响应面法优化氟硅酸铵制备白炭黑和氟化铵

摘要/Abstract

摘要： 本文以氟硅酸铵和碳酸氢铵为原料制备白炭黑和氟化铵(NH₄F)。根据单因素实验并结合Box-Behnken响应面法建立二次回归模型进行方差分析和验证,考察了液固比、配料比、反应温度、反应时间四个因素对白炭黑收率和NH₄F浓度的影响,通过响应面法优化得到较优工艺条件:液固比8,配料比5.49,反应温度76.5 ℃,反应时间49.08 min。在该工艺条件下进行验证实验得到白炭黑收率为96.90%,NH₄F浓度为2.02 mol/L,预测值与实验值无显著差异,验证了二次回归模型的可靠性。对产品白炭黑进行XRD、IR、TG-DSC、SEM、BET表征,及粒度分析和性能测试,对于产品NH₄F,采用氟离子选择性电极法测定其浓度,并对其性能进行检测。证实了白炭黑产品粒度为微米级,且是一种比表面积达316.83 m²/g的介孔材料,其中SiO₂的质量分数高达97.77%,外观、加热减量、灼烧减量、pH值、重金属含量和吸油值均达到行业标准。NH₄F产品中氟化铵含量、游离酸含量和氟硅酸盐含量均达到国家标准。

关键词: 电子废弃物, 氟硅酸铵, 白炭黑, 氟化铵, 响应面法, 工艺优化

Abstract: Ammonium hexafluorosilicate and ammonium bicarbonate as raw materials were used to prepare silica and ammonium fluoride (NH₄F).Based on the single factor experiment and Box-Behnken design response surface methodology, a quadratic regression model was established for variance analysis and verification. The influences of four single factors (liquid-solid ratio, ingredient ratio, reaction temperature and reaction time) on silica yield and NH₄F concentration were investigated. By the response surface analysis, the better process conditions are as follows: liquid-solid ratio 8, ingredient ratio 5.49, reaction temperature 76.5 ℃, reaction time 49.08 min. Under these conditions, the verification experiment was carried out. The silica yield is 96.90%, and the NH₄F concentration is 2.02 mol/L. There is no significant difference between the predicted value and the experimental value, which verifies the reliability of the quadratic regression model. XRD, IR, TG-DSC, SEM, BET characterization, particle size analysis and performance test of the product silica were carried out. The concentration of the product NH₄F was measured by the fluoride ion selective electrode method, and its performance was tested. It is confirmed that the particle size of silica product is micron-sized, and silica is a mesoporous material with specific surface area of 316.83 m²/g. The mass fraction of SiO₂ is as high as 97.77%, and the appearance, heating loss, ignition loss, pH value, heavy metal content, and oil absorption value all meet industry standards. The content of ammonium fluoride, free acid and fluorosilicate in NH₄F product all meets the national standard of the People's Republic of China.

Key words: electronic waste, ammonium hexafluorosilicate, silica, ammonium fluoride, response surface methodology, process optimization

中图分类号:

TQ127.2

马腾, 王泽琦, 任一鸣, 朱留凯, 李涛, 任保增. 响应面法优化氟硅酸铵制备白炭黑和氟化铵[J]. 硅酸盐通报, 2022, 41(3): 940-952.

MA Teng, WANG Zeqi, REN Yiming, ZHU Liukai, LI Tao, REN Baozeng. Response Surface Methodology to Optimize Process of Preparing Silica and Ammonium Fluoride from Ammonium Hexafluorosilicate[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(3): 940-952.

