Foaming Properties of Ceramics Foamed by Polishing Slag System

Abstract

Abstract: Foamed ceramics were prepared by commercially formula of polishing slag system, and the effects of sintering temperature on foaming properties of samples were studied. By contrastive analysis, the microstructure, linear shrinkage rate and volume expansion rate of samples with foaming agents were reseached, and the effects of pore structure on the strength and thermal stability were studied. It was found that, polishing slags can foam by itself, forming spherical pores with size of 10 μm to 200 μm (1 160 ℃ to 1 220 ℃). And the walls of pores were dense. It is very sensitive to sintering temperature, in the range of 1 180 ℃ to 1 200 ℃, the volume of the foamed ceramics sample expanded twice. The foaming property of samples with SiC was significantly improved, the pores were irregular, and the pore size of samples increased by 10 times. After adding foaming agent, There were small pores in the pore wall, which made the strength and the thermal conductivity loss less, while the porosity increased. However, the distribution of pores in the wall was uneven, decreasing the thermal stability of the foamed ceramics.

Key words: foamed ceramics, polishing slag, foaming property, sintering temperature, pore distribution, application performance

CLC Number:

TB321
TQ174

DAI Yonggang, LU Chenglong, ZHANG Yinfeng, ZHANG Guotao. Foaming Properties of Ceramics Foamed by Polishing Slag System[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(8): 2726-2733.

