摘要/Abstract

摘要： 采用纳米强化再生骨料表面的措施来改善再生骨料性能,建立多相再生混凝土细观数值模型,进行氯离子在再生混凝土内部传输的模拟和试验验证,并预测了氯盐环境下再生骨料表面强化混凝土耐久性寿命。结果表明:数值模拟得到的氯离子在再生混凝土内的分布与试验结果吻合较好;同一深度处,越靠近骨料表面,氯离子浓度越大,其中未强化再生骨料表面的氯离子浓度要大于强化再生骨料表面的氯离子浓度;增加保护层厚度可以有效提高纳米强化再生混凝土在氯盐环境下的耐久性寿命;随纳米包裹层氯离子扩散系数的减小,再生混凝土的耐久性寿命有所增加。

关键词: 再生混凝土, 骨料强化, 随机分布, 细观模型, 氯盐侵蚀, 寿命预测

Abstract: The performance of recycled aggregate (RA) was improved by pre-soaking the RA in nano-SiO₂ solution to enhance its weak surface. A mesoscopic model of multi-phase for recycled aggregate concrete (RAC) was established to simulate the chloride ion transportation in concrete. Experiments of RAC immersing in chloride ion solution were carried out to verify the simulation results, and service life of RAC exposed in chloride ion environment was predicted. The results indicate that the mesoscopic numerical simulation results are in good agreement with the experimental results. At the same depth, the closer to the aggregate surface, the greater the chloride ion concentration, and the concentration of chloride ion on the surface of un-strengthened RA is higher than that on the surface of strengthened RA. Increasing the thickness of protective layer effectively improves the durability life of the nano-strengthening RAC in chloride environment. The durability life of RAC increases a little with the decrease of chloride ion diffusion coefficient of nano-coating layer.

Key words: recycled aggregate concrete, aggregate strengthening, random distribution, mesoscopic model, chloride erosion, life prediction

中图分类号:

TU528.45

延永东, 刘甲琪, 徐鹏飞, 王鑫. 考虑骨料表面强化的再生混凝土内氯离子传输细观数值模拟[J]. 硅酸盐通报, 2022, 41(2): 441-449.

YAN Yongdong, LIU Jiaqi, XU Pengfei, WANG Xin. Mesoscopic Numerical Simulation of Chloride Ion Transportation in Recycled Aggregate Concrete with Surface Strengthened Aggregate[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(2): 441-449.

