提钛尾渣对氯氧镁水泥耐水性的影响

硅酸盐通报 ›› 2022, Vol. 41 ›› Issue (5): 1742-1749.

提钛尾渣对氯氧镁水泥耐水性的影响

许星星¹, 段文涵², 陈啸洋³, 关岩¹, 毕万利¹

1.辽宁科技大学材料与冶金学院,鞍山 114051;
2.辽宁科技大学土木工程学院,鞍山 114051;
3.辽宁科技大学化学工程学院,鞍山 114051

收稿日期:2021-12-21 修回日期:2022-01-24 出版日期:2022-05-15 发布日期:2022-06-01
通讯作者: 陈啸洋,博士。E-mail:askdcxy@126.com
作者简介:许星星(1998—),女,硕士研究生。主要从事镁质胶凝材料的研究。E-mail:Xuxx98@126.com
基金资助:
国家重点研发计划(2020YFC1909304);国家自然科学基金(51778101)

Effects of Titanium Extraction Tailings on Water Resistance of Magnesium Oxychloride Cement

XU Xingxing¹, DUAN Wenhan², CHEN Xiaoyang³, GUAN Yan¹, BI Wanli¹

1. School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, China;
2. School of Civil Engineering, University of Science and Technology Liaoning, Anshan 114051, China;
3. School of Chemical Engineering, University of Science and Technology Liaoning, Anshan 114051, China

Received:2021-12-21 Revised:2022-01-24 Online:2022-05-15 Published:2022-06-01

摘要/Abstract

摘要： 为了改善氯氧镁水泥(MOC)的耐水性,资源化利用固废提钛尾渣,向MOC中掺入提钛尾渣,利用维卡仪、万能试验机、离子色谱仪、X射线衍射仪、扫描电镜、压汞仪等检测设备分析了提钛尾渣对MOC凝结时间、抗压强度、氯离子溶出率、相组成、微观形貌和孔结构的影响。结果表明:未处理的提钛尾渣提高了MOC的总孔隙率和有害大气孔(直径>100 nm)含量,降低了MOC的抗压强度和耐水性。经磨细工艺处理后的提钛尾渣改善了MOC体系中氧化镁颗粒的分散性,促进了5Mg(OH)₂·MgCl₂·8H₂O生长发育,降低了MOC的总孔隙率,提高了MOC的抗压强度和耐水性。MOC中掺入20%(轻烧粉质量计)经磨细工艺处理后的提钛尾渣后,其28 d抗压强度和浸水28 d的强度保留系数最高,分别可达102.4 MPa和0.88,浸泡液中氯离子浓度可低至11.2 mmol/L。

关键词: 氯氧镁水泥, 提钛尾渣, 耐水性, 氯离子溶出率, 微观形貌, 孔结构

Abstract: To improve the water resistance of magnesium oxychloride cement (MOC) and transform the solid waste-titanium extraction tailings (TETS) powder into resources, the TETS powder was added into MOC as an admixture. The effect of TETS powder on the setting time, compressive strength, dissolution rate of chloride ion, phase composition, microstructure and pore structure was analyzed by Vicat, electronic servo testing machine, ion chromatograph, X-ray diffractometer, scanning electron microscope and mercury intrusion porosimetry, etc. The results show that untreated TETS increases the total porosity and the large pores (>100 nm in diameter) content of the MOC matrix, resulting in a decrease in the compressive strength and water resistance of MOC. TETS powder treated by grinding can improve the dispersion of MgO particles in the MOC system, promote the growth and development of 5Mg(OH)₂·MgCl₂·8H₂O crystals, and reduce the total porosity of MOC, resulting in an increase in the compressive strength and water resistance of MOC. The 28 d compressive strength and 28 d strength retention coefficient of MOC containing 20% TETS powder treated by grinding (by weight of light-burned magnesia) reach to 102.4 MPa and 0.88, respectively. Meanwhile, the concentration of chloride ion in soaking liquid decreases to 11.2 mmol/L.

Key words: magnesium oxychloride cement, titanium extraction tailings, water resistance, dissolution rate of chloride ion, microstructure, pore structure

中图分类号:

TQ172.1

许星星, 段文涵, 陈啸洋, 关岩, 毕万利. 提钛尾渣对氯氧镁水泥耐水性的影响[J]. 硅酸盐通报, 2022, 41(5): 1742-1749.

XU Xingxing, DUAN Wenhan, CHEN Xiaoyang, GUAN Yan, BI Wanli. Effects of Titanium Extraction Tailings on Water Resistance of Magnesium Oxychloride Cement[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(5): 1742-1749.

