粉煤灰对碱激发矿渣/粉煤灰体系的作用机理研究

摘要/Abstract

摘要： 碱激发胶凝材料是以工业固体废弃物为原料制备的一种绿色无机胶凝材料,具有良好的力学性能与耐久性能。粉煤灰因其独特的球体微观结构与其他固废微粉存在本质区别,因此粉煤灰在碱激发胶凝材料体系中的作用机理亟待研究。以矿渣与粉煤灰为原料,利用碱激发剂制备胶凝材料,并对材料进行抗压强度测试,最后采用XRD、FTIR和SEM探究碱激发矿渣/粉煤灰体系的水化反应机理,研究粉煤灰对矿渣/粉煤灰体系的作用机理。结果表明:外掺3%(质量分数)NaOH作为碱激发剂,水固比为0.4时,随粉煤灰掺量减少,抗压强度呈现先上升后下降的趋势;m(矿渣):m(粉煤灰)为4:1时,28 d抗压强度达到峰值(37.1 MPa)。粉煤灰颗粒在不同龄期形成具有不同反应程度与尺寸的嵌入式微观结构,对材料力学性能起到不利影响;但粉煤灰的活化程度随龄期延长逐渐变大,对后期强度发展有持续贡献。碱激发矿渣/粉煤灰体系水化产物中含有Friedel盐、托贝莫来石、钙矾石、C-S-H/C-A-S-H凝胶,以及粉煤灰中残留的α石英相。随粉煤灰掺量增加,托贝莫来石生成量减少,钙矾石向Friedel盐转变,钙矾石生成量减少,Friedel盐生成量增多。

关键词: 碱激发, 粉煤灰, 抗压强度, 微观结构, Friedel盐, 托贝莫来石

Abstract: With excellent mechanical properties and durability, alkali-activated cementitious material prepared by industrial solid waste is a kind of green inorganic cementitious material. Fly ash is essentially different from other solid waste because of its unique spherical microstructure, therefore, the reaction mechanism of fly ash in alkali-activated cementitious material needs to be studied. In this paper, slag and fly ash were used as raw materials to prepare cementitious materials by alkali activator. The compressive strength of the material was tested, and the hydration mechanism of alkali-activated slag/fly ash system was explored by XRD, FTIR, and SEM. The detailed effect of fly ash on alkali-activated slag/fly ash system and related mechanisms were investigated. The results show that, when 3% (mass fraction) NaOH is added as alkali activator, and the water-solid ratio is 0.4, with the decrease of fly ash content, the compressive strength first increases and then decreases. When m(slag):m(fly ash) is 4:1, 28 d compressive strength reaches the peak value of 37.1 MPa. Embedded microstructure of fly ash particles has different reaction degrees and sizes at different ages, which has a negative effect on the mechanical properties of the material. However, the activation degree of fly ash gradually increases with the extension of age, which has a continuous contribution to the later strength development. The hydration products of alkali-activated slag/fly ash system contain Friedel's salt, tobermorite, ettringite, C-S-H/C-A-S-H gel, and residual alpha quartz of fly ash. With the increase of fly ash content, the amount of tobermorite decreases, ettringite transforms into Friedel's salt, the production of ettringite decreases, and the production of Friedel's salt increases.

Key words: alkali-activation, fly ash, compressive strength, microstructure, Friedel's salt, tobermorite

中图分类号:

TU528

杨达, 庞来学, 宋迪, 卢明阳, 王佳斌, 管泽斌. 粉煤灰对碱激发矿渣/粉煤灰体系的作用机理研究[J]. 硅酸盐通报, 2021, 40(9): 3005-3011.

YANG Da, PANG Laixue, SONG Di, LU Mingyang, WANG Jiabin, GUAN Zebin. Reaction Mechanism of Fly Ash in Alkali-Activated Slag/Fly Ash System[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(9): 3005-3011.

