可控低强度材料(CLSM)性能评价方法分析

摘要/Abstract

摘要： 可控低强度材料(CLSM)是一种高流动性、可控低强的新型充填材料,被广泛应用于工程回填、道路基层、管道垫层等工程。目前,我国尚无CLSM性能测试标准,主要借鉴国外标准与混凝土、砂浆等材料相关评价方法,亟待制定合理、统一、系统的性能测试方法与标准,规范和促进CLSM大规模推广应用。本文综述了现有CLSM相关工作性能、力学性能、环境影响、耐久性等方面的测试方法,从测试原理、实验参数、优缺点等方面进行了对比分析,为CLSM性能测试提供依据,也为我国制定和完善CLSM标准体系提供参考。

关键词: 充填材料, 可控低强度材料, 性能测试方法, 测试原理, 实验参数, 测试标准

Abstract: Controlled low-strength material (CLSM) is a new filling material with high flowability, controllable and low strength, which is widely used in engineering backfills, pavement bases, conduit bedding and other projects. At present, there is no performance test method and standards for CLSM in China and it mainly draws lessons from the relevant evaluation methods of foreign standards and materials such as concrete and mortar, and it is urgent to formulate a reasonable, unified and systematic performance test method to standardize and promote the large-scale popularization and application of CLSM. This paper summarized the existing test methods of CLSM in terms of workability, mechanical properties, environmental impact and durability, and made a comparative analysis from the aspects of test principle, experimental parameters, advantages and disadvantages, so as to provide a basis for the performance test of CLSM and a reference for the formulation and perfection of CLSM standard system in China.

Key words: filling material, controlled low-strength material, performance test method, test principle, experimental parameter, test standard

中图分类号:

X705

汪伟, 张同生, 陈灿峰, 吴正德, 韦江雄, 余其俊. 可控低强度材料(CLSM)性能评价方法分析[J]. 硅酸盐通报, 2021, 40(11): 3634-3643.

WANG Wei, ZHANG Tongsheng, CHEN Canfeng, WU Zhengde, WEI Jiangxiong, YU Qijun. Performance Evaluation Methods of Controlled Low-Strength Materials (CLSM)[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(11): 3634-3643.

