基于粒形分析的再生细骨料颗粒特性和制备砂浆性能研究

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (12): 4061-4069.

基于粒形分析的再生细骨料颗粒特性和制备砂浆性能研究

石艳柯^1,2, 张洛兵¹, 王宇航¹, 刘巍巍², 侯荣彬^1,2, 马军涛^1,2

1.华北水利水电大学土木与交通学院,郑州 450045;
2.黄河水利科学研究院,水利部堤防安全与病害防治工程技术研究中心,郑州 450003

出版日期:2021-12-15 发布日期:2022-01-07
通讯作者: 马军涛,博士,副教授。E-mail:majuntao@ncwu.edu.cn
作者简介:石艳柯(1983—),男,博士,副教授。主要从事材料本构关系和工程防灾减灾研究。E-mail:shiyanke@ncwu.edu.cn
基金资助:
国家自然科学基金(11502081,52004098);水利部堤防安全与病害防治工程技术研究中心开放课题(DFZX202008,2019005);河南省重点研发与推广专项(212102310951)

Particle Characteristics of Recycled Fine Aggregate and Properties of Prepared Mortar Based on Particle Shape Analysis

SHI Yanke^1,2, ZHANG Luobing¹, WANG Yuhang¹, LIU Weiwei², HOU Rongbin^1,2, MA Juntao^1,2

1. School of Civil Engineering and Communication, North China University of Water Resources and Electric Power, Zhengzhou 450045, China;
2. MWR Center for Levee Safety and Disease Prevention Research, Yellow River Institute of Hydraulic Research, Zhengzhou 450003, China

Online:2021-12-15 Published:2022-01-07

摘要/Abstract

摘要： 运用数字图像技术分析再生细骨料的颗粒形貌参数,以此为基础对再生细骨料的堆积密度、吸水率、压碎值等颗粒特性开展研究,并对再生细骨料制备水泥砂浆的工作性能和力学性能进行了分析。实验结果表明,再生细骨料与同级配的标准砂和天然河砂相比,钝度、长宽比、坚固度和球度等指标均相对较低,压碎值和吸水率显著增加;使用再生细骨料制备水泥砂浆时,质量替代量达到30%时流动度明显下降,质量替代量达到40%时抗压强度和峰值应力显著下降。

关键词: 再生细骨料, 颗粒形貌, 颗粒特性, 砂浆, 流动度, 抗压强度

Abstract: Based on the analysis of the particle morphology parameters of recycled fine aggregate by the digital image technology, the particle characteristics such as bulk density, water absorption and crushing value of recycled fine aggregate were studied, and the workability and mechanical properties of cement prepared with the recycled fine aggregates were analyzed. The results show that compared with the standard sand and natural river sand at the same grade, the parameters such as dullness, aspect ratio, solidity and roundness of recycled fine aggregate are decreased, and the crushing value and water absorption are significantly increased. The fluidity of the prepared cement mortar with recycled fine aggregate decreases significantly when the mass substitution amount of recycled fine aggregate reaches 30%, and the compressive strength and peak stress decrease significantly when the mass substitution amount of recycled fine aggregate reaches 40%.

Key words: recycled fine aggregate, particle morphology, particle characteristic, mortar, fluidity, compressive strength

中图分类号:

TU528

石艳柯, 张洛兵, 王宇航, 刘巍巍, 侯荣彬, 马军涛. 基于粒形分析的再生细骨料颗粒特性和制备砂浆性能研究[J]. 硅酸盐通报, 2021, 40(12): 4061-4069.

SHI Yanke, ZHANG Luobing, WANG Yuhang, LIU Weiwei, HOU Rongbin, MA Juntao. Particle Characteristics of Recycled Fine Aggregate and Properties of Prepared Mortar Based on Particle Shape Analysis[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(12): 4061-4069.