参考文献

[1] TURNER L K, COLLINS F G. Carbon dioxide equivalent (CO₂-e) emissions: a comparison between geopolymer and OPC cement concrete[J]. Construction and Building Materials, 2013, 43: 125-130.
[2] 薛翠真,申爱琴,郭寅川,等.碱激发和复合激发下建筑垃圾砖粉活性研究[J].材料导报,2016,30(10):130-134.
XUE C Z, SHEN A Q, GUO Y C, et al. Activity of construction waste brick powder under alkali and compound modifications[J]. Materials Review, 2016, 30(10): 130-134 (in Chinese).
[3] 陈柯宇,吴大志,胡俊涛.基于组分的地聚合物胶凝材料反应机理及其制备参数的研究进展[J].硅酸盐通报,2020,39(7):2033-2041.
CHEN K Y, WU D Z, HU J T. Advances in the reaction mechanism and preparation parameters of geopolymer binder material based on components[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(7): 2033-2041 (in Chinese).
[4] ZHAN X Y, KIRKELUND G M. Electrodialytic remediation of municipal solid waste incineration fly ash as pre-treatment before geopolymerisation with coal fly ash[J]. Journal of Hazardous Materials, 2021, 412: 125220.
[5] 刘全,白志民,王东,等.我国粉煤灰化学成分与理化性能及其应用分析[J].中国非金属矿工业导刊,2021(1):1-9.
LIU Q, BAI Z M, WANG D, et al. Chemical composition and physicochemical properties of fly ash and its application[J]. China Non-Metallic Minerals Industry, 2021(1): 1-9 (in Chinese).
[6] 肖永丰,陈爱国,张雨薇,等.粉煤灰提铝硅渣碱溶脱硅反应及其动力学[J].硅酸盐通报,2021,40(2):542-547.
XIAO Y F, CHEN A G, ZHANG Y W, et al. Desilication reaction and kinetics of aluminum-extracting silicon slag in NaOH solution[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(2): 542-547 (in Chinese).
[7] 程国东,黄天勇,刘泽,等.粉煤灰-矿渣基地聚合物胶砂性能研究[J].新型建筑材料,2020,47(1):50-53.
CHENG G D, HUANG T Y, LIU Z, et al. Research on the performance of ash-slag based geopolymer mortar[J]. New Building Materials, 2020, 47(1): 50-53 (in Chinese).
[8] 高帅,吴岳峻,唐海涛,等.碱矿渣-粉煤灰砂浆的耐高温性能及孔结构研究[J].混凝土与水泥制品,2021(1):90-94.
GAO S, WU Y J, TANG H T, et al. Study on high temperature resistance and pore structure of alkali slag-fly ash mortar[J]. China Concrete and Cement Products, 2021(1): 90-94 (in Chinese).
[9] 王晓敏,郑建岚,朱艺婷.粉煤灰颗粒特性对再生混凝土水化性质的影响[J].福州大学学报(自然科学版),2021,49(2):238-244.
WANG X M, ZHENG J L, ZHU Y T. Effect of particle characteristics of fly ash on hydration properties of recycled concrete[J]. Journal of Fuzhou University (Natural Science Edition), 2021, 49(2): 238-244 (in Chinese).
[10] FERNÁNDEZ-JIMÉNEZ A, PALOMO A, CRIADO M. Microstructure development of alkali-activated fly ash cement: a descriptive model[J]. Cement and Concrete Research, 2005, 35(6): 1204-1209.
[11] YIN B, KANG T H, KANG J T, et al. Analysis of active ion-leaching behavior and the reaction mechanism during alkali activation of low-calcium fly ash[J]. International Journal of Concrete Structures and Materials, 2018, 12(1): 1-13.
[12] 卞立波,董申,陶志.碱激发矿渣/粉煤灰多孔混凝土基本性能试验研究[J].材料导报,2020,34(s2):1299-1303.
BIAN L B, DONG S, TAO Z. Basic properties of alkali activated slag/fly ash pervious concrete[J]. Materials Reports, 2020, 34(s2): 1299-1303 (in Chinese).
[13] KALOMBE R M, OJUMU V T, EZE C P, et al. Fly ash-based geopolymer building materials for green and sustainable development[J]. Materials, 2020, 13(24): 5699.
[14] 李博,陈伟.C-S-H凝胶分子结构研究进展[J].硅酸盐学报,2019,47(8):1095-1100.
LI B, CHEN W. Development on molecular structure of calcium silicate hydrate gel[J]. Journal of the Chinese Ceramic Society, 2019, 47(8): 1095-1100 (in Chinese).
[15] PAUL G, BOCCALERI E, BUZZI L, et al. Friedel's salt formation in sulfoaluminate cements: a combined XRD and 27Al MAS NMR study[J]. Cement and Concrete Research, 2015, 67: 93-102.
[16] SARKAR P K, MITRA N. Molecular level study of uni/multi-axial deformation response of tobermorite 11 Å: a force field comparison study[J]. Cement and Concrete Research, 2021, 145: 106451.
[17] 王露,刘数华.钙矾石相的研究综述[J].混凝土,2013(8):83-86+90.
WANG L, LIU S H. Research review on ettringite phase[J]. Concrete, 2013(8): 83-86+90 (in Chinese).
[18] 乔秀臣,马大伟,薛玉兵.煅烧硬石膏溶解特性对钙矾石形成的影响[J].硅酸盐通报,2021,40(1):201-206.
QIAO X C, MA D W, XUE Y B. Influence of calcined anhydrite solubility on the formation of ettringite[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(1): 201-206 (in Chinese).
[19] 蔡跃波,罗睿,王昌义.水泥-磨细矿渣水化产物—F盐的微结构分析[J].水利水运工程学报,2001(1):45-49.
CAI Y B, LUO R, WANG C Y. Microstructure analysis on Friedel's salt in hydrate of cement and GGBS[J]. Hydro-Science and Engineering, 2001(1): 45-49 (in Chinese).
[20] WANG X, NI W, JIN R Z, et al. Formation of Friedel's salt using steel slag and potash mine brine water[J]. Construction and Building Materials, 2019, 220: 119-127.
[21] BIRNIN-YAURI U A, GLASSER F P. Friedel's salt, Ca₂Al(OH)₆(Cl, OH)·2H₂O: its solid solutions and their role in chloride binding[J]. Cement and Concrete Research, 1998, 28(12): 1713-1723.
[22] TERZIS A, FILIPPAKIS S, KUZEL H J, et al. The crystal structure of Ca₂Al(OH)₆Cl·2H₂O[J]. Zeitschrift Für Kristallographie-Crystalline Materials, 1987, 181(1/2/3/4): 29-34.
[23] WANG H L, HAO R, GAO M P, et al. High temperature adsorption of SO₂ on mixed oxides derived from CaAl hydrotalcite-like compounds[J]. Processes, 2021, 9(2): 325.
[24] 魏威,高彦斌,陈忠清,等.室温碱激发低钙粉煤灰地质聚合物配比试验研究[J].硅酸盐通报,2020,39(12):3889-3896.
WEI W, GAO Y B, CHEN Z Q, et al. Experimental study on proportion of room temperature alkali-activated low-calcium fly ash geopolymer[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(12): 3889-3896 (in Chinese).