 2012, 38(15): 98-99 (in Chinese).
[13] 史巍, 侯景鹏, 张雄. 石蜡相变控温大体积混凝土性能[J]. 建筑材料学报, 2010, 13(3): 414-417.
SHI W, HOU J P, ZHANG X. Properties of paraffin phase-change-material(PCM) mass concrete for temperature control[J]. Journal of Building Materials, 2010, 13(3): 414-417 (in Chinese).
[14] 马娟娟. 石蜡相变混凝土控温机理及其综合性能研究[D]. 西安: 西京学院, 2020: 82-83.
MA J J. Study on temperature control mechanism and performance of paraffin phase change concrete[D]. Xi’an: Xijing University, 2020: 82-83 (in Chinese).
[15] 肖力光, 李冰. 相变材料在建筑节能领域的应用及研究[J]. 北方建筑, 2019, 4(4): 51-55.
XIAO L G, LI B. Research on phase change materials in the field of building energy conservation[J]. Northern Architecture, 2019, 4(4): 51-55 (in Chinese).
[16] LIM M K, ENKHBOLD O, KIM Y H, et al. An experimental study on the development of lightweight concrete using the PCM[J]. KIEAE Journal, 2014, 14(4): 133-138.
[17] 王晴, 丁兆洋, 邱琳格, 等. 一种相变储能相变混凝土及制备方法: CN102503319A[P]. 2012-06-20.
WANG Q, DING Z Y, QIU L G, et al. A phase change energy storage phase change concrete and preparation method: CN102503319A[P]. 2012-06-20 (in Chinese).
[18] 熊吉如, 朱雪峰, 陶婷婷. 一种相变储热调温泡沫混凝土: CN106518142A[P]. 2017-03-22.
XIONG J R, ZHU X F, TAO T T. A kind of phase change foam concrete for heat storage and temperature control: CN106518142A[P]. 2017-03-22 (in Chinese).
[19] QU Y, CHEN J Y, LIU L F, et al. Study on properties of phase change foam concrete block mixed with paraffin/fumed silica composite phase change material[J]. Renewable Energy, 2020, 150: 1127-1135.
[20] 迟碧川, 李应全, 扈士凯, 等. 相变储能调温泡沫混凝土及其制备方法: CN104649632A[P]. 2015-05-27.
CHI B C, LI Y Q, HU S K, et al. Phase change energy storage temperature control foamed concrete and its preparation method: CN104649632A[P]. 2015-05-27 (in Chinese).
[21] 叶伟. 一种相变自保温的陶粒泡沫混凝土的生产方法: CN108017358A[P]. 2018-05-11.
YE W. Production method of phase change self-insulation ceramide foam concrete: CN108017358A[P]. 2018-05-11 (in Chinese).
[22] SHARMA A, TYAGI V V, CHEN C R, et al. Review on thermal energy storage with phase change materials and applications[J]. Renewable and Sustainable Energy Reviews, 2009, 13(2): 318-345.