参考文献

[1] 刘惠,王震,郝亚利,等.再生粗骨料品质对混凝土抗溶蚀性能的影响[J/OL].土木与环境工程学报(中英文):1-7[2021-06-15].http://kns.cnki.net/kcms/detail/50.1218.tu.20210322.1022.002.html.
LIU H, WANG Z, HAO Y L, et al. Effect of quality of recycled coarse aggregate on the corrosion resistance of concrete[J/OL]. Journal of Civil and Environmental Engineering: 1-7 [2021-06-15]. http://kns.cnki.net/kcms/detail/50.1218.tu.20210322.1022.002.html (in Chinese).
[2] 魏达,朱平华,王新杰,等.再生粗骨料附着砂浆含量对再生混凝土抗冻耐久性的影响[J].硅酸盐通报,2021,40(3):765-774.
WEI D, ZHU P H, WANG X J, et al. Effect of attached mortar content of recycled coarse aggregate on frost resistance durability of recycled aggregate concrete[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(3): 765-774 (in Chinese).
[3] 肖建庄,马旭伟,刘琼,等.全再生混凝土概念的衍化与研究进展[J].建筑科学与工程学报,2021,38(2):1-15.
XIAO J Z, MA X W, LIU Q, et al. Evolvement and research progress of concept for full recycled concrete[J]. Journal of Architecture and Civil Engineering, 2021, 38(2): 1-15 (in Chinese).
[4] AL-BAYATI H K A, DAS P K, TIGHE S L, et al. Evaluation of various treatment methods for enhancing the physical and morphological properties of coarse recycled concrete aggregate[J]. Construction and Building Materials, 2016, 112: 284-298.
[5] SHI C J, LI Y K, ZHANG J K, et al. Performance enhancement of recycled concrete aggregate: a review[J]. Journal of Cleaner Production, 2016, 112: 466-472.
[6] KAZMI S M S, MUNIR M J, WU Y F, et al. Effect of recycled aggregate treatment techniques on the durability of concrete: a comparative evaluation[J]. Construction and Building Materials, 2020, 264: 120284.
[7] 郑建岚,胡伟,王雅思.CO₂强化再生粗骨料对混凝土中钢筋锈蚀的影响[J].武汉大学学报(工学版),2020,53(3):225-231.
ZHENG J L, HU W, WANG Y S. Influence of CO₂-enhanced recycled coarse aggregate on corrosion performance of rebar in concrete[J]. Engineering Journal of Wuhan University, 2020, 53(3): 225-231 (in Chinese).
[8] SANTOS W F, QUATTRONE M, JOHN V M, et al. Roughness, wettability and water absorption of water repellent treated recycled aggregates[J]. Construction and Building Materials, 2017, 146: 502-513.
[9] SPAETH V, TEGGUER A D. Improvement of recycled concrete aggregate properties by polymer treatments[J]. International Journal of Sustainable Built Environment, 2013, 2(2): 143-152.
[10] GRABIEC A M, KLAMA J, ZAWAL D, et al. Modification of recycled concrete aggregate by calcium carbonate biodeposition[J]. Construction and Building Materials, 2012, 34: 145-150.
[11] 李文贵,龙初,罗智予,等.纳米改性再生骨料混凝土破坏机理研究[J].建筑材料学报,2017,20(5):685-691+786.
LI W G, LONG C, LUO Z Y, et al. Investigation on failure mechanism of nanomodified recycled aggregate concrete[J]. Journal of Building Materials, 2017, 20(5): 685-691+786 (in Chinese).
[12] 林腾玮,刘孙涛,罗素蓉,等.纳米SiO₂改性再生混凝土抗氯离子的渗透性能实验[J].福州大学学报(自然科学版),2019,47(4):533-537.
LIN T W, LIU S T, LUO S R, et al. Experimental study on chlorine ion penetation resistance of nano-SiO₂ modified recycled concrete[J]. Journal of Fuzhou University (Natural Science Edition), 2019, 47(4): 533-537 (in Chinese).
[13] HOSSEINI P, BOOSHEHRIAN A, MADARI A. Developing concrete recycling strategies by utilization of nano-SiO₂ particles[J]. Waste and Biomass Valorization, 2011, 2(3): 347-355.
[14] 肖建庄,陈祥磊,李标,等.纳米SiO₂和粉煤灰复掺对再生混凝土性能的影响[J].建筑科学与工程学报,2020,37(1):26-32.
XIAO J Z, CHEN X L, LI B, et al. Effect of mixed nano-SiO₂ and fly ash on properties of recycled aggregate concrete[J]. Journal of Architecture and Civil Engineering, 2020, 37(1): 26-32 (in Chinese).
[15] 张建建.荷载作用下氯离子在混凝土中的传输特性[D].石家庄:石家庄铁道大学,2019.
ZHANG J J. Characteristic of chloride ion transport in concrete under loading effect[D]. Shijiazhuang: Shijiazhuang Tiedao University, 2019 (in Chinese).
