再生保温混凝土抗冻性能的细观研究

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (11): 3601-3607.

再生保温混凝土抗冻性能的细观研究

王鲜星, 刘元珍, 赵雨, 戴小伟

太原理工大学土木工程学院,太原 030024

收稿日期:2021-06-03 修回日期:2021-07-11 出版日期:2021-11-15 发布日期:2021-12-08
通讯作者: 刘元珍,博士,教授。E-mail:liuyuanzhen@tyut.edu.cn
作者简介:王鲜星(1997—),女,硕士研究生。主要从事混凝土结构方面的研究。E-mail:1254452072@qq.com
基金资助:
国家自然科学基金(51678384,51911530238);山西省重点研发计划(201903D321043);山西省高等学校科技成果转化培育项目(2020CG023)

Meso-Research on Frost Resistance of Recycled Thermal Insulation Concrete

WANG Xianxing, LIU Yuanzhen, ZHAO Yu, DAI Xiaowei

College of Civil Engineering, Taiyuan University of Technology, Taiyuan 030024, China

Received:2021-06-03 Revised:2021-07-11 Online:2021-11-15 Published:2021-12-08

摘要/Abstract

摘要： 再生粗骨料和玻化微珠保温骨料的加入,会导致再生保温混凝土(RATIC)内部形成复杂的孔隙结构。为了进一步揭示冻融作用下再生保温混凝土的劣化机理,在宏观试验的基础上,通过CT扫描细观试验分析了不同再生粗骨料取代率的RATIC试件在冻融作用下的裂缝发展规律和孔隙特征。试验结果表明:新旧水泥砂浆界面过渡区是冻融循环作用下RATIC的薄弱环节,试件内部多数裂缝产生于新旧水泥砂浆界面过渡区;试件的相对孔隙率是定量反映RATIC试件内部冻融破坏规律的重要指标。

关键词: 再生保温混凝土, 冻融循环, 再生粗骨料取代率, 抗冻性能, 细观研究

Abstract: Due to the addition of recycled coarse aggregate and glazed hollow bead insulation aggregate, the complex pore structure is formed in recycled aggregate thermal insulation concrete (RATIC). In order to further reveal the deterioration mechanism of recycled thermal insulation concrete caused by freeze-thaw action, the crack development law and pore characteristics of RATIC specimens with different replacement rates of recycled coarse aggregate under freeze-thaw action were analyzed by CT scanning microscopic test based on the macro test. The test results show that the interface transition zone between new and old cement mortar is the weak link of RATIC under freeze-thaw cycles, and most cracks in the specimens originate from the interface transition zone between new and old cement mortar. The relative porosity of specimens is the best index to quantitatively reflect the internal failure law of RATIC specimens.

Key words: recycled aggregate thermal insulation concrete, freeze-thaw cycle, replacement rate of recycled coarse aggregate, frost resistance, meso-research

中图分类号:

TU528.01

王鲜星, 刘元珍, 赵雨, 戴小伟. 再生保温混凝土抗冻性能的细观研究[J]. 硅酸盐通报, 2021, 40(11): 3601-3607.

WANG Xianxing, LIU Yuanzhen, ZHAO Yu, DAI Xiaowei. Meso-Research on Frost Resistance of Recycled Thermal Insulation Concrete[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(11): 3601-3607.