参考文献

[1] GALLARDO-HEREDIA S A, FLORES-GARCIA J C, TRUJILLO-VÁZQUEZ E, et al. Taguchi experimental design for films/coatings optimization of (NH₄)₂SiF₆, (NH₄)₃AlF₆, NH₄AlF₄ phases on aluminum sheet substrates by HYSY-CVD route[C]//2014-Sustainable Industrial Processing Summit. Flogen Star Outreach, 2014, 5: 241-256.
[2] OGAWA H, ARAI T, YANAGISAWA M, et al. Dry cleaning technology for removal of silicon native oxide employing hot NH₃/NF₃ exposure[J]. Japanese Journal of Applied Physics, 2002, 41(Part 1, No.8): 5349-5358.
[3] 陈吉宁,徐绍史,郭声琨.环境保护部令部令第39号国家危险废物名录[J].资源再生,2016(6):4.
CHEN J N, XU S S, GUO S K. Ministry of Environmental Protection Order No.39 National hazardous waste list[J]. Resource Recycling, 2016(6): 4 (in Chinese).
[4] KALEM S. Synthesis of ammonium silicon fluoride cryptocrystals on silicon by dry etching[J]. Applied Surface Science, 2004, 236(1/2/3/4): 336-341.
[5] 朱健,刘阳,秦绪峰.氟离子选择性电极测定地下水和自来水中微量的氟[J].广东化工,2015,42(21):169+172.
ZHU J, LIU Y, QIN X F. The determination of trace fluorine in tap water and groundwater with fluorine ion selective electrode[J]. Guangdong Chemical Industry, 2015, 42(21): 169+172 (in Chinese).
[6] 陈研研.氟离子选择电极分析技术浅析[J].南水北调与水利科技,2011(s2):99-101.
CHEN Y Y. Fluoride ion selective electrode analysis of analysis[J]. South-to-North Water Transfers and Water Science & Technology, 2011(s2): 99-101 (in Chinese).
[7] 欧阳文颖.氟硅酸钾容量法测定矿物外加剂硅粉中的二氧化硅含量[J].广东建材,2012,28(9):44-46.
OUYANG W Y. Fluorine content measured by the volume method of fluorinated silicon[J]. Guangdong Building Materials, 2012, 28(9): 44-46 (in Chinese).
[8] 董礼男,朱春要,张良芬,等.氟硅酸钾沉淀-酸碱滴定法测定超低碳碳化稻壳中二氧化硅[J].中国测试,2015,41(8):48-51.
DONG L N, ZHU C Y, ZHANG L F, et al. Determination of silicon dioxide in ultra-low carbon carbonised rice husk by potassium fluosilicate precipitation-acid-base titration method[J]. China Measurement & Test, 2015, 41(8): 48-51 (in Chinese).
[9] 宋红波,梁雨.氟硅酸钾容量法定量测试硅藻泥中二氧化硅含量[J].新型建筑材料,2019,46(12):59-61.
SONG H B, LIANG Y. The application of potassium fluosilicate volumetric method for quantitative determination of silicon dioxide content in diatom ooze[J]. New Building Materials, 2019, 46(12): 59-61 (in Chinese).
[10] 顿磊,李静静,李筠乐,等.石膏中二氧化硅的测定[J].河南建材,2020(9):38-40.
DUN L, LI J J, LI Y L, et al. Determination of silicon dioxide in gypsum[J]. Henan Building Materials, 2020(9): 38-40 (in Chinese).
[11] 卢爱军,卢芳仪.氟化钠制备新工艺[J].海湖盐与化工,2004,33(3):4-7.
LU A J, LU F Y. New preparation process of sodium fluoride[J]. Sea-Lake Salt and Chemical Industry, 2004, 33(3): 4-7 (in Chinese).
[12] 何海霞,万亚萌,陈欢哲,等.响应面法优化含锰钛白废水制备碳酸锰的工艺[J].化工进展,2019,38(6):2649-2657.
HE H X, WAN Y M, CHEN H Z, et al. Process optimization of preparation of manganese carbonate from manganese-containing titanium dioxide wastewater by response surface methodology[J]. Chemical Industry and Engineering Progress, 2019, 38(6): 2649-2657 (in Chinese).
[13] RASTOGI N K, RASHMI K R. Optimisation of enzymatic liquefaction of mango pulp by response surface methodology[J]. European Food Research and Technology, 1999, 209(1): 57-62.
