不同措施对水泥稳定碎石混合料性能的影响

摘要/Abstract

摘要： 通过开展抗压回弹模量测试、强度测试、收缩性能测试和耐久性能测试,研究了采用振动拌和技术、掺加玄武岩纤维、掺加膨胀剂以及提高水泥用量四种措施对水泥稳定碎石混合料性能的提升效果,并基于多因素方差分析评价了不同技术措施对水泥稳定碎石混合料各项性能的影响程度。结果表明,这四种措施对水泥稳定碎石混合料性能具有显著影响,增大水泥用量对其强度、抗压回弹模量和耐久性提升效果最为显著,但对抗收缩开裂性能不利。掺加膨胀剂和玄武岩纤维可以显著改善水泥稳定碎石混合料的干缩性能,与31 d龄期的基准水泥稳定碎石混合料相比,干缩系数分别降低57.7%和18.8%。

关键词: 水泥稳定碎石混合料, 耐久性, 收缩性能, 膨胀剂, 玄武岩纤维, 振动拌和

Abstract: Through compressive rebound modulus tests, strength tests, shrinkage tests and durability tests, the improvement effects of four different measures, including vibration mixing technology, adding basalt fiber, adding expansion agent and increasing the amount of cement, on the performance of cement stabilized macadam mixture were studied. The effect degrees of different technical measures on the properties of cement stabilized macadam mixture were evaluated based on multivariate analysis of variance. The results show that these four measures have significant impact on the performance of cement stabilized macadam mixture. Increasing the amount of cement has the most significant effect on the improvement of its strength, compressive rebound modulus and durability, but the anti-shrinkage cracking performance is unfavorable. The addition of expansive agent and basalt fiber significantly improve the dry shrinkage performance of cement stabilized macadam mixture, and compared with the benchmark cement stabilized macadam mixture at the age of 31 d, the dry shrinkage coefficient is reduced by 57.7% and 18.8%, respectively.

Key words: cement stabilized macadam mixture, durability, shrinkage performance, expansive agent, basalt fiber, vibratory mixing

中图分类号:

U414

田小革, 于水, 李光耀, 闵雪峰, 任全, 杨帆. 不同措施对水泥稳定碎石混合料性能的影响[J]. 硅酸盐通报, 2022, 41(7): 2235-2243.

TIAN Xiaoge, YU Shui, LI Guangyao, MIN Xuefeng, REN Quan, YANG Fan. Effects of Different Measures on Performance of Cement Stabilized Macadam Mixture[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(7): 2235-2243.

