复掺矿物掺合料对氯氧镁水泥耐水性能的影响

摘要/Abstract

摘要： 为了更好地促进氯氧镁水泥(MOC)的工程化应用,研究了原料配比、单掺不同磷酸盐改性剂、复掺磷酸与矿物掺合料改性剂对MOC耐水性能的影响。采用抗折强度、抗压强度(力学性能),变异系数(强度随改性剂掺量变化的稳定性),耐水系数(耐水性能)综合评价了改性剂对MOC耐水性能的改善效果,并结合扫描电子显微镜分析耐水性能改善机理。结果表明:当原料摩尔比n(MgO):n(MgCl₂):n(H₂O)=7:1:15,且1.0%磷酸和60%硅灰(占MgO的质量分数)复掺时,MOC的耐水性能改善效果最佳,改性后MOC的耐水系数在1.1以上;微集料填充效应、火山灰效应、强度相(P5)稳定性的增强效应共同提升了MOC的耐水性能。

关键词: 胶凝材料, 氯氧镁水泥, 矿物掺合料, 力学性能, 耐水性能, 改性机理

Abstract: In order to better promote the engineering application of magnesium oxychloride cement (MOC), the effects of raw material ratio, single mixing of different phosphate modifiers, combined mixing of phosphoric acid and mineral admixture modifiers on the water resistance of MOC were studied. The improvement effect of modifier on the water resistance of MOC was comprehensively evaluated by using flexural strength, compressive strength (mechanical properties), variation coefficient (strength stability with modifier dosage) and water resistance coefficient (water resistance), and the improvement mechanism of water resistance was analyzed by scanning electron microscope. The results show that when the molar ratio of raw materials is n(MgO):n(MgCl₂):n(H₂O)=7:1:15, and 1.0% phosphoric acid and 60% silica fume (mass fraction of MgO), the water resistance of MOC is the best, and the water resistance coefficient of modified MOC is above 1.1. Microaggregate filling effect, pozzolanic effect and enhancement effect of strength phase (P5) stability together improve the water resistance of MOC.

Key words: cementitious material, magnesium oxychloride cement, mineral admixture, mechanical property, water resistance, modification mechanism

中图分类号:

TQ172

翟健梁, 赖淏, 毛楠, 田桂成, 王昊宇, 郭豪彦, 熊锐. 复掺矿物掺合料对氯氧镁水泥耐水性能的影响[J]. 硅酸盐通报, 2022, 41(10): 3590-3598.

ZHAI Jianliang, LAI Hao, MAO Nan, TIAN Guicheng, WANG Haoyu, GUO Haoyan, XIONG Rui. Effects of Compound Mineral Admixtures on Water Resistance of Magnesium Oxychloride Cement[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(10): 3590-3598.

