不同温度下合成沸石对铝酸钙水泥水化行为的影响

摘要/Abstract

摘要： 铝酸钙水泥的水化行为与物相组成、粉体粒径、水化温度、外加剂等因素密切相关。已有研究发现沸石结构矿物对铝酸钙水泥的水化行为影响显著,而作用机制有待进一步研究。本文采用XRD、SEM、FTIR、综合热分析以及电导率测试方法,系统研究了不同养护温度(20 ℃、25 ℃、30 ℃和40 ℃)下合成沸石对铝酸钙水泥水化行为的影响及作用机理。结果表明,合成沸石对铝酸钙水泥水化行为的影响与不同养护温度下离子浓度有关。在20 ℃养护时,铝酸钙水泥的溶解程度较低且沸石具有超高的比表面积及离子吸附能力,离子浓度难以达到饱和,延长了诱导期,从而延缓了铝酸钙水泥的水化;在25~40 ℃养护时,沸石的微孔结构和超高比表面积为水化产物提供更多成核位点,进而促进了铝酸钙水泥的水化。此外,合成沸石的引入有效消除了铝酸钙水泥在25 ℃养护时的异常凝结行为。

关键词: 铝酸钙水泥, 合成沸石, 水化行为, 养护温度, 显微结构, 电导率

Abstract: The hydration behavior of calcium aluminate cement (CAC) is mainly affected by phase composition, particle size, curing temperature, and additive, etc. Research works revealed that the zeolite-type minerals would affect the hydration behavior of CAC, while the specific mechanism should be further investigated. Therefore, the hydration behavior and the detailed mechanism ofCAC containing zeolite at various curing temperatures (20 ℃, 25 ℃, 30 ℃ and 40 ℃) were investigated, through taking XRD, SEM, FTIR, thermal analyses and electrical conductivity tests. The results show that the effect of synthetic zeolite on the hydration behavior of CAC is dominated by the ion concentration at corresponding temperature. At 20 ℃, the low solubility of CAC leads to low ion concentration, meanwhile, the ultra-high specific surface area of synthetic zeolite hinders the saturation of ions, which prolongs the induction period and thus delays the hydration of CAC. In comparison, the pore structure and ultra-high specific surface area of zeolite provide more nucleation sites for hydrates at 25~40 ℃, which facilitate the hydration of CAC. In addition, the introduction of synthetic zeolite effectively eliminates the abnormal setting behavior of CAC cured at 25 ℃.

Key words: calcium aluminate cement, synthetic zeolite, hydration behavior, curing temperature, microstructure, electrical conductivity

中图分类号:

TQ175

刘文静, 单江博, 廖宁, 李亚伟, 潘丽萍, 戴亚洁, 朱天彬. 不同温度下合成沸石对铝酸钙水泥水化行为的影响[J]. 硅酸盐通报, 2022, 41(5): 1510-1521.

LIU Wenjing, SHAN Jiangbo, LIAO Ning, LI Yawei, PAN Liping, DAI Yajie, ZHU Tianbin. Effect of Synthetic Zeolite on Hydration Behavior of Calcium Aluminate Cement at Different Temperatures[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(5): 1510-1521.