参考文献

[1] 兰伟伟.高速公路半刚性基层沥青路面的耐久性影响分析[J].公路交通科技(应用技术版),2020,16(9):131-133.
LAN W W. Durability analysis of semi-rigid asphalt pavement in expressway[J]. Highway Traffic Technology (Application Technology Edition), 2020, 16(9): 131-133 (in Chinese).
[2] 李淑明,许志鸿.沥青路面结构的耐久性分析[J].同济大学学报(自然科学版),2007,35(4):467-471.
LI S M, XU Z H. Durability analysis of asphalt pavement structures[J]. Journal of Tongji University (Natural Science), 2007, 35(4): 467-471 (in Chinese).
[3] 熊杰.抗裂型公路水泥稳定碎石基层混合料配合比设计及路用性能研究[D].南昌:南昌工程学院,2019.
XIONG J. Study on mixture ratio design and road performance of cement stabilized gravel base of fracture resistant highway[D]. Nanchang: Nanchang Institute of Technology, 2019 (in Chinese).
[4] 张亮.沥青稳定碎石设计方法与施工技术研究[D].天津:河北工业大学,2014.
ZHANG L. The study of asphalt treated design and construction technology[D]. Tianjin: Hebei University of Technology, 2014 (in Chinese).
[5] 吴启一,姚华彦,扈惠敏,等.玄武岩纤维对水泥稳定多孔玄武岩碎石力学性能的影响[J].硅酸盐通报,2022,41(1):192-198.
WU Q Y, YAO H Y, HU H M, et al. Effect of basalt fiber on mechanical properties of cement stabilized porous basalt macadam[J]. Bulletin of the Chinese Ceramic Society, 2022, 41(1): 192-198 (in Chinese).
[6] 李明杰,蒋应军,戴经梁.水泥稳定碎石缩裂机理及在级配设计中应用[J].武汉理工大学学报,2010,32(3):1-4+8.
LI M J, JIANG Y J, DAI J L. Analysis and apply of anti-cracking mechanism of cement stabilization of crushed aggregate[J]. Journal of Wuhan University of Technology, 2010, 32(3): 1-4+8 (in Chinese).
[7] 雷蕾,姜慧,顾万,等.外掺剂改良再生水泥稳定碎石基层材料试验研究[J].公路,2022,67(2):31-37.
LEI L, JIANG H, GU W, et al. Research on recycled cement stabilized crushed stone base material improved with admixtures[J]. Highway, 2022, 67(2): 31-37 (in Chinese).
[8] 赵利军,蒋文志,侯劲汝,等.搅拌方式对水泥稳定碎石混合料抗压强度的影响[J].中国公路学报,2018,31(1):151-158.
ZHAO L J, JIANG W Z, HOU J R, et al. Influence of mixing methods on performance of compressive strength for cement stabilized macadam mixture[J]. China Journal of Highway and Transport, 2018, 31(1): 151-158 (in Chinese).
[9] 薛少青.振动搅拌对水泥稳定碎石性能影响的试验研究[D].西安:长安大学,2016.
XUE S Q. Vibratory mixing mechanism and experimental study on improving the cement stabilized macadam performance[D]. Xi’an: Chang’an University, 2016 (in Chinese).
[10] 杨明.掺玄武岩纤维水泥稳定碎石基层抗裂性能研究[D].哈尔滨:东北林业大学,2011.
YANG M. Study of crack resistance on cement stabilized macadam base with mixed basalt fiber[D]. Harbin: Northeast Forestry University, 2011 (in Chinese).
[11] 程培峰,于铭泽.掺玄武岩纤维水泥稳定碎石温缩抗裂性能试验研究[J].中外公路,2013,33(6):234-238.
CHENG P F, YU M Z. Experimental study on temperature shrinkage and crack resistance of stabilized macadam with basalt fiber cement[J]. Journal of China & Foreign Highway, 2013, 33(6): 234-238 (in Chinese).
[12] 李淑.玄武岩纤维水泥稳定碎石路用性能试验研究[D].青岛:中国海洋大学,2014.
LI S. Experimental study on pavement performance of basalt fiber cement stabilized macadam[D]. Qingdao: Ocean University of China, 2014 (in Chinese).
[13] 暴英波.玄武岩纤维水泥稳定碎石性能研究[D].西安:长安大学,2017.
BAO Y B. Performance study of the cement stabilized macadam with basalt fiber[D]. Xi’an: Chang’an University, 2017 (in Chinese).
[14] 马士宾,曲磊,任俊财,等.基于最优混合设计法的掺膨胀剂的水泥稳定碎石配合比设计[J].公路,2022,67(1):63-69.
MA S B, QU L, REN J C, et al. Mixture ratio design of cement stabilized macadam with expansion agent based on optimal mixture design method[J]. Highway, 2022, 67(1): 63-69 (in Chinese).
[15] 李欢.冀北地区掺膨胀剂水泥稳定碎石材料抗裂性能研究[D].张家口:河北建筑工程学院,2021.
LI H. Research on anti-cracking performance of cement stabilized crushed stone material mixed with expansion agent in northern Hebei region[D]. Zhangjiakou: Hebei University of Architecture, 2021 (in Chinese).
[16] 应荣华,张福生,祝明.基于路用要求的膨胀剂水稳碎石防裂研究[J].中外公路,2013,33(2):278-281.
YING R H, ZHANG F S, ZHU M. Study on crack prevention of water-stabilized macadam with expansion agent based on road requirements[J]. Journal of China & Foreign Highway, 2013, 33(2): 278-281 (in Chinese).
[17] LI J, ZI J M, JIANG T, et al. Impact of the implementation of continuous construction method on pavement cracking performance[J]. International Journal of Pavement Engineering, 2016, 17(3): 201-210.
[18] 张显安,周宇豪,李雪连,等.振动搅拌水泥稳定碎石的力学性能研究[J].中外公路,2021,41(4):332-336.
ZHANG X N, ZHOU Y H, LI X L, et al. Study on mechanical properties of vibration-stirred cement stabilized macadam[J]. Journal of China & Foreign Highway, 2021, 41(4): 332-336 (in Chinese).
[19] 陆青清.脱硫石膏水泥稳定碎石减缩与增强行为机制[J].吉林大学学报(工学版),2021,51(1):252-258.
LU Q Q. Strength enhancement and shrinkage reduction mechanism of desulfurized gypsum cement stabilized aggregates[J]. Journal of Jilin University (Engineering and Technology Edition), 2021, 51(1): 252-258 (in Chinese).
[20] CARRET J C, LAMOTHE S, HOUNKPONOU S E, et al. Effects of pre-cracking on the early-age mechanical properties of a cement-treated base material mixed and tested in laboratory[J]. Construction and Building Materials, 2021, 303: 124488.
[21] 国家质量监督检验检疫总局,中国国家标准化管理委员会.通用硅酸盐水泥:GB 175—2007[S].北京:中国标准出版社,2008.
General Administration of Quality Supervision, Inspection and Quarantine, Standardization Administration of the People’s Republic of China. General purpose Portland cement: GB 175—2007[S]. Beijing: China Communications Press, 2008 (in Chinese).
[22] 中华人民共和国交通运输部.公路路面基层施工技术细则:JTG/T F20—2015[S].北京:人民交通出版社,2015.
Ministry of Transport of the People’s Republic of China. Technical specification for highway pavement base construction: JTG/T F20—2015[S]. Beijing: China Communications Press, 2015 (in Chinese).
[23] 中华人民共和国交通运输部.公路工程无机结合料稳定材料试验规程:JTG E51—2009[S].北京:人民交通出版社,2009.
Ministry of Transport of the People’s Republic of China. Specification for test of inorganic binder stabilized materials for highway engineering: JTG E51—2009[S]. Beijing: China Communications Press, 2009 (in Chinese).
[24] 朱文强.冻融条件下水泥稳定碎石力学性能变化规律试验研究[D].哈尔滨:哈尔滨工业大学,2015.
ZHU W Q. Experimental study on evolution under freeze-thaw conditions mechanical properties of cement stabilized macadam[D]. Harbin: Harbin Institute of Technology, 2015 (in Chinese).