喷射3D打印磷酸镁水泥与混凝土界面粘结性能研究

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (6): 1895-1904.

• 3D 打印水泥基材料 • 上一篇下一篇

喷射3D打印磷酸镁水泥与混凝土界面粘结性能研究

刘雄飞^1,2, 李琦¹, 王里¹, 王楠¹

1.河北工业大学土木与交通学院,天津 300401;
2.北京理工大学,冲击环境材料技术重点实验室,北京 100081

收稿日期:2021-03-29 修回日期:2021-05-14 出版日期:2021-06-15 发布日期:2021-07-08
作者简介:刘雄飞(1988—),男,博士,副教授。主要从事3D打印高性能水泥基材料研究。E-mail:liuxfking@foxmail.com
基金资助:
国家自然科学基金(51627812,51908182);河北省自然科学基金(E2019202484,E2020202043);天津市自然科学基金(18JCZDJC39300);冲击环境材料技术重点实验室基金(6142902200304)

Bonding Behavior of Spray-Based 3D Printing Magnesium Phosphate Cement and Concrete

LIU Xiongfei^1,2, LI Qi¹, WANG Li¹, WANG Nan¹

1. School of Civil Engineering and Transportation, Hebei University of Technology, Tianjin 300401, China;
2. State Key Laboratory of Science and Technology on Materials in Impact Environment, Beijing Institute of Technology, Beijing 100081, China

Received:2021-03-29 Revised:2021-05-14 Online:2021-06-15 Published:2021-07-08

摘要/Abstract

摘要： 本文结合喷射3D打印全角度智能建造与磷酸镁水泥(MPC)快硬早强、高粘结性能,研究喷射3D打印MPC与混凝土界面粘结性能。通过掺加偏高岭土(MK)和粉煤灰(FA)调控MPC凝结时间、流变和力学性能,研发可喷射3D打印MPC,分析喷射3D打印MPC与混凝土界面粘结强度和微观结构变化规律。结果表明:MK通过降低MPC水化放热速率可明显提高MPC凝结时间,FA可缩短MPC初凝与终凝时间差,进而提高喷射3D打印MPC稳定性;MPC抗折强度随MK掺量先增大后降低,FA可进一步提高MPC抗折强度;随MK掺量增加,MPC静态屈服应力逐渐提高,FA对MPC屈服应力作用不明显,但可显著降低MPC塑性粘度,当掺加30%MK和15%FA时,可保证MPC良好可喷射3D打印建造性和泵送性;喷射3D打印通过高速喷射挤压作用,提高MPC与混凝土界面以及MPC层间粘结强度,使喷射3D打印MPC层间及其与混凝土微观界面粘结密实。

关键词: 喷射3D打印, 磷酸镁水泥, 界面粘结, 流变性能

Abstract: In this paper, combining the all-angle intelligent construction of spray-based 3D printing and magnesium phosphate cement (MPC) with fast hardening, high early strength and excellent bonding performance, the bonding behavior of the spray-based 3D printing MPC and concrete was studied. By adding metakaolin (MK) and fly ash (FA) to adjust the setting time, rheological properties and mechanical properties of the MPC, a spray-based 3D printing MPC was developed, and the change rule of the bond strength and microstructure of the interface between the spray-based 3D printing MPC and concrete was investigated. The results show that MK significantly prolongs the setting time of MPC by reducing the hydration heat release rate of MPC, and FA shortens the difference between initial setting time and final setting time of MPC, thus improving the stability of spray-based 3D printing MPC. The flexural strength of MPC increases first and then decreases with the addition of MK. FA further improves the flexural strength of MPC. With the increase of MK content, the static yield stress of MPC gradually increases. The effect of FA on the yield stress of MPC is not obvious, but the plastic viscosity of MPC significantly reduces. When adding 30%MK and 15%FA, the construction and pumping performance of MPC can be ensured. Through high-speed spray extrusion, the spray-based 3D printing improves the bond strength between MPC and concrete, which make the micro interface between MPC and concrete compact.

