Preparation and Mechanical Properties of Ultra-High Temperature Rare Earth Boride (Y1-xYbx)B6

Abstract

Abstract: The structural instability of yttrium hexaboride (YB₆) at high temperature limits its application in the ultra-high temperature field. By introducing Yb element, high-temperature stable (Y_1-xYb_x)B₆ solid solution can be formed. In this paper, (Y_0.5Yb_0.5)B₆ powders were prepared via boron/carbon thermal reduction method using (Y_0.5Yb_0.5)₂O₃ and B₄C as raw materials, and the ceramics were densified by pressureless sintering. The crystal structure, microstructure and mechanical properties were investigated based on the experimental results and density functional theory calculations. The results show that the (Y_0.5Yb_0.5)B₆ powders synthesized at 1 650 ℃ have the highest purity when B₄C is excess by 6.25%. (Y_0.5Yb_0.5)B₆ ceramics have a relative density of 95.80% after pressureless sintered at 2 000 ℃, but the grains are coarse with the average size of (80.71±35.51) μm. The relative density, grain size, hardness and fracture toughness of ceramics obtained by two-step sinteringare 95.47%,(14.54±6.31) μm, (14.53±1.37) GPa and (2.81±0.34) MPa·m^1/2, respectively. The fracture morphology of ceramics is very similar to that of typical high damage tolerance ceramics Ti₃SiC₂ and Hf₃AlN, which indicates that (Y_0.5Yb_0.5)B₆ has good damage tolerance and is expected to improve the toughness and ductility of ultra-high temperature ceramics.

Key words: yttrium boride, ultra-high temperature ceramics, boron/carbon thermal reduction method, first principle calculation, damage tolerance

CLC Number:

TQ174

LIU Hulin, HOU Huihui, YU Chenglong, MAN Zhenyong, DANG Fengzhen, XUE Yunlong, WU Yuanting. Preparation and Mechanical Properties of Ultra-High Temperature Rare Earth Boride (Y_1-xYb_x)B₆[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(1): 276-286.

