硅酸盐通报 ›› 2022, Vol. 41 ›› Issue (2): 678-684.

尾矿制备气泡混合轻质土的力学与抗冻性能研究

段龙飞¹, 刘赫然¹, 房泽志², 于海洋³, 孔宁⁴, 王聿梁¹, 王林¹, 孙仁娟¹

1.山东大学齐鲁交通学院,济南 250000;
2.三东筑工有限公司,德州 253000;
3.山东高速岩土科技有限公司,济南 250000;
4.烟台市瑞凯环保材料有限公司,烟台 264000

收稿日期:2021-10-22 修回日期:2021-11-28 出版日期:2022-02-15 发布日期:2022-03-01
通讯作者: 孙仁娟,博士,副教授。E-mail:sunrenjuan@sdu.edu.cn
作者简介:段龙飞(1996—),男,硕士研究生。主要从事道路材料方面的研究。E-mail:18769799237@163.com
基金资助:
国家自然科学基金面上项目(51478252)

Mechanical Property and Frost Resistance of Foamed Mixture Lightweight Soil Prepared by Tailings

DUAN Longfei¹, LIU Heran¹, FANG Zezhi², YU Haiyang³, KONG Ning⁴, WANG Yuliang¹, WANG Lin¹, SUN Renjuan¹

1. School of Qilu Transportation, Shandong University, Jinan 250000, China;
2. Sandong Zhugong Co. Ltd., Dezhou 253000, China;
3. ShanDong High Speed Geotechnical Technology Co. Ltd, Jinan 250000, China;
4. Yantai Ruikai Environmental Protection Material Co., Ltd., Yantai 264000, China

Received:2021-10-22 Revised:2021-11-28 Online:2022-02-15 Published:2022-03-01

摘要/Abstract

摘要： 以尾矿制备气泡混合轻质土,研究了湿密度和尾矿质量掺量对轻质土力学和抗冻性能的影响,并研究了尾矿对轻质土气孔结构的影响。结果表明,气泡混合轻质土的抗压强度与湿密度成正相关,与尾矿掺量成负相关。当尾矿掺量达到45%(质量分数,下同)时,湿密度为700 kg/m³和800 kg/m³的轻质土抗压强度分别为0.97 MPa和1.40 MPa,相比未掺尾矿的轻质土强度分别下降约69%和66%。尾矿制备气泡混合轻质土具有良好的抗冻性,30次冻融循环中,湿密度为700 kg/m³尾矿掺量为0%~45%的轻质土抗压强度损失率均在15%以内,且抗压强度均大于0.80 MPa,提高湿密度等级可以进一步改善轻质土的抗冻性。尾矿的掺入会导致轻质土孔隙率和平均孔径增大,孔圆度降低,相比于未掺尾矿的轻质土,当尾矿掺量达到30%时,孔隙率增大3.58%、平均孔径增大16.7%、圆度值增加7.4%。

关键词: 尾矿, 气泡混合轻质土, 抗压强度, 抗冻性能, 孔结构, 路基填筑

Abstract: The foamed mixture lightweight soil was prepared by tailings. The effects of wet density and tailings concent on the mechanical property and frost resistance of lightweight soil were researched, and the effects of tailings on the pore structure of lightweight soil were researched. The results show that the compressive strength of foamed mixture lightweight soil is positively correlated with wet density and negatively correlated with tailings content. When the content of tailings reaches 45% (mass fraction, the same below), the compressive strength of light soil with 700 kg/m³ and 800 kg/m³ wet density is 0.97 MPa and 1.40 MPa respectively, which is about 69% and 66% lower than that of lightweight soil without tailings. Tailings foamed mixture lightweight soil has good frost resistance. In 30 freeze-thaw cycles, the loss rate of compressive strength of lightweight soil with 700 kg/m³ wet density of 0% to 45% tailings is less than 15%, and the compressive strength is greater than 0.80 MPa. Improving the wet density grade can further improve the frost resistance of lightweight soil. The addition of tailings will increase the porosity and average pore diameter of lightweight soil and reduce the pore roundness. Compared with the lightweight soil without tailings, when the content of tailings reaches 30%, the porosity increases by 3.58%, the average pore size increases by 16.7%, and the roundness increases by 7.4%.

Key words: tailing, foamed mixture lightweight soil, compressive strength, frost resistance, pore structure, subgrade filling

中图分类号:

U416.1

段龙飞, 刘赫然, 房泽志, 于海洋, 孔宁, 王聿梁, 王林, 孙仁娟. 尾矿制备气泡混合轻质土的力学与抗冻性能研究[J]. 硅酸盐通报, 2022, 41(2): 678-684.