参考文献

[1] WALLING S A, PROVIS J L. Magnesia-based cements: a journey of 150 years, and cements for the future?[J]. Chemical Reviews, 2016, 116(7): 4170-4204.
[2] 文静,余红发,吴成友,等.氯氧镁水泥水化历程的影响因素及水化动力学[J].硅酸盐学报,2013,41(5):588-596.
WEN J, YU H F, WU C Y, et al. Hydration kinetic and influencing parameters in hydration process of magnesium oxychloride cement[J]. Journal of the Chinese Ceramic Society, 2013, 41(5): 588-596 (in Chinese).
[3] LU Z Y, ZHANG J R, SUN G X, et al. Effects of the form-stable expanded perlite/paraffin composite on cement manufactured by extrusion technique[J]. Energy, 2015, 82: 43-53.
[4] 陈啸洋,毕万利,张婷婷,等.柠檬酸对氯氧镁水泥的改性[J].硅酸盐学报,2019,47(7):884-890.
CHEN X Y, BI W L, ZHANG T T, et al. Modification of magnesium oxychloride cement by citric acid[J]. Journal of the Chinese Ceramic Society, 2019, 47(7): 884-890 (in Chinese).
[5] CHEN X Y, ZHANG T T, BI W L, et al. Effect of tartaric acid and phosphoric acid on the water resistance of magnesium oxychloride (MOC) cement[J]. Construction and Building Materials, 2019, 213: 528-536.
[6] 赵华,王永维,关博文,等.粉煤灰对氯氧镁水泥早期性能的影响[J].材料导报,2015,29(18):117-121+135.
ZHAO H, WANG Y W, GUAN B W, et al. Effect of fly ash on early properties of magnesium oxychloride cement[J]. Materials Review, 2015, 29(18): 117-121+135 (in Chinese).
[7] 孙恩禹,陈啸洋.天然沸石粉对氯氧镁水泥耐水性影响研究[J].硅酸盐通报,2021,40(1):41-47.
SUN E Y, CHEN X Y. Effect of natural zeolite powder on water resistance of magnesium oxychloride cement[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(1): 41-47 (in Chinese).
[8] GUO Y Y, ZHANG Y X, SOE K, et al. Development of magnesium oxychloride cement with enhanced water resistance by adding silica fume and hybrid fly ash-silica fume[J]. Journal of Cleaner Production, 2021, 313: 127682.
[9] LI Y, LI Z J, PEI H F, et al. The influence of FeSO₄ and KH₂PO₄ on the performance of magnesium oxychloride cement[J]. Construction and Building Materials, 2016, 102: 233-238.
[10] GU K, CHEN B, BI W L, et al. Recycling of waste gypsum in preparation of magnesium oxychloride cement (MOC)[J]. Journal of Cleaner Production, 2021, 313: 127958.
[11] HE P P, POON C S, TSANG D C W. Comparison of glass powder and pulverized fuel ash for improving the water resistance of magnesium oxychloride cement[J]. Cement and Concrete Composites, 2018, 86: 98-109.
[12] 王景然,柯昌明,张锦化.提钛尾渣对硅酸盐水泥水化性能的影响[J].硅酸盐通报,2020,39(5):1511-1516.
WANG J R, KE C M, ZHANG J H. Effect of Ti-bearing blast furnace slag on hydration properties of Portland cement[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(5): 1511-1516 (in Chinese).
[13] 陈啸洋.提钛尾渣在氯氧镁/硫氧镁水泥中的应用[D].鞍山:辽宁科技大学,2019.
CHEN X Y. Application of Ti-extracted residues in magnesium oxychloride/oxysulfate cement[D]. Anshan: University of Science and Technology Liaoning, 2019 (in Chinese).
[14] WU J Y, GUAN B W, CHEN H X, et al. Effects of polycarboxylate superplasticiser on the early hydration properties of magnesium oxychloride cement[J]. Construction and Building Materials, 2020, 259: 119862.
[15] 文静.氯氧镁水泥的水化历程及动力学机理研究[D].北京:中国科学院大学,2013.
WEN J. Study on hydration mechanism and kinetic of magnesium oxychloride cement[D]. Beijing: University of Chinese Academy of Science, 2013 (in Chinese).
[16] LI K, WANG Y S, YAO N N, et al. Recent progress of magnesium oxychloride cement: manufacture, curing, structure and performance[J]. Construction and Building Materials, 2020, 255: 119381.
[17] TAN Y N, LIU Y, GROVER L. Effect of phosphoric acid on the properties of magnesium oxychloride cement as a biomaterial[J]. Cement and Concrete Research, 2014, 56: 69-74.
[18] LUO X R, FAN W Q, LI C Q, et al. Effect of hydroxyacetic acid on the water resistance of magnesium oxychloride cement[J]. Construction and Building Materials, 2020, 246: 118428.
[19] CHEN X Y, ZHANG T T, CHEESEMAN C, et al. Production of rapid-hardening magnesium oxysulfate cement containing boric acid[J]. Journal of Materials in Civil Engineering, 2022, 34(5): 04022045.