References

[1] DING L P, TIANDONG Y H, SHAO P, et al. Crystal structures, phase stabilities, electronic properties, and hardness of yttrium borides: new insight from first-principles calculations[J]. The Journal of Physical Chemistry Letters, 2021, 12(22): 5423-5429.
[2] KOVÁČOVÁ Z, OROVČÍK L’, SEDLÁČEK J, et al. The effect of YB₄ addition in ZrB₂-SiC composites on the mechanical properties and oxidation performance tested up to 2 000 ℃[J]. Journal of the European Ceramic Society, 2020, 40(12): 3829-3843.
[3] VORONOVYCH D, TARAN A, PODSHYVALOVA O, et al. Thermionic emission of yttrium dodecaboride single crystal[J]. Solid State Phenomena, 2019, 289: 47-52.
[4] 陈健,刘欢,史磊,等.YB₄光热转换材料的制备及其性能[J].贵州师范大学学报(自然科学版),2018,36(5):48-53.
CHEN J, LIU H, SHI L, et al. Synthesis and properties of YB₄ photothermal conversion materials[J]. Journal of Guizhou Normal University (Natural Sciences), 2018, 36(5): 48-53 (in Chinese).
[5] ZHOU Y C, LIU B, XIANG H M, et al. YB₆: a ‘ductile’ and soft ceramic with strong heterogeneous chemical bonding for ultrahigh-temperature applications[J]. Materials Research Letters, 2015, 3(4): 210-215.
[6] ZHOU Y C, XIANG H M, FENG Z H, et al. Theoretical prediction on electronic structure, mechanical properties and lattice dynamics of YB₄ for ultrahigh temperature applications[J]. Journal of the European Ceramic Society, 2015, 35(16): 4437-4445.
[7] ZHOU Y C, DAI F Z, XIANG H M, et al. Shear anisotropy: tuning high temperature metal hexaborides from soft to extremely hard[J]. Journal of Materials Science & Technology, 2017, 33(11): 1371-1377.
[8] SEKIDO N, OHMURA T, PEREPEZKO J H. Mechanical properties and dislocation character of YB₄ and YB₆[J]. Intermetallics, 2017, 89: 86-91.
[9] CAHILL J T, GRAEVE O A. Hexaborides: a review of structure, synthesis and processing[J]. Journal of Materials Research and Technology, 2019, 8(6): 6321-6335.
[10] KOVÁČOVÁ Z, BAČA L’, NEUBAUER E, et al. Synthesis and reaction sintering of YB₄ ceramics[J]. Ceramics International, 2019, 45(15): 18795-18802.
[11] FAHRENHOLTZ W G, BINNER J, ZOU J. Synthesis of ultra-refractory transition metal diboride compounds[J]. Journal of Materials Research, 2016, 31(18): 2757-2772.
[12] LI J G, PENG A Y, HE Y, et al. Synthesis of pure YB₄ powder via the reaction of Y₂O₃ with B₄C[J]. Journal of the American Ceramic Society, 2012, 95(7): 2127-2129.
[13] GUO Q Q, XIANG H M, SUN X, et al. Preparation of porous YB₄ ceramics using a combination of in situ borothermal reaction and high temperature partial sintering[J]. Journal of the European Ceramic Society, 2015, 35(13): 3411-3418.
[14] 王军,包黎红,潮洛蒙.六硼化钇纳米粒子超导及光吸收性能研究[J].内蒙古师范大学学报(自然科学版),2021,50(3):204-209.
WANG J, BAO L H, CHAO L M. Study on superconductivity and optical absorption of yttrium hexaboride nanoparticles[J]. Journal of Inner Mongolia Normal University (Natural Science Edition), 2021, 50(3): 204-209 (in Chinese).
[15] ETOURNEAU J, MERCURIO J P, HAGENMULLER P. Compounds based on octahedral B6 units: hexaborides and tetraborides[M]//Boron and Refractory Borides. Springer, Berlin, Heidelberg, 1977: 115-138.
[16] ZHANG W M, ZHAO B, NI N, et al. High entropy rare earth hexaborides/tetraborides (HE REB₆/HE REB₄) composite powders with enhanced electromagnetic wave absorption performance[J]. Journal of Materials Science & Technology, 2021, 87: 155-166.
[17] ZHOU Y C, WANG X F, XIANG H M, et al. Theoretical prediction, preparation, and mechanical properties of YbB₆, a candidate interphase material for future UHTCf/UHTC composites[J]. Journal of the European Ceramic Society, 2016, 36(15): 3571-3579.
[18] LIU Z, LI Z H, LIU J H, et al. Long-circulating Er³⁺-doped Yb₂O₃ up-conversion nanoparticle as an in vivo X-ray CT imaging contrast agent[J]. Biomaterials, 2012, 33(28): 6748-6757.
[19] CHEN I W, WANG X H. Sintering dense nanocrystalline ceramics without final-stage grain growth[J]. Nature, 2000, 404(6774): 168-171.
[20] EVANS A G, CHARLES E A. Fracture toughness determinations by indentation[J]. Journal of the American Ceramic Society, 1976, 59(7/8): 371-372.
[21] CLARK S J, SEGALL M D, PICKARD C J, et al. First principles methods using CASTEP[J]. Zeitschrift Für Kristallographie-Crystalline Materials, 2005, 220(5/6): 567-570.
[22] PERDEW J P, BURKE K, ERNZERHOF M. Generalized gradient approximation made simple[J]. Physical Review Letters, 1996, 77(18): 3865-3868.
[23] KRESSE G, JOUBERT D. From ultrasoft pseudopotentials to the projector augmented-wave method[J]. Physical Review B, 1999, 59(3): 1758-1775.
[24] BLÖCHL P E. Projector augmented-wave method[J]. Physical Review B, 1994, 50(24): 17953-17979.
[25] MOSTARI F, RAHMAN M A, KHATUN R. First principles study on the structural, elastic, electronic and optical properties of cubic ‘half-heusler’ alloy RuVAs under pressure[J]. International Journal of Material and Mathematical Sciences, 2020: 51-63.
[26] PETTIFOR D G. Theoretical predictions of structure and related properties of intermetallics[J]. Materials Science and Technology, 1992, 8(4): 345-349.
[27] PUGH S F. XCII. Relations between the elastic moduli and the plastic properties of polycrystalline pure metals[J]. The London, Edinburgh, and Dublin Philosophical Magazine and Journal of Science, 1954, 45(367): 823-843.
[28] PIZ M, FILIPEK E, JABLONSKI M. Mechanochemical synthesis and thermal stability of phases in the Y₂O₃-Yb₂O₃ system[J]. Journal of Thermal Analysis and Calorimetry, 2019, 138(6): 4313-4319.
[29] WANG X F, XIANG H M, SUN X, et al. Porous YbB₆ ceramics prepared by in situ reaction between Yb₂O₃ and B₄C combined with partial sintering[J]. Journal of the American Ceramic Society, 2015, 98(7): 2234-2239.
[30] CHOPADE S S, BARVE S A, THULASI RAMAN K H, et al. RF plasma MOCVD of Y₂O₃ thin films: effect of RF self-bias on the substrates during deposition[J]. Applied Surface Science, 2013, 285: 524-531.
[31] LI Y Q, QIU T. Oxidation behaviour of boron carbide powder[J]. Materials Science and Engineering: A, 2007, 444(1/2): 184-191.
[32] TEL’NOVA G B, KONOVALOV A A, DUDENKOV I V, et al. Mechanisms of formation of solid solutions and optical spectroscopic properties of transparent ceramic materials based on Y₂O₃: Yb[J]. Russian Journal of Inorganic Chemistry, 2013, 58(11): 1335-1340.
[33] KINGERY W D, BOWEN H K, UHLMANN D R, et al. Introduction to ceramics[J]. Journal of the Electrochemical Society, 1977, 124(3): 152C.
[34] ZHU S M, FAHRENHOLTZ W G, HILMAS G E. Influence of silicon carbide particle size on the microstructure and mechanical properties of zirconium diboride-silicon carbide ceramics[J]. Journal of the European Ceramic Society, 2007, 27(4): 2077-2083.
[35] BARSOUM M W, EL-RAGHY T. Synthesis and characterization of a remarkable ceramic: Ti₃SiC₂[J]. Journal of the American Ceramic Society, 1996, 79(7): 1953-1956.
[36] LI F Z, LIU B, WANG J Y, et al. Hf₃AlN: a novel layered ternary ceramic with excellent damage tolerance[J]. Journal of the American Ceramic Society, 2010, 93(1): 228-234.

Preparation and Mechanical Properties of Ultra-High Temperature Rare Earth Boride (Y_1-xYb_x)B₆

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 1

Recommended Articles

Metrics

Comments