Key words: spray-based 3D printing, magnesium phosphate cement, bonding behavior, rheological property

中图分类号:

TU528

刘雄飞, 李琦, 王里, 王楠. 喷射3D打印磷酸镁水泥与混凝土界面粘结性能研究[J]. 硅酸盐通报, 2021, 40(6): 1895-1904.

LIU Xiongfei, LI Qi, WANG Li, WANG Nan. Bonding Behavior of Spray-Based 3D Printing Magnesium Phosphate Cement and Concrete[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(6): 1895-1904.

参考文献

[1] MECHTCHERINE V, BOS F P, PERROT A, et al. Extrusion-based additive manufacturing with cement-based materials-Production steps, processes, and their underlying physics: a review[J]. Cement and Concrete Research, 2020, 132: 106037.
[2] 王香港,王申,贾鲁涛,等.3D打印混凝土技术在新冠肺炎防疫方舱中的应用[J].混凝土与水泥制品,2020(4):1-4+13.
WANG X G, WANG S, JIA L T, et al. Application of 3D printing technology in epidemic prevention cabins during the outbreak of COVID-19[J]. China Concrete and Cement Products, 2020(4): 1-4+13 (in Chinese).
[3] ZHANG Y, ZHANG Y S, SHE W, et al. Rheological and harden properties of the high-thixotropy 3D printing concrete[J]. Construction and Building Materials, 2019, 201: 278-285.
[4] LU B, QIAN Y, LI M Y, et al. Designing spray-based 3D printable cementitious materials with fly ash cenosphere and air entraining agent[J]. Construction and Building Materials, 2019, 211: 1073-1084.
[5] NEUDECKER S, BRUNS C, GERBERS R, et al. A new robotic spray technology for generative manufacturing of complex concrete structures without formwork[J]. Procedia CIRP, 2016, 43: 333-338.
[6] LINDEMANN H, KLOFT H, HACK N. Gradual transition shotcrete 3D printing[J]. Advances in Architectural Geometry, 2018, 9: 22-25.
[7] KLOFT H, HACK N, MAINKA J, et al. Additive Fertigung im Bauwesen: erste 3-D-gedruckte und bewehrte betonbauteile im shotcrete-3-D-printing-verfahren (SC3DP)[J]. Bautechnik, 2019, 96(12): 929-938.
[8] LU B, LI M, LEONG K F, et al. Develop cementitious materials incorporating fly ash cenophere for spray-based 3D printing[C]//Proceedings of the 3rd International Conference on Progress in Additive Manufacturing, 2018: 38-43.
[9] CHEN Y, CHAVES FIGUEIREDO S, LI Z M, et al. Improving printability of limestone-calcined clay-based cementitious materials by using viscosity-modifying admixture[J]. Cement and Concrete Research, 2020, 132: 106040.
[10] KLOFT H, KRAUSS H W, HACK N, et al. Influence of process parameters on the interlayer bond strength of concrete elements additive manufactured by Shotcrete 3D Printing (SC3DP)[J]. Cement and Concrete Research, 2020, 134: 106078.
[11] DRESSLER I, FREUND N, LOWKE D. The effect of accelerator dosage on fresh concrete properties and on interlayer strength in shotcrete 3D printing[J]. Materials, 2020, 13(2): 374.
[12] YU J C, QIAN J S, WANG F, et al. Preparation and properties of a magnesium phosphate cement with dolomite[J]. Cement and Concrete Research, 2020, 138: 106235.
[13] XU B W, LOTHENBACH B, MA H Y. Properties of fly ash blended magnesium potassium phosphate mortars: effect of the ratio between fly ash and magnesia[J]. Cement and Concrete Composites, 2018, 90: 169-177.
