Effect of Plastic Expansion Agent on Performance of Ultra High Performance Grouting Materials for Offshore Wind Power

Abstract

Abstract: C125 ultra high performance grouting materials for offshore wind power were prepared by using azo compound plastic expansion agent (PEA1) and nitroso compound plastic expansion agent (PEA2), respectively. The effects of the type and content of plastic expansion agent on the fluidity, expansion rate, compressive strength, electric flux and pore structure distribution of C125 ultra high performance grouting materials for offshore wind power were studied. The results show that with the increase of plastic expansion agent content, the fluidity of grouting materials increases first and then decreases, the compressive strength decreases gradually, and the vertical expansion rate and electric flux increase gradually. Compared with PEA2, PEA1 has greater influence on the fluidity, compressive strength, vertical expansion rate and electric flux of grouting materials at the same content. The total void fraction, average pore diameter and large pore proportion of grouting materials with PEA1 increase more obviously than that of grouting materials with PEA2 at the same content.

Key words: offshore wind power, grouting material, plastic expansion agent, fluidity, expansion rate, compressive strength, pore structure, electric flux

CLC Number:

TU521.1

SONG Putao, WANG Jing, LENG Faguang, XIA Jingliang, CHEN Xi, ZHANG Yaochen. Effect of Plastic Expansion Agent on Performance of Ultra High Performance Grouting Materials for Offshore Wind Power[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(5): 1608-1614.