参考文献

[1] ACI 229R. Controlled low-strength materials (CLSM)[R]. Farmington Hills: American Concrete Institute, 2013.
[2] SIDDIQUE R. Utilization of waste materials and by-products in producing controlled low-strength materials[J]. Resources, Conservation and Recycling, 2009, 54(1): 1-8.
[3] Standard test method for flow consistency of controlled low strength material (CLSM): ASTM D6103—2017[S]. West Conshohocken: The American Society for Testing and Materials, 2017.
[4] LACHEMI M, HOSSAIN K M A, SHEHATA M, et al. Controlled low strength materials incorporating cement kiln dust from various sources[J]. Cement and Concrete Composites, 2008, 30(5): 381-392.
[5] 中华人民共和国住房和城乡建设部.建筑砂浆基本性能试验方法标准:JGJ/T 70—2009[S].北京:中国建筑工业出版社,2009.
Ministry of Housing and Urban-Rural Development of the People's Republic of China. Standard for test method of performance on building mortar: JGJ/T 70—2009[S]. Beijing: China Building Industry Press, 2009 (in Chinese).
[6] QIAN J S, HU Y Y, ZHANG J K, et al. Evaluation the performance of controlled low strength material made of excess excavated soil[J]. Journal of Cleaner Production, 2019, 214: 79-88.
[7] Standard test method for bleeding of concrete: ASTM C232—2014[S]. West Conshohocken: ASTM International, 2014.
[8] Standard test method for expansion and bleeding of freshly mixed grouts for preplaced-aggregate concrete in the laboratory: ASTM C 940—2010[S]. West Conshohocken: ASTM International, 2010.
[9] Standard test method for ball drop on controlled low strength material (CLSM) to determine suitability for load application: ASTM D6024—2016[S]. West Conshohocken: ASTM International, 2016.
[10] Standard test method for time of setting of concrete mixtures by penetration resistance: ASTM-C403/C403M-16[S]. West Conshohocken: ASTM International, 2008.
[11] 刘萌.建筑渣土制备可控低强材料及性能研究[D].北京:北京建筑大学,2016.
LIU M. Preparation and properties of controlled low-strength materials produced by construction waste[D]. Beijing: Beijing University of Civil Engineering and Architecture, 2016 (in Chinese).
[12] DO T M, KIM Y S, DANG M Q. Influence of curing conditions on engineering properties of controlled low strength material made with cementless binder[J]. KSCE Journal of Civil Engineering, 2017, 21(5): 1774-1782.
[13] TÜRKEL S. Strength properties of fly ash based controlled low strength materials[J]. Journal of Hazardous Materials, 2007, 147(3): 1015-1019.
[14] 王帅.利用地铁盾构渣土制备可控低强度材料的研究[D].郑州:郑州大学,2020.
WANG S. Study on controllable low-strength materials made from subway shield muck[D]. Zhengzhou: Zhengzhou University, 2020 (in Chinese).
[15] LIM S, LEE W, CHOO H, et al. Utilization of high carbon fly ash and copper slag in electrically conductive controlled low strength material[J]. Construction and Building Materials, 2017, 157: 42-50.
[16] MNEINA A, SOLIMAN A M, AHMED A, et al. Engineering properties of controlled low-strength materials containing treated oil sand waste[J]. Construction and Building Materials, 2018, 159: 277-285.
[17] ETXEBERRIA M, AINCHIL J, PÉREZ M E, et al. Use of recycled fine aggregates for control low strength materials (CLSMs) production[J]. Construction and Building Materials, 2013, 44: 142-148.
[18] QIAN J S, SHU X, DONG Q, et al. Laboratory characterization of controlled low-strength materials[J]. Materials & Design, 2015, 65: 806-813.
[19] KIM Y S, DO T M, KIM H K, et al. Utilization of excavated soil in coal ash-based controlled low strength material (CLSM)[J]. Construction and Building Materials, 2016, 124: 598-605.
[20] LEE N K, KIM H K, PARK I S, et al. Alkali-activated, cementless, controlled low-strength materials (CLSM) utilizing industrial by-products[J]. Construction and Building Materials, 2013, 49: 738-746.
[21] NAGANATHAN S, RAZAK H A, HAMID S N A. Properties of controlled low-strength material made using industrial waste incineration bottom ash and quarry dust[J]. Materials & Design, 2012, 33: 56-63.
[22] Standard test method for preparation and testing of controlled low strength material (CLSM) test cylinders: ASTM D4832—2010[S]. West Conshohocken: The American Society for Testing and Materials, 2010.
[23] 中华人民共和国交通运输部.公路工程无机结合料稳定材料试验规程:JTG E51—2009[S].北京:人民交通出版社,2009.
Ministry of Transport of the People's Republic of China. Test methods of materials stabilized with inorganic binders for highway engineering: JTG E51—2009[S]. Beijing: China Communications Press, 2009 (in Chinese).
[24] Geotechnical investigation and testing-laboratory testing of soil-Part 8: unconsolidated undrained triaxial test: DIN ISO/TS 17892-8—2005[S]. German Version CEN ISO/TS 17892-8, 2004.
[25] Methods of test for soils for civil engineering purposes-Part 4: compaction-related tests: BS 1377-4—1990[S]. London: BSI Publications, 1990.
[26] 中华人民共和国交通部.公路土工试验规程:JTG E40—2007[S].北京:人民交通出版社,2007.