参考文献

[1] 叶国田,尚学军,张传银,等.不同因素对铝酸钙水泥水化行为的影响[J].耐火材料,2015(49):661-667.
YE G T, SHANG X J, ZHANG C Y, et al. Influence of different factors on hydration behavior of calcium aluminate cement[J]. Refractories, 2015(49): 661-667 (in Chinese).
[2] UKRAINCZYK N. Kinetic modeling of calcium aluminate cement hydration[J]. Chemical Engineering Science, 2010, 65(20): 5605-5614.
[3] KLAUS S R, NEUBAUER J, GOETZ-NEUNHOEFFER F. Hydration kinetics of CA₂ and CA—Investigations performed on a synthetic calcium aluminate cement[J]. Cement and Concrete Research, 2013, 43: 62-69.
[4] ANTONOVIČ V, KERIENE· J, BORIS R, et al. The effect of temperature on the formation of the hydrated calcium aluminate cement structure[J]. Procedia Engineering, 2013, 57: 99-106.
[5] 王亚娟,张传银,李欢欢,等.水泥粒度和养护温度对铝酸钙水泥水化行为的影响[C]//耐火材料综合学术年会暨全国不定形耐火材料学术会议.2015:658-660.
WANG Y J, ZHANG C Y, LI H H, et al. Effect of cement particle size and curing temperature on hydration behavior of calcium aluminate cement[C]//Comprehensive Academic Conference on Refractory Materials and National Academic Conference on Indeterminate Refractory Materials. 2015: 658-660 (in Chinese).
[6] CARDOSO F A, INNOCENTINI M D M, AKIYOSHI M M, et al. Effect of curing time on the properties of CAC bonded refractory castables[J]. Journal of the European Ceramic Society, 2004, 24(7): 2073-2078.
[7] SON H M, PARK S, KIM H Y, et al. Effect of CaSO₄ on hydration and phase conversion of calcium aluminate cement[J]. Construction and Building Materials, 2019, 224: 40-47.
[8] LUZ A P, PANDOLFELLI V C. CaCO₃ addition effect on the hydration and mechanical strength evolution of calcium aluminate cement for endodontic applications[J]. Ceramics International, 2012, 38(2): 1417-1425.
[9] CHEN J H, LIANG C J, LI B, et al. The effect of nano-γAl₂O₃ additive on early hydration of calcium aluminate cement[J]. Construction and Building Materials, 2018, 158: 755-760.
[10] OLIVEIRA I R, PANDOLFELLI V C. Castable matrix, additives and their role on hydraulic binder hydration[J]. Ceramics International, 2009, 35(4): 1453-1460.
[11] GENG G Q, LI J Q, YU Y S, et al. Nanometer-resolved spectroscopic study reveals the conversion mechanism of CaO·Al₂O₃·10H₂O to 2CaO·Al₂O₃·8H₂O and 3CaO·Al₂O₃·6H₂O at an elevated temperature[J]. Crystal Growth & Design, 2017, 17(8): 4246-4253.
[12] PACEWSKA B, NOWACKA M. Studies of conversion progress of calcium aluminate cement hydrates by thermal analysis method[J]. Journal of Thermal Analysis and Calorimetry, 2014, 117(2): 653-660.
[13] CONG X D, KIRKPATRICK R J. Hydration of calcium aluminate cements: a solid-state ²⁷Al NMR study[J]. Journal of the American Ceramic Society, 1993, 76(2): 409-416.
[14] CHOTARD T J, SMITH A, BONCOEUR M P, et al. Characterisation of early stage calcium aluminate cement hydration by combination of non-destructive techniques: acoustic emission and X-ray tomography[J]. Journal of the European Ceramic Society, 2003, 23(13): 2211-2223.
[15] ZHANG Y, YE G T, GU W J, et al. Conversion of calcium aluminate cement hydrates at 60 ℃ with and without water[J]. Journal of the American Ceramic Society, 2018, 101(7): 2712-2717.
[16] HUELLER F, NEUBAUER J, KAESSNER S, et al. Hydration of calcium aluminates at 60 ℃—Development paths of C₂AH_x in dependence on the content of free water[J]. Journal of the American Ceramic Society, 2019, 102(7): 4376-4387.
[17] 谷文静.养护时间和氧化铝微粉对铝酸盐水泥水化产物转化的影响[D].郑州:郑州大学,2019.
GU W J. Effect of curing time and alumina micro-powder on conversion of CAC hydrates[D]. Zhengzhou: Zhengzhou University, 2019 (in Chinese).
[18] BENSTED J. Scientific aspects of high alumina cement[J]. Cement Lime Concrete, 2004, 3: 109-133.
[19] BUSHNELL-WATSON S M, SHARP J H. On the cause of the anomalous setting behaviour with respect to temperature of calcium aluminate cements[J]. Cement and Concrete Research, 1990, 20(5): 677-686.
[20] NOWACKA M, PACEWSKA B. Enhanced conductometric method in the studies of calcium aluminate cement hydration process[J]. Cement, Wapno, Beton, 2015, 4: 225-234.
[21] 刘雅贤.不同氧化硅微粉对水泥水化和浇注料性能的影响[D].郑州:郑州大学,2018.
LIU Y X. Effect of different silica fumes on hydration of calcium aluminate cement and properties of castables[D]. Zhengzhou: Zhengzhou University, 2018 (in Chinese).
[22] 侯丹.氧化铝微粉对商品铝酸钙水泥水化凝结行为的影响[D].郑州:郑州大学,2016.
HOU D. Effect of alumina powder on hydration and setting behavior of commercial calcium aluminate cements[D]. Zhengzhou: Zhengzhou University, 2016 (in Chinese).
[23] ÖZEN S, GÖNCÜOG LU M C, LIGUORI B, et al. A comprehensive evaluation of sedimentary zeolites from Turkey as pozzolanic addition of cement- and lime-based binders[J]. Construction and Building Materials, 2016, 105: 46-61.