参考文献

[1] 崔素萍,刘晓.建筑废弃物资源化关键技术及发展战略[M].北京:科学出版社,2017.
CUI S P, LIU X. Key technologies and development strategies of construction waste recycling[M]. Beijing: Science Press, 2017 (in Chinese).
[2] 卢洪波.建筑垃圾处理与处置[M].郑州:河南科学技术出版社,2016.
LU H B, LIAO Q Q, SI C J. Construction waste treatment and disposal[M]. Zhengzhou: Henan Science and Technology Press, 2016 (in Chinese).
[3] 李北星,王威,陈梦义,等.粗骨料的等轴率、圆度和球度及其相互关系[J].建筑材料学报,2015,18(4):531-536.
LI B X, WANG W, CHEN M Y, et al. Isometric ratio, roundness and sphericity of coarse aggregates and their relationship[J]. Journal of Building Materials, 2015, 18(4): 531-536 (in Chinese).
[4] 曾晓辉,戴亚鹏,瞿福林,等.基于图像处理技术的石灰石机制砂形貌研究[J].西南交通大学学报,2017,52(1):69-74.
ZENG X H, DAI Y P, QU F L, et al. Morphology of limestone manufactured sand based on image processing technology[J]. Journal of Southwest Jiaotong University, 2017, 52(1): 69-74 (in Chinese).
[5] 钟国才,范志,李文科,等.机制砂形貌特性的测试与分析[J].贵州大学学报(自然科学版),2020,37(1):52-58.
ZHONG G C, FAN Z, LI W K, et al. Test and analysis of morphology characteristics of mechanism sand[J]. Journal of Guizhou University (Natural Sciences), 2020, 37(1): 52-58 (in Chinese).
[6] 靳月清,刘巍,杨希涛.基于球形度比的精品机制砂粒形特征研究[J].铁道建筑,2020,60(2):148-151.
JIN Y Q, LIU W, YANG X T. Research on the shape characteristics of fine machine-made sand based on sphericity ratio[J]. Railway Engineering, 2020, 60(2): 148-151 (in Chinese).
[7] ZEGHICHI L, BENGHAZI Z, BAALI L. The effect of the kind of sands and additions on the mechanical behaviour of S.C.C[J]. Physics Procedia, 2014, 55: 485-492.
[8] ROCCO C G, ELICES M. Effect of aggregate shape on the mechanical properties of a simple concrete[J]. Engineering Fracture Mechanics, 2009, 76(2): 286-298.
[9] 黄晓峰.粗骨料形状对混凝土物理和力学性能的影响[D].杭州:浙江工业大学,2010.
HUANG X F. Effect of coarse aggregate shape on the physicomechanical properties of concrete[D]. Hangzhou: Zhejiang University of Technology, 2010 (in Chinese).
[10] 魏艺博,陈雷,于蕾,等.机制砂颗粒特性对胶砂综合性能的影响研究[J].公路交通科技(应用技术版),2018,14(7):137-138.
WEI Y B, CHEN L, YU L, et al. Research on the influence of the particle characteristics of machine-made sand on the comprehensive performance of mortar[J]. Highway and Transportation Science and Technology (Applied Technology Edition), 2018, 14(7): 137-138 (in Chinese).
[11] 邢心魁,刘晶,孙冠晓,等.粗骨料形状对混凝土力学性质的影响[J].混凝土,2014(2):61-63+67.
XING X K, LIU J, SUN G X, et al. Influence of different shape of coarse aggregate on concrete mechanical properties[J]. Concrete, 2014(2): 61-63+67 (in Chinese).
[12] 史巍,侯景鹏.再生混凝土技术及其配合比设计方法[J].建筑技术开发,2001,28(8):18-20.
SHI W, HOU J P. Technology and mix design on recycled concrete[J]. Building Technique Development, 2001, 28(8): 18-20 (in Chinese).
[13] 肖建庄,孙振平,李佳彬,等.废弃混凝土破碎及再生工艺研究[J].建筑技术,2005,36(2):141-144.
XIAO J Z, SUN Z P, LI J B, et al. Studies on crushing and regenerating technology of waste concrete[J]. Architecture Technology, 2005, 36(2): 141-144 (in Chinese).
[14] 张领雷.废弃混凝土全组分建材化再生利用的关键技术研究[D].徐州:中国矿业大学,2018.
ZHANG L L. Key technologies on reuse and reactivation in building materials of all components of waste concrete[D]. Xuzhou: China University of Mining and Technology, 2018 (in Chinese).
[15] 刘天杰,刘新飞.再生骨料比表面积和形状指数测定方法计算与分析[J].长江科学院院报,2020,37(5):170-173+179.
LIU T J, LIU X F. Determining specific surface area and shape index of recycled aggregate: calculation and analysis[J]. Journal of Yangtze River Scientific Research Institute, 2020, 37(5): 170-173+179 (in Chinese).
[16] 苏栋,吴炯,肖政健,等.基于三维扫描和球谐分析的骨料和再生骨料颗粒形状表征[J].沈阳建筑大学学报(自然科学版),2020,36(5):827-835.
SU D, WU J, XIAO Z J, et al. Geometrical characterization of natural and recycled aggregate particles based on 3D scanning and spherical harmonic analyses[J]. Journal of Shenyang Jianzhu University (Natural Science), 2020, 36(5): 827-835 (in Chinese).
[17] NAGATAKI S, GOKCE A, SAEKI T, et al. Assessment of recycling process induced damage sensitivity of recycled concrete aggregates[J]. Cement and Concrete Research, 2004, 34(6): 965-971.
[18] FAN C C, HUANG R, HWANG H, et al. Properties of concrete incorporating fine recycled aggregates from crushed concrete wastes[J]. Construction and Building Materials, 2016, 112: 708-715.
[19] 邢成,丁涛,周捍东,等.粒度粒形分布特点对板材锯切和油漆砂光粉尘流动性的影响[J].林业科学,2018,54(12):142-148.
XING C, DING T, ZHOU H D, et al. Influence of size and shape distribution on the flowability of particles emitted during panel cutting and paint sanding[J]. Scientia Silvae Sinicae, 2018, 54(12): 142-148 (in Chinese).