玻璃粉和生物炭对砂浆塑性收缩及开裂行为的影响

硅酸盐通报 ›› 2024, Vol. 43 ›› Issue (9): 3337-3347.

玻璃粉和生物炭对砂浆塑性收缩及开裂行为的影响

罗浩然¹, 刘惠¹, 周一一², Amardeep Singh³, 刘琼⁴

1.常州大学环境科学与工程学院,常州 213614;
2.河海大学力学与材料学院,南京 210000;
3.常州工学院土木建筑工程学院,常州 213032;
4.上海理工大学环境与建设学院,上海 200093

收稿日期:2024-02-01 修订日期:2024-04-09 出版日期:2024-09-15 发布日期:2024-09-19
通信作者: 刘惠,博士,副教授。E-mail:liuhui@cczu.edu.cn
作者简介:罗浩然(1998—),男,硕士研究生。主要从事固废材料再利用的研究。E-mail:1065479569@qq.com
基金资助:
国家自然科学基金(52178109)

Effects of Glass Powder and Biochar on Plastic Shrinkage and Cracking Behavior of Mortar

LUO Haoran¹, LIU Hui¹, ZHOU Yiyi², AMARDEEP Singh³, LIU Qiong⁴

1. School of Environmental Science and Engineering, Changzhou University, Changzhou 213164, China;
2. College of Mechanics and Materials, Hohai University, Nanjing 210000, China;
3. School of Civil Engineering & Architecture, Changzhou Institute of Technology, Changzhou 213032, China;
4. School of Environment and Architecture, University of Shanghai for Science and Technology, Shanghai 200093, China

Received:2024-02-01 Revised:2024-04-09 Published:2024-09-15 Online:2024-09-19

摘要/Abstract

摘要： 为探究可再生材料对砂浆塑性收缩及开裂的影响,本文选取玻璃粉和生物炭两种可再生材料,采用数字图像相关技术(DIC)定量评估不同掺量(2%、4%、6%,占水泥质量分数)玻璃粉和生物炭对砂浆塑性收缩和开裂行为的影响。结果表明,掺玻璃粉和生物炭组砂浆最大裂缝宽度均小于未添加玻璃粉和生物炭的对照组,因此添加2%~6%玻璃粉或生物炭对砂浆的塑性收缩及开裂均起到积极作用。玻璃粉表面光滑疏水,提高了砂浆的流动性,其填充效应和火山灰活性减缓了塑性收缩。生物炭具有多孔结构和吸水性,降低了砂浆的流动性,有效减缓了塑性收缩。

关键词: 玻璃粉, 生物炭, DIC, 塑性收缩, 开裂, 裂缝宽度

Abstract: To investigate the effect of renewable materials on the plastic shrinkage and cracking behavior of mortar, this study selected two renewable materials, glass powder and biochar. Digital image correlation (DIC) technique was employed to quantitatively assess the influence of different dosages (2%, 4%, 6% by cement mass fraction) of glass powder and biochar on the plastic shrinkage and cracking behavior of mortar. The results indicate that the maximum crack width of mortar with glass powder and biochar is smaller than that of the control group without glass powder and biochar. Therefore, adding 2%~6% of glass powder or biochar has a positive effect on the plastic shrinkage and cracking of mortar. Glass powder, due to its smooth surface and hydrophobic nature, enhances the flowability of mortar, but the filling effect and pozzolanic activity of volcanic ash slow down the plastic shrinkage. Biochar, with its porous structure and water absorption capacity, reduces the flowability of mortar, effectively mitigating plastic shrinkage.

Key words: glass powder, biochar, DIC, plastic shrinkage, cracking, crack width

中图分类号:

TU528

罗浩然, 刘惠, 周一一, Amardeep Singh, 刘琼. 玻璃粉和生物炭对砂浆塑性收缩及开裂行为的影响[J]. 硅酸盐通报, 2024, 43(9): 3337-3347.

LUO Haoran, LIU Hui, ZHOU Yiyi, AMARDEEP Singh, LIU Qiong. Effects of Glass Powder and Biochar on Plastic Shrinkage and Cracking Behavior of Mortar[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(9): 3337-3347.

