不同碳材料对铝碳浇注料性能的影响

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (10): 3241-3247.

不同碳材料对铝碳浇注料性能的影响

邝昌柳, 王杏, 刘正龙, 丁军, 余超, 邓承继, 祝洪喜

武汉科技大学,省部共建耐火材料与冶金国家重点实验室,武汉 430081

收稿日期:2021-07-23 修回日期:2021-08-21 出版日期:2021-10-15 发布日期:2021-11-11
通讯作者: 丁军,博士,副教授。E-mail:dingjun@wust.edu.cn
作者简介:邝昌柳(1997—),女,硕士研究生。主要从事高温陶瓷材料的研究。E-mail:1132428619@qq.com
基金资助:
国家自然科学基金区域创新发展联合基金(U20A20239);武汉科技大学研究生创新创业基金(JCX201905)

Influences of Different Carbon Materials on Properties of Alumina-Carbon Castables

KUANG Changliu, WANG Xing, LIU Zhenglong, DING Jun, YU Chao, DENG Chengji, ZHU Hongxi

The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China

Received:2021-07-23 Revised:2021-08-21 Online:2021-10-15 Published:2021-11-11

摘要/Abstract

摘要： 含碳浇注料因碳材料的水润湿性差及高温氧化引起的材料性能差等问题一直备受关注。分别以热氧化石墨、ZrC包覆改性石墨和水热碳化生物质碳材料为碳源制备铝碳浇注料,研究不同碳材料对铝碳浇注料显气孔率、物理性能、物相组成,以及抗氧化性和抗渣侵蚀性能的影响。结果表明:引入热氧化石墨的浇注料具有最高的加水量,残留孔隙破坏了材料内部结构,浇注料机械性能较差;添加ZrC表面改性石墨可以降低浇注料的加水量,抗氧化性能较好,但对力学性能的提升无显著影响;以生物质碳材料为碳源可以显著提高浇注料的物理性能,相比于添加石墨的试样,生物质碳材料并未显著提升试样的抗渣侵蚀性能。

关键词: 耐火材料, 铝碳浇注料, 改性石墨, 生物质碳材料, 抗氧化性能, 抗侵蚀性能

Abstract: Carbon containing castables have always attracted attention due to the poor water wettability of carbon materials and poor material properties caused by high-temperature oxidation. Thermal oxidized graphite, ZrC coated graphite and biomass carbon materials were added as carbon sources to alumina-carbon castables, and their influences on the apparent porosity, physical properties, phase composition, oxidation resistance and slag corrosion resistance were studied. The results show that the castable with thermal oxide graphite has the highest water addition, its residual pores impart the internal structure of the castable, leading to low mechanical properties. Adding ZrC coated graphite reduces the water addition of the castable, then gets better oxidation resistance and effects slightly the improvement of mechanical properties. Using biomass carbon material as carbon source significantly improves the physical properties of the castable, and compared to the sample with thermal oxidized graphite added, the biomass carbon material does not significantly improve the slag corrosion resistance of the sample.

Key words: refractory, alumina-carbon castable, modified graphite, biomass carbon material, oxidation resistance, corrosion resistance

中图分类号:

TQ175

邝昌柳, 王杏, 刘正龙, 丁军, 余超, 邓承继, 祝洪喜. 不同碳材料对铝碳浇注料性能的影响[J]. 硅酸盐通报, 2021, 40(10): 3241-3247.

KUANG Changliu, WANG Xing, LIU Zhenglong, DING Jun, YU Chao, DENG Chengji, ZHU Hongxi. Influences of Different Carbon Materials on Properties of Alumina-Carbon Castables[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(10): 3241-3247.

