Preparation and Properties of Coal Gasification Coarse Slag-Blast Furnace Slag Based Geopolymer

Abstract

Abstract: Mixing blast furnace slag (BFS) in coal gasification coarse slag (CGCS) based geopolymer improves its early mechanical properties. In this paper, CGCS and BFS were used as raw materials to prepare geopolymer, and the effect of different BFS content on the early mechanical properties and microstructure of geopolymer was studied. The microstructure of activated CGCS-BFS based geopolymer was characterized by X-ray diffraction, mercury intrusion porosimeter, scanning electron microscope and Fourier transformed infrared spectroscopy. The results show that the compressive strength of geopolymer increases gradually when the BFS content increases. When the BFS content reaches 40% (mass fraction), the 28 d compressive strength of sample is as high as 53.1 MPa. According to the microscopic analysis, a large amount of calcium/sodium silicate aluminate hydrate (C(N)-A-S-H) gel is formed on the surface of the geopolymer, which makes the microstructure of geopolymer more denser, and thus improves the mechanical properties of geopolymer.

Key words: coal gasification coarse slag, blast furnace slag, geopolymer, alkali activation, mechanical property, microstructure

CLC Number:

TU52

ZHAO Lijie, ZHANG Tong, HUANG Wei, SU Zhuangfei, LIU Ze. Preparation and Properties of Coal Gasification Coarse Slag-Blast Furnace Slag Based Geopolymer[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(10): 3542-3547.

References

[1] DAVIDOVITS J. Geopolymers[J]. Journal of Thermal Analysis, 1991, 37(8): 1633-1656.
[2] 尚建丽,刘琳.矿渣-粉煤灰地质聚合物制备及力学性能研究[J].硅酸盐通报,2011,30(3):741-744.
SHANG J L, LIU L. Study on preparation and mechanical properties of slag and fly ash based geopolymeric[J]. Bulletin of the Chinese Ceramic Society, 2011, 30(3): 741-744 (in Chinese).
[3] 陆银平,邓宗义,李瑞乐,等.矿渣/偏高岭土基地质聚合物多孔材料制备与性能研究[J].非金属矿,2019,42(3):44-47.
LU Y P, DENG Z Y, LI R L, et al. Preparation and properties of slag/metakaolin-based polymer porous materials[J]. Non-Metallic Mines, 2019, 42(3): 44-47 (in Chinese).
[4] KRIVENKO P, GOTS V I, PETROPAVLOVSKYI O, et al. Complex shrinkage-reducing additives for alkali activated slag cement fine concrete[J]. Solid State Phenomena, 2021, 321: 165-170.
[5] VIGGH E, ERIKSSON M, WILHELMSSON B, et al. Early formation of belite in cement clinker raw materials with slag[J]. Advances in Cement Research, 2021, 33(6): 249-256.
[6] 罗忠涛,康少杰,张美香,等.碱激发赤泥-矿渣地质聚合物制备及力学性能研究[J].武汉理工大学学报,2019,41(3):47-51.
LUO Z T, KANG S J, ZHANG M X, et al. Study of preparation and mechanical property of red mud and slag geopolymer[J]. Journal of Wuhan University of Technology, 2019, 41(3): 47-51 (in Chinese).
[7] 刘泽,周瑜,孔凡龙,等.碱激发矿渣基地质聚合物微观结构与性能研究[J].硅酸盐通报,2017,36(6):1830-1834.
LIU Z, ZHOU Y, KONG F L, et al. Microstructure and properties of alkali-activated blast furnace slag based geopolymer[J]. Bulletin of the Chinese Ceramic Society, 2017, 36(6): 1830-1834 (in Chinese).
[8] 王殿生.大型煤气化技术的研究与发展[J].化工设计通讯,2018,44(2):11.
WANG D S. Research and development of large coal gasification technology[J]. Chemical Engineering Design Communications, 2018, 44(2): 11 (in Chinese).
[9] ZHANG J Y, ZUO J, JIANG Y S, et al. Kinetic analysis on the mesoporous formation of coal gasification slag by acid leaching and its thermal stability[J]. Solid State Sciences, 2020, 100: 106084.
[10] 张彤,刘泽,苏壮飞,等.TiO₂改性煤气化粗渣基地质聚合物的微观结构与性能[J].硅酸盐通报,2022,41(2):520-525+535.
ZHANG T, LIU Z, SU Z F, et al. Microstructure and properties of TiO₂ modified coal gasification coarse slag based geopolymer[J]. Bulletin of the Chinese Ceramic Society, 2022, 41(2): 520-525+535 (in Chinese).
[11] 商晓甫,马建立,张剑,等.煤气化炉渣研究现状及利用技术展望[J].环境工程技术学报,2017,7(6):712-717.
SHANG X F, MA J L, ZHANG J, et al. Research status and prospects of utilization technologies of slag from coal gasification[J]. Journal of Environmental Engineering Technology, 2017, 7(6): 712-717 (in Chinese).
[12] 曲江山,张建波,孙志刚,等.煤气化渣综合利用研究进展[J].洁净煤技术,2020,26(1):184-193.
QU J S, ZHANG J B, SUN Z G, et al. Research progress on comprehensive utilization of coal gasification slag[J]. Clean Coal Technology, 2020, 26(1): 184-193 (in Chinese).
[13] 盛燕萍,扈培臻,冀欣,等.粉磨时间对煤气化渣复合胶凝材料的性能影响研究[J].应用化工,2020,49(8):1999-2003.
SHENG Y P, HU P Z, JI X, et al. Study on the effect of pulverizing time on the properties of coal gasification slag composite cementitious material[J]. Applied Chemical Industry, 2020, 49(8): 1999-2003 (in Chinese).
[14] 傅博,马梦凡,申旺,等.气化渣对硅酸盐水泥强度和微观结构的影响研究[J].硅酸盐通报,2020,39(8):2523-2527.
FU B, MA M F, SHEN W, et al. Influence of coal gasification slag on strength and microstructure of Portland cement[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(8): 2523-2527 (in Chinese).
[15] LIU Y Y, LEI S M, LIN M, et al. Assessment of pozzolanic activity of calcined coal-series kaolin[J]. Applied Clay Science, 2017, 143: 159-167.
[16] DEHGHANI A, ASLANI F, GHAEBI PANAH N. Effects of initial SiO₂/Al₂O₃ molar ratio and slag on fly ash-based ambient cured geopolymer properties[J]. Construction and Building Materials, 2021, 293: 123527.
[17] 郭伟.煤矸石的活性激发及活性评价方法的探讨[D].南京:南京工业大学,2005.
GUO W. Research on coal gangue activation and its activity evaluation method[D]. Nanjing: Nanjing University of Technology, 2005 (in Chinese).
[18] GARCIA-LODEIRO I, PALOMO A, FERNÁNDEZ-JIMÁNEZ A, et al. Compatibility studies between N-A-S-H and C-A-S-H gels. Study in the ternary diagram Na₂O-CaO-Al₂O₃-SiO₂-H₂O[J]. Cement and Concrete Research, 2011, 41(9): 923-931.