References

[1] 黄惠宁.2019我国发泡陶瓷产业现状及技术分析[J].佛山陶瓷,2019,29(11):1-4.
HUANG H N. Current situation and technical analysis of foamed ceramic industry in our country in 2019[J]. Foshan Ceramics, 2019, 29(11): 1-4 (in Chinese).
[2] 彭团儿,李洪潮,刘玉林,等.工业固废制备发泡陶瓷研究及应用进展[J].陶瓷,2019(12):9-22.
PENG T E, LI H C, LIU Y L, et al. Applications and research of foam ceramic prepared by using industry solid waste[J]. Ceramics, 2019(12): 9-22 (in Chinese).
[3] 熊灿光,王慧,曾令可.利用抛光废渣制造发泡陶瓷[J].山东陶瓷,2019,42(3):3-8.
XIONG C G, WANG H, ZENG L K. Research status of foaming ceramics made from polishing waste slag[J]. Shandong Ceramics, 2019, 42(3): 3-8 (in Chinese).
[4] 谢红波,陈哲,麦俊明,等.利用陶瓷工业废弃物抛光渣制备陶瓷砖的研究[J].非金属矿,2019,42(3):100-103.
XIE H B, CHEN Z, MAI J M, et al. Study on preparation of ceramic tiles by using ceramic industrial waste polishing slag[J]. Non-Metallic Mines, 2019, 42(3): 100-103 (in Chinese).
[5] 杨超,饶宗旺,邓坚勇.利用抛光砖废渣制备轻质外墙砖的研究[J].佛山陶瓷,2010,20(7):25-27+39.
YANG C, RAO Z W, DENG J Y. Preparation of lightweight external brick with tile polished waste[J]. Foshan Ceramics, 2010, 20(7): 25-27+39 (in Chinese).
[6] 李剑桥.陶瓷抛光渣烧成发泡的气氛影响与控制研究[D].广州:华南理工大学,2019.
LI J Q. Study on the atmosphere effect and control of foaming of porcelain polished tiles waste during firing[D]. Guangzhou: South China University of Technology, 2019 (in Chinese).
[7] 罗浩乐,顾幸勇,游小棠.建陶抛光砖废渣制备轻质外墙砖研究[J].陶瓷学报,2009,30(1):112-116.
LUO H L, GU X Y, YOU X T. Fabrication of lightweight external wall tile with waste polished ceramic tile[J]. Journal of Ceramics, 2009, 30(1): 112-116 (in Chinese).
[8] 税安泽,夏海斌,曾令可,等.利用抛光砖废料制备多孔保温建筑材料[J].硅酸盐通报,2008,27(1):191-195.
SHUI A Z, XIA H B, ZENG L K, et al. Preparation of porous thermal insulation building material with tile polished waste[J]. Bulletin of the Chinese Ceramic Society, 2008, 27(1): 191-195 (in Chinese).
[9] 赵威,王竹,戴永刚,等.陶瓷废料制备轻质保温泡沫陶瓷的研究[J].硅酸盐通报,2019,38(7):2288-2294.
ZHAO W, WANG Z, DAI Y G, et al. Research on preparation of lightweight thermal insulation foam ceramics with ceramic wastes[J]. Bulletin of the Chinese Ceramic Society, 2019, 38(7): 2288-2294 (in Chinese).
[10] 谭洪波,吕周岭,马保国,等.黄姜废渣发泡陶瓷的制备及其性能研究[J].硅酸盐通报,2021,40(2):597-604.
TAN H B, LYU Z L, MA B G, et al. Preparation and properties of foamed ceramics from turmeric residue[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(2): 597-604 (in Chinese).
[11] 张勇林.高温发泡陶瓷制备基础研究[D].广州:华南理工大学,2014.
ZHANG Y L. Fundamental research on preparation of high-temperature floamed ceramics[D]. Guangzhou: South China University of Technology, 2014 (in Chinese).
[12] 关振铎,张中太,焦金生.无机材料物理性能[M].2版.北京:清华大学出版社,2011.
GUAN Z D, ZHANG Z T, JIAO J S. Physical properties of inorganic materials[M]. 2nd edition. Beijing: Tsinghua University Press, 2011 (in Chinese).
[13] 张银凤,张校飞.陶瓷材料的抗热震机理分析[J].湖北理工学院学报,2018,34(3):35-40.
ZHANG Y F, ZHANG X F. Thermal shock resistance mechanism analysis of ceramic materials[J]. Journal of Hubei Polytechnic University, 2018, 34(3): 35-40 (in Chinese).
[14] 王开宇,刘瑞祥,李秀涛,等.轻质刚性隔热材料的制备及性能研究[J].硅酸盐通报,2019,38(11):3529-3533+3540.
WANG K Y, LIU R X, LI X T, et al. Preparation and properties research of light rigid thermal insulation materials[J]. Bulletin of the Chinese Ceramic Society, 2019, 38(11): 3529-3533+3540 (in Chinese).
[15] 李启伟,李楠,鄢文.碱性隔热耐火材料的组成、结构与性能研究[J].硅酸盐通报,2014,33(7):1758-1761+1768.
LI Q W, LI N, YAN W. Study on compositions, microstructure and properties of basic insulating refractory[J]. Bulletin of the Chinese Ceramic Society, 2014, 33(7): 1758-1761+1768 (in Chinese).
[16] 石纪军,邓一星,孙国梁.尾砂和煤矸石制备闭孔泡沫陶瓷的导热性能研究[J].新型建筑材料,2020,47(12):103-106.
SHI J J, DENG Y X, SUN G L. The thermal conductivity properties of closed foam ceramic prepared by tailings and coal gangue[J]. New Building Materials, 2020, 47(12): 103-106 (in Chinese).
[17] 李子恒.发泡陶瓷耐火极限性能的研究[J].佛山陶瓷,2019,29(9):19-22.
LI Z H. Study on refractory limit performance of foam ceramic[J]. Foshan Ceramics, 2019, 29(9): 19-22 (in Chinese).
[18] 吴浩,周明凯,王怀德,等.铝尾矿制备发泡陶瓷组成设计研究[J].新型建筑材料,2020,47(8):149-154.
WU H, ZHOU M K, WANG H D, et al. Research on composition design of foam ceramics with bauxite tailing[J]. New Building Materials, 2020, 47(8): 149-154 (in Chinese).
[19] 赵威,王竹,戴永刚,等.MnO₂对钼尾矿基发泡陶瓷升温速率影响的研究[J].硅酸盐通报,2020,39(4):1266-1271.
ZHAO W, WANG Z, DAI Y G, et al. Influence of MnO₂ on heating rate of foam ceramics based on molybdenum tailing[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(4): 1266-1271 (in Chinese).
[20] 丁建明.发泡陶瓷冷加工设备现状和趋势[J].佛山陶瓷,2020,30(2):46-49.
DING J M. Present status and tendency of cold-working equipment for foam ceramic[J]. Foshan Ceramics, 2020, 30(2): 46-49 (in Chinese).