参考文献

[1] ZHANG S, LEE W E. Carbon containing castables: current status and future prospects[J]. British Ceramic Transactions, 2002, 101(1): 1-8.
[2] 丁岩峰,谢朝晖.MgO-C质浇注料的研究[J].耐火材料,2002,36(1):21-23.
DING Y F, XIE Z H. Research on MgO-C castable[J]. Refractories, 2002, 36(1): 21-23 (in Chinese).
[3] 朱伯铨.含炭浇注料的现状与发展[J].耐火材料,1999,33(1): 53-56.
ZHU B Q. Current situation and development of the carboncontained castables[J]. Refractories, 1999, 33(1): 53-56 (in Chinese).
[4] ZHU B Q, ZHU Y N, LI X C, et al. Effect of ceramic bonding phases on the thermo-mechanical properties of Al₂O₃-C refractories[J]. Ceramics International, 2013, 39(6): 6069-6076.
[5] DING J, YU C, LIU J P, et al. Effects of silicon powder content on the properties and interface bonding of nitrided Al₂O₃-C refractories[J]. Materials Chemistry and Physics, 2018, 206: 193-203.
[6] WANG H, LI Y W, ZHU T B, et al. Microstructures and mechanical properties of Al₂O₃-C refractories with addition of microcrystalline graphite[J]. Ceramics International, 2014, 40(7): 11139-11148.
[7] WANG Q H, LI Y W, SANG S B, et al. Effect of the reactivity and porous structure of expanded graphite (EG) on microstructure and properties of Al₂O₃-C refractories[J]. Journal of Alloys and Compounds, 2015, 645: 388-397.
[8] LIU Z L, DENG C J, YU C, et al. Preparation of in situ grown silicon carbide whiskers onto graphite for application in Al₂O₃-C refractories[J]. Ceramics International, 2018, 44(12): 13944-13950.
[9] FRANKLIN S A, TUCKER B J S. Hot strength and thermal shock resistance of magnesia-carbon refractories[J]. British Ceramic Transactions, 1995, 94(4): 151-156.
[10] MUÑOZ V, PENA P, MARTÍNEZ A G T. Physical, chemical and thermal characterization of alumina-magnesia-carbon refractories[J]. Ceramics International, 2014, 40(7): 9133-9149.
[11] OLIVEIRA I R D, STUDART A R, PANDOLFELLI V C, et al. Zero-cement refractory castables[J]. American Ceramic Society Bulletin, 2002, 81(12): 27-34.
[12] 丁军.熔盐介质中碳材料改性及微孔轻质材料制备的基础研究[D].武汉:武汉科技大学,2013.
DING J. Basic research of carbon material modification and the preparation of microporous lightweight materials in molten salt media[D]. Wuhan: Wuhan University of Science and Technology, 2013 (in Chinese).
[13] LIU Z L, DENG C J, YU C, et al. Molten salt synthesis and characterization of SiC whiskers containing coating on graphite for application in Al₂O₃-SiC-C castables[J]. Journal of Alloys and Compounds, 2019, 777: 26-33.
[14] DUTTA S, DAS P, DAS A, et al. Significant improvement of refractoriness of Al₂O₃-C castables containing calcium aluminate nano-coatings on graphite[J]. Ceramics International, 2014, 40(3): 4407-4414.
[15] MUKHOPADHYAY S, DAS S, MOITRA S. Thermomechanical and thermophysical characteristics of alumina-carbon monolithic refractory containing surface-modified graphites in matrix[J]. Ceramics International, 2018, 44(9): 10061-10068.
[16] 李赛赛,王军凯,段红娟,等.水热碳化制备碳微球及其在Al₂O₃-SiC-C浇注料中的应用[J].硅酸盐学报,2018,46(3):341-346.
LI S S, WANG J K, DUAN H J, et al. Preparation of carbon spheres by hydrothermal carbonization and its application in Al₂O₃-SiC-C castable[J]. Journal of the Chinese Ceramic Society, 2018, 46(3): 341-346 (in Chinese).
[17] LI S S, LIU J H, WANG J K, et al. Catalytic preparation of graphitic carbon spheres for Al₂O₃-SiC-C castables[J]. Ceramics International, 2018, 44(11): 12940-12947.
[18] BI Y B, ZHANG H J, WANG H F, et al. Catalytic Fabrication of SiC/SiO₂ coated graphite and its behaviour in Al₂O₃-C castable systems[J]. Ceramics International, 2019, 45(13): 16180-16187.