参考文献

[1] 光鉴淼, 邹小童. 减缩剂对水泥砂浆塑性收缩开裂的影响及机理分析[J]. 新型建筑材料, 2023, 50(9): 57-61.
GUANG J M, ZOU X T. Effect of shrinkage-reducing admixture on the plastic shrinkage cracking of mortar and mechanism analysis[J]. New Building Materials, 2023, 50(9): 57-61 (in Chinese).
[2] 黎碧云, 孙振平, 胡匡艺, 等. 减缩剂对新拌水泥浆体体积变化的影响[J]. 建筑材料学报, 2020, 23(3): 493-499.
LI B Y, SUN Z P, HU K Y, et al. Effect of shrinkage reducer on volume change of fresh cement paste[J]. Journal of Building Materials, 2020, 23(3): 493-499 (in Chinese).
[3] 杨文秀, 赵青林, 周明凯, 等. 复合增稠剂对大流态薄层砂浆性能的影响及其抗裂机理[J]. 硅酸盐通报, 2023, 42(6): 1938-1949.
YANG W X, ZHAO Q L, ZHOU M K, et al. Effect of composite thickener on properties of large fluidity thin-layer mortar and its anti-cracking mechanism[J]. Bulletin of the Chinese Ceramic Society, 2023, 42(6): 1938-1949 (in Chinese).
[4] 李林香, 谭盐宾, 谢永江, 等. 增稠剂对混凝土收缩性能的影响[J]. 新型建筑材料, 2022, 49(3): 38-41.
LI L X, TAN Y B, XIE Y J, et al. Effects of different thickeners on shrinkage properties of concrete[J]. New Building Materials, 2022, 49(3): 38-41 (in Chinese).
[5] 何健辉, 程从密, 张亚芳, 等. 玻璃纤维参数对水泥砂浆减裂效果的影响[J]. 混凝土, 2020(10): 118-120+160.
HE J H, CHENG C M, ZHANG Y F, et al. Effect of glass fiber parameters on plastic shrinkage cracking of mortar[J]. Concrete, 2020(10): 118-120+160 (in Chinese).
[6] 马一平, 余少同, 游璐, 等. 纤维参数对水泥基材料减裂效果的影响[J]. 建筑材料学报, 2018, 21(5): 797-802.
MA Y P, YU S T, YOU L, et al. Effect of fiber parameters on crack reduction of cement based materials[J]. Journal of Building Materials, 2018, 21(5): 797-802 (in Chinese).
[7] 郭秀艳, 马国金. 纤维素纤维自养护水泥砂浆塑性收缩行为的研究[J]. 硅酸盐通报, 2018, 37(1): 337-341.
GUO X Y, MA G J. Plastic shrinkage behaviors of internal curing mortar with cellulose fibers[J]. Bulletin of the Chinese Ceramic Society, 2018, 37(1): 337-341 (in Chinese).
[8] 杨晓杰, 明守旺, 马一平, 等. 矿物掺合料对砂浆塑性收缩开裂影响的研究[J]. 粉煤灰综合利用, 2016, 29(5): 7-11.
YANG X J, MING S W, MA Y P, et al. Research on influence of the mineral admixture on the plastic shrinkage cracking of cement mortar[J]. Fly Ash Comprehensive Utilization, 2016, 29(5): 7-11 (in Chinese).
[9] 韩松, 涂亚秋, 安明喆, 等. 活性粉末混凝土早期收缩规律及其控制方法[J]. 中国铁道科学, 2015, 36(1): 40-47.
HAN S, TU Y Q, AN M Z, et al. The shrinkage of reactive powder concrete in early age and its control methods[J]. China Railway Science, 2015, 36(1): 40-47 (in Chinese).
[10] 赵宪忠, 李秋云. 土木工程结构试验量测技术研究进展与现状[J]. 西安建筑科技大学学报(自然科学版), 2017, 49(1): 48-55.
ZHAO X Z, LI Q Y. A review on measurement technology for structural testing in civil engineering[J]. Journal of Xi'an University of Architecture & Technology (Natural Science Edition), 2017, 49(1): 48-55 (in Chinese).
[11] 邵新星, 陈振宁, 戴云彤, 等. 数字图像相关方法若干关键问题研究进展[J]. 实验力学, 2017, 32(3): 305-325.
SHAO X X, CHEN Z N, DAI Y T, et al. Research progress of several key problems in digital image correlation method[J]. Journal of Experimental Mechanics, 2017, 32(3): 305-325 (in Chinese).
[12] PATEL D, TIWARI R P, SHRIVASTAVA R, et al. Effective utilization of waste glass powder as the substitution of cement in making paste and mortar[J]. Construction and Building Materials, 2019, 199: 406-415.
[13] WANG Y B, LI J W, HE X Y, et al. Effects of wet-grinded superfine waste glass on the fresh properties and reaction characteristic of cement pastes[J]. Construction and Building Materials, 2020, 247: 118593.
[14] WU J D, GUO L P, CAO Y Z, et al. Mechanical and fiber/matrix interfacial behavior of ultra-high-strength and high-ductility cementitious composites incorporating waste glass powder[J]. Cement and Concrete Composites, 2022, 126: 104371.
[15] 熊志文, 柯国军, 陶望, 等. 废玻璃粉对水泥基材料流动性能的影响[J]. 中国粉体技术, 2021, 27(1): 80-89.
XIONG Z W, KE G J, TAO W, et al. Influence of waste glass powder on fluidity of cement-based materials[J]. China Powder Science and Technology, 2021, 27(1): 80-89 (in Chinese).
[16] 周文建, 薛文, 许丹, 等. 山核桃蒲壳生物炭砂浆基本性能及机理研究[J]. 硅酸盐通报, 2023, 42(9): 3186-3195.
ZHOU W J, XUE W, XU D, et al. Research on basic properties and mechanism of carya cathayensis peels biochar mortar[J]. Bulletin of the Chinese Ceramic Society, 2023, 42(9): 3186-3195 (in Chinese).
[17] HARBI R, DERABLA R, NAFA Z. Improvement of the properties of a mortar with 5% of kaolin fillers in sand combined with metakaolin, brick waste and glass powder in cement[J]. Construction and Building Materials, 2017, 152: 632-641.
[18] 郑克仁, 陈楼, 周瑾. 玻璃粉的火山灰反应及对水化硅酸钙组成的影响[J]. 硅酸盐学报, 2016, 44(2): 202-210.
ZHENG K R, CHEN L, ZHOU J. Pozzolanic reaction of soda-lime glass and its influences on composition of calcium silicate hydrate[J]. Journal of the Chinese Ceramic Society, 2016, 44(2): 202-210 (in Chinese).
[19] 李方, 杨健, 李粒珲. 废玻璃粉作为辅助胶凝材料对砂浆性能影响及作用机理[J]. 硅酸盐通报, 2022, 41(9): 3208-3218.
LI F, YANG J, LI L H. Effect and mechanism of waste glass powder as supplementary cementitious material on mortar properties[J]. Bulletin of the Chinese Ceramic Society, 2022, 41(9): 3208-3218 (in Chinese).