[16] SUN G W, ZHANG Y S, SUN W, et al. Multi-scale prediction of the effective chloride diffusion coefficient of concrete[J]. Construction and Building Materials, 2011, 25(10): 3820-3831.
[17] 应敬伟,肖建庄.模型再生混凝土氯离子非线性扩散细观仿真[J].建筑材料学报,2013,16(5):863-868.
YING J W, XIAO J Z. Meso-level simulation of chloride nonlinear diffusion in modeled recycled aggregate concrete[J]. Journal of Building Materials, 2013, 16(5): 863-868 (in Chinese).
[18] 肖建庄,卢登,马志鸣.考虑再生粗骨料随机分布的混凝土氯离子扩散细观数值模拟[J].东南大学学报(自然科学版),2014,44(6):1240-1245.
XIAO J Z, LU D, MA Z M. Mesoscopic numerical simulation on chloride diffusion in concrete with random distributed recycled coarse aggregate[J]. Journal of Southeast University (Natural Science Edition), 2014, 44(6): 1240-1245 (in Chinese).
[19] WALRAVEN J C, REINHARDT H W. Theory and experiments on the mechanical behaviour of cracks in plain and reinforced concrete subjected to shear loading[J]. NASA STI/Recon Technical Report N, 1981.
[20] 沈大钦.再生骨料混凝土性能的研究[D].北京:北京交通大学,2006.
SHEN D Q. Study of recycled aggregate concrete[D]. Beijing: Beijing Jiaotong University, 2006 (in Chinese).
[21] 袁飚.再生混凝土抗压抗拉强度取值研究[D].上海:同济大学,2007.
YUAN B. On values of compressive strength and tensile strength of recycled aggregate concrete[D]. Shanghai: Tongji University, 2007 (in Chinese).
[22] 肖建庄,刘琼,李文贵,等.再生混凝土细微观结构和破坏机理研究[J].青岛理工大学学报,2009,30(4):24-30.
XIAO J Z, LIU Q, LI W G, et al. On the micro-and meso-structure and failure mechanism of recycled concrete[J]. Journal of Qingdao Technological University, 2009, 30(4): 24-30 (in Chinese).
[23] DU X L, JIN L, MA G W. A meso-scale numerical method for the simulation of chloride diffusivity in concrete[J]. Finite Elements in Analysis and Design, 2014, 85: 87-100.
[24] 金伟良,袁迎曙,卫军.氯盐环境下混凝土结构耐久性理论与设计方法[M].北京:科学出版社,2011.
JIN W L, YUAN Y S, WEI J, et al. Durability Theory and design method of concrete structure in chloride environment[M]. Beijing: Science Press, 2011 (in Chinese).
[25] 张伟平,王浩,顾祥林.粗骨料随机分布对混凝土导热性能的影响[J].建筑材料学报,2017,20(2):168-173+197.
ZHANG W P, WANG H, GU X L. Effects of randomly distributed aggregates on thermal properties of concrete[J]. Journal of Building Materials, 2017, 20(2): 168-173+197 (in Chinese).
[26] 徐鹏飞.氯盐环境下纳米强化再生骨料混凝土梁耐久性能提升研究[D].镇江:江苏大学,2020.
XU P F. Study on the durability improvement of nano-reinforced recycled aggregate concrete beams in chloride environment[D]. Zhenjiang: Jiangsu University, 2020 (in Chinese).
[27] 党娜娜,彭一江,周化平,等.基于随机骨料模型的再生混凝土材料细观损伤分析方法[J].固体力学学报,2013,33(s1):58-62.
DANG N N, PENG Y J, ZHOU H P, et al. A meso-mechanical damage method base on random aggregate model for recycled aggregate concrete[J]. Chinese Journal of Solid Mechanics, 2013, 33(s1): 58-62 (in Chinese).
[28] 陆春华.钢筋混凝土受弯构件开裂性能及耐久性能研究[D].杭州:浙江大学,2011.
LU C H. Flexural and durability performance of RC members with cracks[D]. Hangzhou: Zhejiang University, 2011 (in Chinese).
[29] 中国工程院土木水利与建筑学部.混凝土结构耐久性设计与施工指南[R].北京:中国建筑工业出版社,2004.
Department of Civil, Water and Architecture, Chinese Academy of Engineering. Guide for durability design and construction of concrete structures[R]. Beijing: China Construction Industry Press, 2004 (in Chinese).
[30] 郭瑞琦,郭增伟,施跃毅.钢筋初始锈蚀时刻的氯离子临界浓度研究综述[J].硅酸盐通报,2020,39(9):2706-2713.
GUO R Q, GUO Z W, SHI Y Y. Review on research of critical chloride concentration in initial corrosion time of steel bar[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(9): 2706-2713 (in Chinese).
[31] 延永东.氯离子在损伤及开裂混凝土内的输运机理及作用效应[D].杭州:浙江大学,2011.
YAN Y D. Transportation of chloride ions in damaged and cracked concrete and its action[D]. Hangzhou: Zhejiang University, 2011 (in Chinese).