Ministry of Transport of the People's Republic of China. Test methods of soils for highway engineering: JTG E40—2007[S]. Beijing: China Communications Press, 2007 (in Chinese).
[27] Standard test method for splitting tensile strength of cylindrical concrete specimens: ASTM C496/C496M—17[S]. West Conshohocken: ASTM International, 2017.
[28] OKUYUCU O, JAYAWICKRAMA P, SENADHEERA S. Mechanical properties of steel fiber-reinforced self-consolidating controlled low-strength material for pavement base layers[J]. Journal of Materials in Civil Engineering, 2019, 31(9): 04019177.
[29] ZHANG J X, WANG J G, LI X H, et al. Rapid-hardening controlled low strength materials made of recycled fine aggregate from construction and demolition waste[J]. Construction and Building Materials, 2018, 173: 81-89.
[30] BASSANI M, BERTOLA F, BIANCHI M, et al. Environmental assessment and geomechanical properties of controlled low-strength materials with recycled and alternative components for cements and aggregates[J]. Cement and Concrete Composites, 2017, 80: 143-156.
[31] KIM Y S, DINH B H, DO T M, et al. Development of thermally enhanced controlled low-strength material incorporating different types of steel-making slag for ground-source heat pump system[J]. Renewable Energy, 2020, 150: 116-127.
[32] ALIZADEH V. New approach for proportioning of controlled low strength materials[J]. Construction and Building Materials, 2019, 201: 871-878.
[33] WU H, HUANG B S, SHU X, et al. Utilization of solid wastes/byproducts from paper mills in controlled low strength material (CLSM)[J]. Construction and Building Materials, 2016, 118: 155-163.
[34] BOUZALAKOS S, DUDENEY A W L, CHAN B K C. Formulating and optimising the compressive strength of controlled low-strength materials containing mine tailings by mixture design and response surface methods[J]. Minerals Engineering, 2013, 53: 48-56.
[35] WANG L, ZOU F L, FANG X L, et al. A novel type of controlled low strength material derived from alum sludge and green materials[J]. Construction and Building Materials, 2018, 165: 792-800.
[36] 贾冬冬.低强度流动性建筑垃圾回填材料基本性能研究[D].北京:北京工业大学,2014.
JIA D D. Study on performance of low-strength flowable backfill materials made of construction waste[D]. Beijing: Beijing University of Technology, 2014 (in Chinese).
[37] 雷霆.建筑垃圾低强度流动化回填材料性能优化及中试研究[D].北京:北京工业大学,2017.
LEI T. Study on performance optimization and pilotscale experiment of low-strength flowable backfill materials made of construction waste[D]. Beijing: Beijing University of Technology, 2017 (in Chinese).
[38] NAGANATHAN S, RAZAK H A, HAMID S N. Effect of Kaolin addition on the performance of controlled low-strength material using industrial waste incineration bottom ash[J]. Waste Management & Research, 2010, 28(9): 848-860.
[39] Standard test method for permeability of granular soils (constant head): ASTM D2434—1968 (2006)[S]. West Conshohocken: ASTM International, 2006.
[40] Testing concrete-Part 208: recommendations for the determination of the initial surface absorption of concrete: BS 1881-208—1996[S]. London: BSI Publications, 1996.
[41] 贺智敏,龙广成,谢友均,等.蒸养混凝土的毛细吸水特性研究[J].建筑材料学报,2012,15(2):190-195.
HE Z M, LONG G C, XIE Y J, et al. Water sorptivity of steam curing concrete[J]. Journal of Building Materials, 2012, 15(2): 190-195 (in Chinese).
[42] Standard test methods for freezing and thawing compacted soil-cement mixtures: ASTM D560—2003[S]. West Conshohocken: ASTM International, 2003.
[43] 刘卫东,张东芹,王依民.混凝土结构抗冻性超声检测方法的研究[J].水利学报,2003,34(3):125-128.
LIU W D, ZHANG D Q, WANG Y M. Study on the ultrasonic checking method for frost resistance in concrete structure[J]. Journal of Hydraulic Engineering, 2003, 34(3): 125-128 (in Chinese).
[44] Standard test method for drying shrinkage of mortar containing hydraulic cement: ASTM C596—09(2007)[S].West Conshohocken: ASTM International, 2007.
[45] 中华人民共和国国家发展和改革委员会.水泥胶砂干缩试验方法:JC/T 603—2004[S].北京:中国建材工业出版社,2005.
National Development and Reform Commission. Standard test method for drying shrinkage of mortar: JC/T 603—2004[S]. Beijing: China Building Materials Industry Press, 2005 (in Chinese).
[46] 国家环境保护总局.固体废物浸出毒性浸出方法硫酸硝酸法:HJ/T 299—2007[S].北京:中国环境科学出版社,2007.
State Environmental Protection Administration. Solid waste-extraction procedure for leaching toxicity-sulphuric acid & nitric acid method: HJ/T 299—2007[S]. Beijing: China Environmental Science Press, 2007 (in Chinese).
[47] EPA U S. Toxicity characteristics leaching procedure, method 1311[S]. Test Methods for the Evaluation of Solid Waste, 1992.
[48] Characterization of waste-leaching-compliance test for leaching of granular waste materials and sludges-Part 3: two stage batch test at a liquid to solid ratio of 2 L/kg and 8 L/kg for materials with a high solid content and with a particle size below 4 mm (without or with size reduction): BS EN 12457-3—2002[S]. London: BSI Publications, 2002.