Effect of Ultraviolet Pretreatment on Early Carbonation Properties of Portland Cement Paste

Abstract

Abstract: Pretreatment is the key step in carbon curing system, which is very important for cement paste carbonization. In this study, the cement specimens before carbonation were pretreated by ultraviolet (UV) irradiation and compared with standard pretreatment, and the carbonation depth, compressive strength, CO₂ absorption and structural morphological changes of hydration products were tested and analyzed. The results show that the mass loss of cement specimens after UV pretreatment is 5.3 times as standard curing pretreatment. After accelerated carbonization, the carbonization depth increases by 2.4 times, the mass increases by 4.5 times, the early compressive strength increases by 18.9%, and the CO₂ absorption increases by 0.25%. It is found that UV pretreatment increases the formation of silica gel (Q³+Q⁴) content with high degree of polymerization of carbonized cement specimens. Therefore, UV pretreatment can significantly accelerate the water loss and decalcification of the specimen, which has a significant enhancement effect on the carbonization process of cement specimens.

Key words: Portland cement, CO₂ curing, UV pretreatment, standard curing pretreatment, carbonization depth, compressive strength

CLC Number:

TU502

SHI Xiaochen, SHUI Zhonghe, LI Haoyuan, XIAO Xunguang, SUN Tao, WANG Leichong. Effect of Ultraviolet Pretreatment on Early Carbonation Properties of Portland Cement Paste[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(3): 786-792.

References

[1] LU B, DRISSI S, LIU J H, et al. Effect of temperature on CO₂ curing, compressive strength and microstructure of cement paste[J]. Cement and Concrete Research, 2022, 157: 106827.
[2] BAE J H, KIM S, AMR I T, et al. Evaluation of physicochemical properties and environmental impact of environmentally amicable Portland cement/metakaolin bricks exposed to humid or CO₂ curing condition[J]. Journal of Building Engineering, 2022, 47: 103831.
[3] WINNEFELD F, LEEMANN A, GERMAN A, et al. CO₂ storage in cement and concrete by mineral carbonation[J]. Current Opinion in Green and Sustainable Chemistry, 2022, 38: 100672.
[4] QI C C, XU X H, CHEN J, et al. Ab initio calculations of CO₂ adsorption on β-C₂S(100) and M₃-C₃S(001) surfaces: an exploration of early CO₂ sequestration pathways[J]. Environmental Research, 2022, 215: 114412.
[5] ZHANG K, YIO M, WONG H, et al. Real-time monitoring of carbonation of hardened cement pastes using Raman microscopy[J]. Journal of Microscopy, 2022, 286(2): 126-133.
[6] LU B, HE P P, LIU J H, et al. Microstructure of Portland cement paste subjected to different CO₂ concentrations and further water curing[J]. Journal of CO₂ Utilization, 2021, 53: 101714.
[7] PENG Y Z, MENG X, SONG F J, et al. Experimental study on the corrosion characteristics of concrete exposed to acid water containing aggressive carbon dioxide and sodium sulfate[J]. Construction and Building Materials, 2022, 321: 126397.
[8] ZHANG D, SHAO Y X. Early age carbonation curing for precast reinforced concretes[J]. Construction and Building Materials, 2016, 113: 134-143.
[9] ZHAN B J, POON C S, LIU Q, et al. Experimental study on CO₂ curing for enhancement of recycled aggregate properties[J]. Construction and Building Materials, 2014, 67: 3-7.
[10] PAN G H, ZHAN M M, FU M H, et al. Effect of CO₂ curing on demolition recycled fine aggregates enhanced by calcium hydroxide pre-soaking[J]. Construction and Building Materials, 2017, 154: 810-818.
[11] El-HASSAN H, SHAO Y, GHOULEH Z. Effect of initial curing on carbonation of lightweight concrete masonry units[J]. ACI Materials Journal, 2013, 110(4): 441-450.
[12] DE CEUKELAIRE L, VAN NIEUWENBURG D. Accelerated carbonation of a blast-furnace cement concrete[J]. Cement and Concrete Research, 1993, 23(2): 442-452.
[13] MO L W, PANESAR D K. Effects of accelerated carbonation on the microstructure of Portland cement pastes containing reactive MgO[J]. Cement and Concrete Research, 2012, 42(6): 769-777.
[14] HE P P, SHI C J, TU Z J, et al. Effect of further water curing on compressive strength and microstructure of CO₂-cured concrete[J]. Cement and Concrete Composites, 2016, 72: 80-88.
[15] ZHANG D, SHAO Y X. Surface scaling of CO₂-cured concrete exposed to freeze-thaw cycles[J]. Journal of CO₂ Utilization, 2018, 27: 137-144.
[16] ZHAN B J, XUAN D X, POON C S, et al. Effect of curing parameters on CO₂ curing of concrete blocks containing recycled aggregates[J]. Cement and Concrete Composites, 2016, 71: 122-130.
[17] WANG H X, LONG G C, XIE Y J, et al. Effects of intense ultraviolet irradiation on drying shrinkage and microstructural characteristics of cement mortar[J]. Construction and Building Materials, 2022, 347: 128513.
[18] 水中和, 余杰, 余睿, 等. 紫外线对硬化水泥浆表层物理化学性质的影响[J]. 武汉理工大学学报, 2018, 40(5): 14-18.
SHUI Z H, YU J, YU R, et al. Effects of ultraviolet radiation on the surface of hardened cement paste of the physical and chemical properties[J]. Journal of Wuhan University of Technology, 2018, 40(5): 14-18 (in Chinese).
[19] QIN L, GAO X J, CHEN T F. Influence of mineral admixtures on carbonation curing of cement paste[J]. Construction and Building Materials, 2019, 212: 653-662.
[20] LI L, POON C S, XIAO J Z, et al. Effect of carbonated recycled coarse aggregate on the dynamic compressive behavior of recycled aggregate concrete[J]. Construction and Building Materials, 2017, 151: 52-62.