References

[1] 丁成. 超高性能海上风电灌浆料试验研究[D]. 广州: 华南理工大学, 2021.
DING C. Experimental research on ultra-high performance grouting for offshore wind power[D]. Guangzhou: South China University of Technology, 2021 (in Chinese).
[2] 汪冬冬, 张悦然, 孙烜, 等. 海上风电导管架灌浆料产品开发与工程应用研究[J]. 海洋开发与管理, 2018, 35(s1): 27-33.
WANG D D, ZHANG Y R, SUN X, et al. Research on development and engineering application of grouting material for offshore wind power jacket[J]. Ocean Development and Management, 2018, 35(s1): 27-33 (in Chinese).
[3] 游先辉. 海上风电基础结构灌浆连接段研究综述[J]. 海峡科学, 2022(1): 67-74.
YOU X H. Summary of research on grouting connection section of offshore wind power infrastructure[J]. Straits Science, 2022(1): 67-74 (in Chinese).
[4] 元国凯, 汤东升, 刘晋超, 等. 海上风电机组基础灌浆技术应用与发展[J]. 南方能源建设, 2017, 4(1): 10-17.
YUAN G K, TANG D S, LIU J C, et al. Grouting technology application and development in offshore wind farm[J]. Southern Energy Construction, 2017, 4(1): 10-17 (in Chinese).
[5] 徐元超, 赵哲伦, 涂传彬. 海上升压站基础导管架安装及灌浆质量控制: 以江苏大丰300 MW海上风电项目为例[J]. 人民长江, 2020, 51(s2): 209-212.
XU Y C, ZHAO Z L, TU C B. Installation andquality control of foundation grouting for offshore booster station grouting: case of 300 MW offshore wind power project in Dafeng County, Jiangsu Province[J]. Yangtze River, 2020, 51(s2): 209-212 (in Chinese).
[6] 杨方奇. 低粘超高性能灌浆料的制备及性能研究[D]. 广州: 华南理工大学, 2021.
YANG F Q. Study on preparation and properties of low viscosity and ultra-high performance grouting material[D]. Guangzhou: South China University of Technology, 2021 (in Chinese).
[7] 吴世芳, 付弯弯, 任皓, 等. 套筒灌浆料性能影响因素的研究[J]. 武汉轻工大学学报, 2022, 41(1): 58-63.
WU S F, FU W W, REN H, et al. Study on influencing factors of performance of sleeve grouting material[J]. Journal of Wuhan Polytechnic University, 2022, 41(1): 58-63 (in Chinese).
[8] 袁伟, 田晓航, 杨辉, 等. 超细矿物掺合料对超细灌浆料性能的影响[J]. 混凝土世界, 2022(1): 65-68.
YUAN W, TIAN X H, YANG H, et al. Effect of superfine mineral admixture on superfine grouting material[J]. China Concrete, 2022(1): 65-68 (in Chinese).
[9] 蒋涛, 廖开星, 潘从玲, 等. 高性能水泥基灌浆料的制备及研究[J]. 混凝土与水泥制品, 2021(12): 6-11.
JIANG T, LIAO K X, PAN C L, et al. Study on preparation and application of high performance cement-based grouting material[J]. China Concrete and Cement Products, 2021(12): 6-11 (in Chinese).
[10] 王均伟. 一种高性能风电机组基础灌浆料配制试验研究[D]. 济南: 山东建筑大学, 2021.
WANG J W. Experimental study on preparation of a high-performance foundation grouting material for wind turbine[D]. Jinan: Shandong Jianzhu University, 2021 (in Chinese).
[11] 陈涛. 高性能水泥基灌浆料制备技术、力学性能与微观机理研究[D]. 广州: 广州大学, 2020.
CHEN T. Study on preparation technology, mechanical properties and micromechanism of high performance cement-based grouting[D]. Guangzhou: Guangzhou University, 2020 (in Chinese).
[12] 汪刘顺. 高性能铁尾矿砂水泥基灌浆料耐久性及微观结构试验研究[D]. 合肥: 合肥工业大学, 2012.
WANG L S. Experimental study on durability and microstructure of high-performance iron-mine-tailings cement-based grouting material[D]. Hefei: Hefei University of Technology, 2012 (in Chinese).
[13] 朱清利. 铜尾矿砂对高强灌浆料性能的影响[J]. 新型建筑材料, 2022, 49(3): 87-90.
ZHU Q L. Effects of copper tailings sand on properties of high strength cement grouts[J]. New Building Materials, 2022, 49(3): 87-90 (in Chinese).
[14] 程平阶, 宋小婧, 李北星, 等. 塑性膨胀剂对预应力孔道压浆料体积变形与亚微观结构的影响[J]. 硅酸盐通报, 2014, 33(6): 1329-1335.
CHENG P J, SONG X J, LI B X, et al. Effect of plastic expansion agent on the volume deformation and submicroscopic structure of pre-stressed duct grouting materials[J]. Bulletin of the Chinese Ceramic Society, 2014, 33(6): 1329-1335 (in Chinese).
[15] 王冬, 祝烨然, 陈国新, 等. HLC-PE水泥基灌浆材料有机塑性膨胀剂的研究[J]. 混凝土, 2012(11): 67-70.
WANG D, ZHU Y R, CHEN G X, et al. Study on HLC-PE organic plasticizing expanding agent of cementitious grouting material[J]. Concrete, 2012(11): 67-70 (in Chinese).
[16] 胡亮, 徐智勇, 段双, 等. 孔道压浆料专用塑性膨胀剂的试验研究[J]. 新型建筑材料, 2011, 38(10): 18-20.
HU L, XU Z Y, DUAN S, et al. The experimental study of special plastic expansive agent used in duct grouts[J]. New Building Materials, 2011, 38(10): 18-20 (in Chinese).
[17] 刘云霄, 茌引引, 田威, 等. 不同膨胀剂对水泥基灌浆料性能的影响[J]. 建筑材料学报, 2022, 25(3): 307-313.
LIU Y X, CHI Y Y, TIAN W, et al. Effect of different expanders on properties of cement based grouting material[J]. Journal of Building Materials, 2022, 25(3): 307-313 (in Chinese).
[18] 张亨. 发泡剂研究进展[J]. 塑料助剂, 2001(4): 1-6+10.
ZHANG H. Research progress of foaming agent[J]. Plastic Additives, 2001(4): 1-6+10 (in Chinese).
[19] 闻庆祥. 有机发泡剂品种开发现状及发展趋向[J]. 石油化工动态, 1994, 2(6): 30-33.
WEN Q X. Development status and development trend of organic foaming agent varieties[J]. Petrochemical Industry Trends, 1994, 2(6): 30-33 (in Chinese).