Properties of Carbide Slag-Slag Composite Cementitious Material

Abstract

Abstract: Carbide slag (CS), as a kind of industrial waste slag with high alkalinity has low comprehensive utilization rate. In order to solve the problem of excessive carbide slag, the alkali excitation performance of carbide slag on slag cementitious system was studied by using the strong alkaline of carbide slag. Based on the characteristics that carbide slag carbonization reaction generated calcium carbonate, the influences of different carbonization systems on the performance of alkali-activated slag cementitious system were explored. The results show that CS with large dosage has a good alkali-activated effect on the slag cementitious material, and a large amount of C-(A)-S-H gel is generated. The cementitious material with fly ash and metakaolin has best performance. The mechanical properties of carbide slag-slag composite material can be effectively improved after being treated by different carbonation systems. CO₂ gas using as the external carbonation source leads to dense structure on the surface of material matrix, while urea as internal carbonization source makes the internal carbonation of matrix uniform, which improve mechanical properties of the carbide slag-slag composite cementitious material.

Key words: carbide slag, slag, alkali excitation, cementitious material, carbonation, calcium hydroxide, urea

CLC Number:

TQ172

WAN Zonghua, ZHANG Wenqin, LIU Zhichao, WANG Fazhou. Properties of Carbide Slag-Slag Composite Cementitious Material[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(5): 1704-1714.

References

[1] 赵立文,朱干宇,李少鹏,等.电石渣特性及综合利用研究进展[J].洁净煤技术,2021,27(3):13-26.
ZHAO L W, ZHU G Y, LI S P, et al. Research progress on characteristics and comprehensive utilization of calcium carbide slag[J]. Clean Coal Technology, 2021, 27(3): 13-26 (in Chinese).
[2] 曹春霞,王波,成怀刚,等.电石渣及二氧化碳资源化利用现状与展望[J].化工矿物与加工,2022,51(2):1-9.
CAO C X, WANG B, CHENG H G, et al. The status and outlook of the resource utilization of calcium carbide slag and carbon dioxide[J]. Industrial Minerals & Processing, 2022, 51(2): 1-9 (in Chinese).
[3] 樊利勋.电石渣烟气脱硫工艺的改造和应用[D].北京:北京化工大学,2015.
FAN L X. Improvement and application of carbide slag desulfurization[D]. Beijing: Beijing University of Chemical Technology, 2015 (in Chinese).
[4] 戴巍.电石渣碳化技术及碳化砖[J].砖瓦,2006(8):32-33.
DAI W. The carbonation technology of calcium carbide residue and carbonated lime brick[J]. Block-Brick-Tile, 2006(8): 32-33 (in Chinese).
[5] 冯爽,常彩霞,张金君,等.基于电石渣原料的方解石型碳酸钙制备研究[J].广东化工,2021,48(18):37-38.
FENG S, CHANG C X, ZHANG J J, et al. Preparation of calcite calcium carbonate based on carbide slag[J]. Guangdong Chemical Industry, 2021, 48(18): 37-38 (in Chinese).
[6] ALVENTOSA K M L, WILD B, WHITE C E. The effects of calcium hydroxide and activator chemistry on alkali-activated metakaolin pastes exposed to high temperatures[J]. Cement and Concrete Research, 2022, 154: 106742.
[7] ADESINA A. Influence of various additives on the early age compressive strength of sodium carbonate activated slag composites: an overview[J]. Journal of the Mechanical Behavior of Materials, 2020, 29(1): 106-113.
[8] 胡张莉.碱激发矿渣粉煤灰水泥早期水化及收缩特性研究[D].长沙:湖南大学,2013.
HU Z L. Early hydration and shrinkage of alkali-activated slag/fly ash blend cement[D]. Changsha: Hunan University, 2013 (in Chinese).
[9] 白云志.碱激发矿渣的力学性能以及与微观表征的相关性研究[D].青岛:青岛理工大学,2016.
BAI Y Z. Investigation of mechanical performance and relationship between mechanical and microstructure characrization of alkali-activated slag[D]. Qingdao: Qingdao Tehcnology University, 2016 (in Chinese).
[10] ZHANG B L, TAN H B, SHEN W G, et al. Nano-silica and silica fume modified cement mortar used as surface protection material to enhance the impermeability[J]. Cement and Concrete Composites, 2018, 92: 7-17.
[11] 何彤彤.碱激发矿渣的碳化性能研究[D].南京:东南大学,2018.
HE T T. Study on the carbonation performance of alkali-activated slag[D]. Nanjing: Southeast University, 2018 (in Chinese).
[12] 汪鹏.再生胶凝材料快速碳化硬化行为[D].武汉:武汉理工大学,2021:37-39.
WANG P. Rapid carbonization hardening behavior of recycled cementitious materials[D]. Wuhan: Wuhan University of Technology, 2021:37-39 (in Chinese).
[13] 郑晓惠.受热条件下水化硅酸钙的结构变化及再水化特性[D].武汉:武汉理工大学,2018.
ZHENG X H. Structure changes of calcium silicate hydrate after heating and its rehydration characteristic[D]. Wuhan: Wuhan University of Technology, 2018 (in Chinese).
[14] CAMERINI R, POGGI G, CHELAZZI D, et al. The carbonation kinetics of calcium hydroxide nanoparticles: a boundary nucleation and growth description[J]. Journal of Colloid and Interface Science, 2019, 547: 370-381.
[15] 李勇.氢氧化钙的加速碳化机理研究[D].大连:大连理工大学,2014.
LI Y. Research on the mechanism of accelerated carbonation of calcium hydroxide[D]. Dalian: Dalian University of Technology, 2014 (in Chinese).
[16] 乔欣元.CO₂浓度对氢氧化钙碳化性能的影响[J].广州化工,2015,43(15):3-4+25.
QIAO X Y. Influence of CO₂ concentrations on carbonation property of Ca(OH)₂[J]. Guangzhou Chemical Industry, 2015, 43(15): 3-4+25 (in Chinese).