[24] SALEM S, SALEM A. A novel design for clean and economical manufacturing new nano-porous zeolite based adsorbent by alkali cement kiln dust for lead uptake from wastewater[J]. Journal of Cleaner Production, 2017, 143: 440-451.
[25] UZAL B, TURANLI L. Blended cements containing high volume of natural zeolites: properties, hydration and paste microstructure[J]. Cement and Concrete Composites, 2012, 34(1): 101-109.
[26] POON C S, LAM L, KOU S C, et al. A study on the hydration rate of natural zeolite blended cement pastes[J]. Construction and Building Materials, 1999, 13(8): 427-432.
[27] TRAN Y T, LEE J, KUMAR P, et al. Natural zeolite and its application in concrete composite production[J]. Composites Part B: Engineering, 2019, 165: 354-364.
[28] PACEWSKA B, NOWACKA M, ALEKNEVIČIUS M, et al. Early hydration of calcium aluminate cement blended with spent FCC catalyst at two temperatures[J]. Procedia Engineering, 2013, 57: 844-850.
[29] SHAN J B, LI Y W, LIAO N, et al. Critical roles of synthetic zeolite on the properties of ultra-low cement-bonded Al₂O₃-SiC-C castables[J]. Journal of the European Ceramic Society, 2020, 40(15): 6132-6140.
[30] OTROJ S, SAGAEIAN A, DAGHIGHI A, et al. The effect of nano-size additives on the electrical conductivity of matrix suspension and properties of self-flowing low-cement high alumina refractory castables[J]. Ceramics International, 2010, 36(4): 1411-1416.
[31] ZHANG C, YE G, SHANG X, et al. Effect of B₂O₃ on hydration behavior of calcium aluminate cement[J]. Journal of Chinese Ceramic Society, 2016, 44(8): 1161-1165.
[32] MAAROUFI M A, LECOMTE A, DILIBERTO C, et al. Thermo-hydrous behavior of hardened cement paste based on calcium aluminate cement[J]. Journal of the European Ceramic Society, 2015, 35(5): 1637-1646.
[33] CHAVDA M A, BERNAL S A, APPERLEY D C, et al. Identification of the hydrate gel phases present in phosphate-modified calcium aluminate binders[J]. Cement and Concrete Research, 2015, 70: 21-28.
[34] TARTE P. Infra-red spectra of inorganic aluminates and characteristic vibrational frequencies of AlO₄ tetrahedra and AlO₆ octahedra[J]. Spectrochimica Acta Part A: Molecular Spectroscopy, 1967, 23(7): 2127-2143.
[35] FERNÁNDEZ-CARRASCO L, PUERTAS F, BLANCO-VARELA M T, et al. Carbonatación de pastas de cemento de aluminato de calcio[J]. Materiales De Construcción, 2001, 51(263/264): 127-136.
[36] HIDALGO A, GARCÍA J L, ALONSO M C, et al. Microstructure development in mixes of calcium aluminate cement with silica fume or fly ash[J]. Journal of Thermal Analysis and Calorimetry, 2009, 96(2): 335-345.
[37] NOWACKA M, PACEWSKA B. Effect of structurally different aluminosilicates on early-age hydration of calcium aluminate cement depending on temperature[J]. Construction and Building Materials, 2020, 235: 117404.
[38] GARCIA-LODEIRO I, IRISAWA K, JIN F Y, et al. Reduction of water content in calcium aluminate cement with/out phosphate modification for alternative cementation technique[J]. Cement and Concrete Research, 2018, 109: 243-253.
[39] 李楠,顾华志,赵惠忠.耐火材料学[M].北京:冶金工业出版社,2010:291-292.
LI N, GU H Z, ZHAO H Z. Refractories[M]. Beijing: Metallurgical Industry Press, 2010: 291-292 (in Chinese).
[40] TAYLOR H F W. Cement chemistry[M]. 2nd ed. New York: Thomas Telford Publishing, 1997.
[41] DAMIDOT D, SORRENTION D, GUINIT G. Factors influencing the nucleation and growth of the hydrates in cementitious systems: an experimental approach[C]//Second International Symposium on Hydration & Setting. 1997: 30-33.
[42] 王亚娟.水泥粒度对铝酸钙水泥水化行为及浇注料性能的影响[D].郑州:郑州大学,2016:33-35.
WANG Y J. Effect of particle size of cement on hydration behavior of calcium aluminate and properties of castables[D]. Zhengzhou: Zhengzhou University, 2016: 33-35 (in Chinese).
[43] EL-GAMAL S M A, HASHEM F S, AMIN M S. Influence of carbon nanotubes, nanosilica and nanometakaolin on some morphological-mechanical properties of oil well cement pastes subjected to elevated water curing temperature and regular room air curing temperature[J]. Construction and Building Materials, 2017, 146: 531-546.
[44] SZEREMENT J, SZATANIK-KLOC A, JAROSZ R, et al. Contemporary applications of natural and synthetic zeolites from fly ash in agriculture and environmental protection[J]. Journal of Cleaner Production, 2021, 311: 127461.
[45] RASHED M N, PALANISAMY P N. Introductory chapter: adsorption and ion exchange properties of zeolites for treatment of polluted water[M]//Zeolites and Their Applications. 2018: 3-10.
[46] PINTO C A, BÜCHLER P M, DWECK J. Pozzolanic properties of a residual FCC catalyst during the early stages of cement hydration[J]. Journal of Thermal Analysis and Calorimetry, 2007, 87(3): 715-720.