[14] HU B, ZHOU K, LIU Y T, et al. Optimization of microwave-assisted extraction of oil from tiger nut (Cyperus esculentus L.) and its quality evaluation[J]. Industrial Crops and Products, 2018, 115: 290-297.
[15] 张圆圆,孟永斌,张琳,等.响应面法优化微波辅助水蒸气蒸馏法提取油樟精油工艺[J].化工进展,2020,39(s2):291-299.
ZHANG Y Y, MENG Y B, ZHANG L, et al. Optimization of microwave-assisted steam distillation extraction of Cinnamomum longepaniculatum essential oil by response surface methodology[J]. Chemical Industry and Engineering Progress, 2020, 39(s2): 291-299 (in Chinese).
[16] 薛山,肖夏,刘伯虎,等.双响应面结合Matlab法优化菠萝皮渣高抗氧化活性多酚的提取工艺[J].保鲜与加工,2020,20(6):63-71.
XUE S, XIAO X, LIU B H, et al. Extraction technique of pineapple peel residue polyphenols with high antioxidant activity by dual response surface method combined with Matlab analysis[J]. Storage and Process, 2020, 20(6): 63-71 (in Chinese).
[17] DRAPER N R. Response surface methodology: process and product optimization using designed experiments[J]. Journal of Statistical Planning and Inference, 1997, 59(1): 185-186.
[18] 周桂明,郑典模,李少飞,等.氟硅酸制备白炭黑和氟化氢铵的工艺研究[J].硅酸盐通报,2013,32(1):30-34.
ZHOU G M, ZHENG D M, LI S F, et al. Study on preparation technology of silica and ammonium bifluoride from fluosilicic acid[J]. Bulletin of the Chinese Ceramic Society, 2013, 32(1): 30-34 (in Chinese).
[19] 胡志波,郑水林,陈洋,等.沉淀白炭黑吸湿特性及动力学、热力学分析[J].化工进展,2017,36(5):1818-1824.
HU Z B, ZHENG S L, CHEN Y, et al. Adsorption characteristic of moisture by precipitated silica including kinetics and thermodynamics analysis[J]. Chemical Industry and Engineering Progress, 2017, 36(5): 1818-1824 (in Chinese).
[20] 刘成龙,许爱华,夏举佩,等.煤矸石浸渣制备白炭黑工艺优化及性能分析[J].精细化工,2019,36(11):2177-2184.
LIU C L, XU A H, XIA J P, et al. Process optimization and performance analysis for preparation of silica from coal gangue leaching residue[J]. Fine Chemicals, 2019, 36(11): 2177-2184 (in Chinese).
[21] 王杰,宋丽贤,卢忠远,等.水热辅助法制备纳米白炭黑及其表征[J].纳米科技,2011(2):63-66.
WANG J, SONG L X, LU Z Y, et al. Preparation and characterization of nano-silica by assisted hydrothermal method[J]. Nanoscience & Nanotechnology, 2011(2): 63-66 (in Chinese).
[22] 王利华.纳米白炭黑的制备及性能表征[D].沈阳:沈阳理工大学,2014.
WANG L H. Preparation and performance characterization of the nanometer white carbon black[D]. Shenyang: Shenyang Ligong University, 2014 (in Chinese).
[23] 任卫国,王建成,常丽萍,等.MTS有机改性白炭黑及其性能表征[J].人工晶体学报,2019,48(3):555-560.
REN W G, WANG J C, CHANG L P, et al. MTS organic modification and properties characterization of silica[J]. Journal of Synthetic Crystals, 2019, 48(3): 555-560 (in Chinese).
[24] JESIONOWSKI T, KRYSZTAFKIEWICZ A, URAWSKA J, et al. Novel precipitated silicas: an active filler of synthetic rubber[J]. Journal of Materials Science, 2009, 44(3): 759-769.
[25] 缪烨,孔令汉,黄溪岱,等.沉淀法白炭黑的制备及其填充SSBR/BR的研究[J].北京化工大学学报(自然科学版),2019,46(2):31-37.
MIAO Y, KONG L H, HUANG X D, et al. Preparation of precipitated silica and its use as a filler with SSBR/BR[J]. Journal of Beijing University of Chemical Technology (Natural Science Edition), 2019, 46(2): 31-37 (in Chinese).