参考文献

[1] WANG W J, ZHAO L, LIU Y Z, et al. Mechanical properties and stress-strain relationship in axial compression for concrete with added glazed hollow beads and construction waste[J]. Construction and Building Materials, 2014, 71: 425-434.
[2] LIU Y Z, WANG W J, CHEN Y F, et al. Residual stress-strain relationship for thermal insulation concrete with recycled aggregate after high temperature exposure[J]. Construction and Building Materials, 2016, 129: 37-47.
[3] XIAO Q H, CAO Z Y, GUAN X, et al. Damage to recycled concrete with different aggregate substitution rates from the coupled action of freeze-thaw cycles and sulfate attack[J]. Construction and Building Materials, 2019, 221: 74-83.
[4] LU C F, ZHOU Q S, WANG W, et al. Freeze-thaw resistance of recycled aggregate concrete damaged by simulated acid rain[J]. Journal of Cleaner Production, 2021, 280: 124396.
[5] GOKCE A, NAGATAKI S, SAEKI T, et al. Freezing and thawing resistance of air-entrained concrete incorporating recycled coarse aggregate: the role of air content in demolished concrete[J]. Cement and Concrete Research, 2004, 34(5): 799-806.
[6] LIU Y Z, CHEN Y F, WANG W J, et al. Bond performance of thermal insulation concrete under freeze-thaw cycles[J]. Construction and Building Materials, 2016, 104: 116-125.
[7] 刘元珍,郑晓红,李珠,等.玻化微珠承重保温混凝土抗冻性能试验研究[J].施工技术,2013,42(9):83-85+105.
LIU Y Z, ZHENG X H, LI Z, et al. Experimental study on frost resistance of vitrified microsphere bearing and insulation concrete[J]. Construction Technology, 2013, 42(9): 83-85+105 (in Chinese).
[8] 魏毅萌,柴军瑞,覃源,等.冻融循环下再生混凝土孔隙分布变化及其对抗冻性能的影响[J].硅酸盐通报,2018,37(3):825-830.
WEI Y M, CHAI J R, QIN Y, et al. Effect of pore distribution of recycled concrete on frost resistance under freeze-thaw cycling[J]. Bulletin of the Chinese Ceramic Society, 2018, 37(3): 825-830 (in Chinese).
[9] WANG J G, ZHANG J X, CAO D D. Pore characteristics of recycled aggregate concrete and its relationship with durability under complex environmental factors[J]. Construction and Building Materials, 2021, 272: 121642.
[10] XU F, WANG S L, LI T, et al. The mechanical properties and resistance against the coupled deterioration of sulfate attack and freeze-thaw cycles of tailing recycled aggregate concrete[J]. Construction and Building Materials, 2021, 269: 121273.
[11] DENG X H, GAO X Y, WANG R, et al. Investigation of microstructural damage in air-entrained recycled concrete under a freeze-thaw environment[J]. Construction and Building Materials, 2021, 268: 121219.
[12] 张士萍,邓敏,唐明述.混凝土冻融循环破坏研究进展[J].材料科学与工程学报,2008,26(6):990-994.
ZHANG S P, DENG M, TANG M S. Advance in research on damagement of concrete due to freeze-thaw cycles[J]. Journal of Materials Science and Engineering, 2008, 26(6): 990-994 (in Chinese).
[13] 陈洁静,秦拥军,肖建庄,等.基于CT技术的掺锂渣再生混凝土孔隙特征研究[J].建筑材料学报,2020:1-15.
CEHNG J J, QIN Y J, XIAO J Z, et al. Study on pore structure characteristics of recycled concrete with lithium slag based on CT technology[J]. Journal of Building Materials, 2020:1-15 (in Chinese).
[14] 吴呈锋,於修龄,卢升高.运用同步辐射显微CT揭示红壤团聚体内孔隙形态与空间分布[J].土壤学报,2020,57(6):1422-1429.
WU C F, YU X L, LU S G. Synchrotron-based X-ray tomographic microscopy reveals morphology and spatial structure of intra-aggregate pores in red soils[J]. Acta Pedologica Sinica, 2020, 57(6): 1422-1429 (in Chinese).
[15] 杜红秀,樊亚男.基于X-CT的C60高性能混凝土高温细观结构损伤研究[J].建筑材料学报,2020,23(1):210-215.
DU H X, FAN Y N. Meso-structure damage of C60 high performance concrete at high temperature based on X-CT[J]. Journal of Building Materials, 2020, 23(1): 210-215 (in Chinese).