DUAN Longfei, LIU Heran, FANG Zezhi, YU Haiyang, KONG Ning, WANG Yuliang, WANG Lin, SUN Renjuan. Mechanical Property and Frost Resistance of Foamed Mixture Lightweight Soil Prepared by Tailings[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(2): 678-684.

参考文献

[1] 高英力,马路,关宏信,等.矿粉气泡混合轻质土组成设计及性能试验研究[J].硅酸盐通报,2017,36(1):352-358.
GAO Y L, MA L, GUAN H X, et al. Experimental study on composition design and performance of foamed cement banking with slag powder[J]. Bulletin of the Chinese Ceramic Society, 2017, 36(1): 352-358 (in Chinese).
[2] 卢春莎.泡沫轻质土在高速公路施工中的应用[J].西部交通科技,2020(1):21-23+161.
LU C S. Application of foamed lightweight soil in expressway construction[J]. Western China Communications Science & Technology, 2020(1): 21-23+161 (in Chinese).
[3] 唐素芳.泡沫轻质土制备技术及其在高速公路中的应用[J].低碳世界,2020,10(9):120-122.
TANG S F. Preparation technology of foamed lightweight soil and its application in expressway[J]. Low Carbon World, 2020, 10(9): 120-122 (in Chinese).
[4] 李铁彬.分析水泥生产的物质消耗和环境排放[J].建材与装饰,2018(25):164-165.
LI T B. Analysis of material consumption and environmental emissions in cement production[J]. Construction Materials & Decoration, 2018(25): 164-165 (in Chinese).
[5] 宋强,张鹏,鲍玖文,等.泡沫混凝土的研究进展与应用[J].硅酸盐学报,2021,49(2):398-410.
SONG Q, ZHANG P, BAO J W, et al. Research progress and application of foam concrete[J]. Journal of the Chinese Ceramic Society, 2021, 49(2): 398-410 (in Chinese).
[6] REISI M, DADVAR S A, SHARIF A. Microstructure and mixture proportioning of non-structural foamed concrete with silica fume[J]. Magazine of Concrete Research, 2017, 69(23): 1218-1230.
[7] YAVUZ B O, KAPLAN G, GENCEL O, et al. Physico-mechanical, durability and thermal properties of basalt fiber reinforced foamed concrete containing waste marble powder and slag[J]. Construction and Building Materials, 2021, 288: 123128.
[8] 孙旭东,刘晓敏,龚裕,等.黄金尾矿建材化利用的研究现状及展望[J].金属矿山,2020(3):12-22.
SUN X D, LIU X M, GONG Y, et al. Research status and prospects for the utilization of gold tailings as building materials[J]. Metal Mine, 2020(3): 12-22 (in Chinese).
[9] TANG L, LIU X M, WANG X Q, et al. Statistical analysis of tailings ponds in China[J]. Journal of Geochemical Exploration, 2020, 216: 106579.
[10] 张肖艳,宋强,李辉,等.铁尾矿粉对C40混凝土性能的影响[J].硅酸盐通报,2013,32(12):2559-2563.
ZHANG X Y, SONG Q, LI H, et al. Effect of iron tailings powder on properties of C40 concrete[J]. Bulletin of the Chinese Ceramic Society, 2013, 32(12): 2559-2563 (in Chinese).
[11] 朴春爱,王栋民,张力冉,等.铁尾矿粉对混凝土耐久性能的影响[J].硅酸盐通报,2016,35(10):3295-3300.
PIAO C N, WANG D M, ZHANG L R, et al. Effect of iron ore tailings powder on concrete durability[J]. Bulletin of the Chinese Ceramic Society, 2016, 35(10): 3295-3300 (in Chinese).
[12] 范定强,水中和,余睿,等.铅锌尾矿回收制备环保型超高性能混凝土研究[J].硅酸盐通报,2018,37(7):2231-2236.
FAN D Q, SHUI Z H, YU R, et al. Preparation of eco-friendly ultra-high performance concrete by lead-zinc tailings[J]. Bulletin of the Chinese Ceramic Society, 2018, 37(7): 2231-2236 (in Chinese).
[13] ESMAEILI J, ASLANI H. Use of copper mine tailing in concrete: strength characteristics and durability performance[J]. Journal of Material Cycles and Waste Management, 2019, 21(3): 729-741.
[14] KATHIRVEL P, KWON S J, LEE H S, et al. Graphite ore tailings as partial replacement of sand in concrete[J]. ACI Materials Journal, 2018, 115(3): 481-492.
[15] 刘润清,欧阳鹏,黄紫妍,等.气孔特征对泡沫混凝土耐干湿循环能力的影响[J].混凝土,2014(11):38-43.
LIU R Q, OUYANG P, HUANG Z Y, et al. Effect of air-void characteristics on dry-wet resistance of foam concrete[J]. Concrete, 2014(11): 38-43 (in Chinese).