参考文献

[1] 余红发.氯氧镁水泥及其应用[M].北京:中国建材工业出版社,1993.
YU H F. Magnesium oxychloride cement and its application[M]. Beijing: China Building Materials Press, 1993 (in Chinese).
[2] LI K, WANG Y S, YAO N N, et al. Recent progress of magnesium oxychloride cement: manufacture, curing, structure and performance[J]. Construction and Building Materials, 2020, 255: 119381.
[3] GUO Y Y, ZHANG Y X, SOE K, et al. Recent development in magnesium oxychloride cement[J]. Structural Concrete, 2018, 19(5): 1290-1300.
[4] 马慧,关博文,王永维,等.氯氧镁水泥胶凝材料的研究进展[J].材料导报,2015,29(15):103-107.
MA H, GUAN B W, WANG Y W, et al. Research progress of magnesium oxychloride cement gelled material[J]. Materials Review, 2015, 29(15): 103-107 (in Chinese).
[5] TANG S W, HU Y, REN W, et al. Modeling on the hydration and leaching of eco-friendly magnesium oxychloride cement paste at the micro-scale[J]. Construction and Building Materials, 2019, 204: 684-690.
[6] 冯超,关博文,张奔,等.减水剂作用下氯氧镁水泥中水分侵蚀行为[J].非金属矿,2019,42(2):41-44.
FENG C, GUAN B W, ZHANG B, et al. Moisture erosion behavior of magnesium oxychloride cement with the action of water reducer[J]. Non-Metallic Mines, 2019, 42(2): 41-44 (in Chinese).
[7] 阿旦春,肖学英,文静,等.氢氧化镁煅烧工艺和原料配比对氯氧镁水泥抗压强度的影响[J].盐湖研究,2020,28(3):85-92.
A D C, XIAO X Y, WEN J, et al. Influence of calcining process of magnesium hydroxide and raw material ratio on compressive strength of MOC based on orthogonal experiment[J]. Journal of Salt Lake Research, 2020, 28(3): 85-92 (in Chinese).
[8] ZHANG X, GE S J, WANG H N, et al. Effect of 5-phase seed crystal on the mechanical properties and microstructure of magnesium oxychloride cement[J]. Construction and Building Materials, 2017, 150: 409-417.
[9] 张婷婷,孙延杰.硅灰和六偏磷酸钠对氯氧镁水泥耐水性影响的数学建模和微观分析[J].建材技术与应用,2018(2):1-5+11.
ZHANG T T, SUN Y J. Mathematical modeling and microscopic analysis of effect of silica fume and sodium hexametaphosphate on water resistance of magnesium oxychloride cement[J]. Research & Application of Building Materials, 2018(2): 1-5+11 (in Chinese).
[10] FAN T B, HAO Y F, LI L X, et al. Water resistance modification of magnesium oxychloride cement with H₃PO₄/Na₂O·xSiO₂·nH₂O[J]. Key Engineering Materials, 2019, 814: 393-398.
[11] LUO X R, FAN W Q, LI C Q, et al. Effect of hydroxyacetic acid on the water resistance of magnesium oxychloride cement[J]. Construction and Building Materials, 2020, 246: 118428.
[12] LI K, WANG Y S, WANG X, et al. Superhydrophobic magnesium oxychloride cement based composites with integral stability and recyclability[J]. Cement and Concrete Composites, 2021, 118: 103973.
[13] HUANG J X, GE S J, WANG H N, et al. Study on the improvement of water resistance and water absorption of magnesium oxychloride cement using long-chain organosilane-nonionic surfactants[J]. Construction and Building Materials, 2021, 306: 124872.
[14] QIAO H X, ZHU B R, SHI Y Y, et al. Strength development and micro-mechanism of magnesium oxychloride cement concrete[J]. Materials Research Innovations, 2015, 19(s1): S1-185.
[15] WU J Y, CHEN H X, GUAN B W, et al. Effect of fly ash on rheological properties of magnesium oxychloride cement[J]. Journal of Materials in Civil Engineering, 2019, 31(3): 04018405.
[16] GUAN X L, ZHOU G, CUI Y Y, et al. Effect of different-sizes of hydroxyapatite on the water resistance of magnesium oxychloride cement for bone repair[J]. RSC Advances, 2019, 9(66): 38619-38628.
[17] GUO Y Y, ZHANG Y X, SOE K, et al. Development of magnesium oxychloride cement with enhanced water resistance by adding silica fume and hybrid fly ash-silica fume[J]. Journal of Cleaner Production, 2021, 313: 127682.
[18] CHEN X Y, ZHANG T T, BI W L, et al. Effect of tartaric acid and phosphoric acid on the water resistance of magnesium oxychloride (MOC) cement[J]. Construction and Building Materials, 2019, 213: 528-536.
[19] 李天鹏,严云,胡志华,等.磷石膏改善氯氧镁水泥耐水性的可行性研究[J].非金属矿,2020,43(6):13-16.
LI T P, YAN Y, HU Z H, et al. Study on the feasibility of improving water resistance of magnesium oxychloride cement by phosphogypsum[J]. Non-Metallic Mines, 2020, 43(6): 13-16 (in Chinese).
[20] TAN Y N, LIU Y, GROVER L. Effect of phosphoric acid on the properties of magnesium oxychloride cement as a biomaterial[J]. Cement and Concrete Research, 2014, 56: 69-74.
[21] 邓德华.磷酸根离子对氯氧镁水泥水化物稳定性的影响[J].建筑材料学报,2002,5(1):9-12.
DENG D H. Effect of the phosphate anion on the stabilization of hydrate in magnesium oxychloride cement[J]. Journal of Building Materials, 2002, 5(1): 9-12 (in Chinese).
[22] LI Y, LI Z J, PEI H F, et al. The influence of FeSO₄ and KH₂PO₄ on the performance of magnesium oxychloride cement[J]. Construction and Building Materials, 2016, 102: 233-238.
[23] 王雨利,管学茂,廖建国.磷酸和磷酸钠对氯氧镁水泥强度的影响及机理分析[C]//中国硅酸盐学会水泥分会首届学术年会,2009:399-404.
WANG Y L, GUAN X M, LIAO J G. Effects of phosphoric acid and sodium phosphate on strength of magnesium oxychloride cement and its mechanics analysis[C]//The First Annual Conference of Cement Branch of Chinese Ceramic Society, 2009: 399-404 (in Chinese).
[24] PIVÁK A, PAVLÍKOVÁ M, ZÁLESKÁ M, et al. Magnesium oxychloride cement composites with silica filler and coal fly ash admixture[J]. Materials (Basel, Switzerland), 2020, 13(11): 2537.
[25] 李颖,余红发.基于测量高温侵蚀厚度的氯氧镁水泥抗水性的快速评价方法(英文)[J].硅酸盐学报,2014,42(8):1047-1054.
LI Y, YU H F. Rapid assessment method for water resistance of magnesium oxychloride cement based on measurement of high-temperature erosion thickness[J]. Journal of the Chinese Ceramic Society, 2014, 42(8): 1047-1054.
[26] YAN Z B, YANG P W, HUANG J X, et al. Promoting effect and mechanism of several inorganic salts on hydration reaction of magnesium oxychloride cement at low temperature[J]. Construction and Building Materials, 2022, 317: 126171.