[14] QIN J H, QIAN J S, YOU C, et al. Bond behavior and interfacial micro-characteristics of magnesium phosphate cement onto old concrete substrate[J]. Construction and Building Materials, 2018, 167: 166-176.
[15] LI Y, CHEN B. Factors that affect the properties of magnesium phosphate cement[J]. Construction and Building Materials, 2013, 47: 977-983.
[16] QIAO F, CHAU C K, LI Z J. Property evaluation of magnesium phosphate cement mortar as patch repair material[J]. Construction and Building Materials, 2010, 24(5): 695-700.
[17] KIM H, HAN D, KIM K, et al. Performance assessment of repair material for deteriorated concrete slabs using chemically bonded cement[J]. Construction and Building Materials, 2020, 237: 117468.
[18] 刘周强,张力文,孙卓,等.磷酸镁嵌入式纤维筋加固系统界面试验研究[J].哈尔滨工程大学学报,2020,41(9):1287-1294.
LIU Z Q, ZHANG L W, SUN Z, et al. Experimental study of the interface of magnesium phosphate cement near-surface mounted GFRP system[J]. Journal of Harbin Engineering University, 2020, 41(9): 1287-1294 (in Chinese).
[19] 李悦,白伟亮,施同飞,等.用MPC黏结CFRP布约束混凝土柱轴压试验研究[J].北京工业大学学报,2017,43(3):467-472.
LI Y, BAI W L, SHI T F, et al. Research on axial compression test of CFRP confined concrete column with MPC[J]. Journal of Beijing University of Technology, 2017, 43(3): 467-472 (in Chinese).
[20] LIU X F, LI Y. Plain concrete prisms externally strengthened by CFRP bonded with graphene oxide-modified magnesium phosphate cement[J]. Journal of Materials in Civil Engineering, 2020, 32(5): 04020069.
[21] LI Y, LIU X F, WANG Z G. Experimental study on reinforcement and chloride extraction of concrete column with MPC-CFRP composite anode[J]. KSCE Journal of Civil Engineering, 2019, 23(4): 1766-1775.
[22] LI Y, LIU X F, WU M K, et al. Research of electrochemical chloride extraction and reinforcement of concrete column using MPC-bonded carbon fiber reinforced plastic sheet & mesh[J]. Construction and Building Materials, 2017, 153: 436-444.
[23] 李振,王大富.旋转黏度计测定水泥浆体静态屈服应力和黏弹性研究[J].硅酸盐通报,2017,36(6):1818-1822.
LI Z, WANG D F. Static yield stress and viscoelasticity of fresh cement paste measured by rotational viscometer[J]. Bulletin of the Chinese Ceramic Society, 2017, 36(6): 1818-1822 (in Chinese).
[24] 谢友均,陈小波,马昆林,等.粉煤灰对水泥浆体的剪切变稀和剪切增稠作用[J].硅酸盐学报,2015,43(8):1040-1046.
XIE Y J, CHEN X B, MA K L, et al. Effects of fly ash on shearing thinning and thickening of cement paste[J]. Journal of the Chinese Ceramic Society, 2015, 43(8): 1040-1046 (in Chinese).
[25] QIN Z H, MA C, ZHENG Z Q, et al. Effects of metakaolin on properties and microstructure of magnesium phosphate cement[J]. Construction and Building Materials, 2020, 234: 117353.
[26] 石亚文,陈兵.偏高岭土改性磷酸镁水泥[J].硅酸盐学报,2018,46(8):1111-1116.
SHI Y W, CHEN B. Magnesium phosphate cement modified by metakaolin[J]. Journal of the Chinese Ceramic Society, 2018, 46(8): 1111-1116 (in Chinese).

喷射3D打印磷酸镁水泥与混凝土界面粘结性能研究

Bonding Behavior of Spray-Based 3D Printing Magnesium Phosphate Cement and Concrete

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	焦敏. 氧化石墨烯对新拌水泥浆体流变性的影响[J]. 硅酸盐通报, 2021, 40(7): 2159-2164.
[2]	赵楠, 卿龙邦, 杨卓凡, 慕儒. 不同龄期钢纤维增强水泥砂浆纤维拉拔试验与模拟研究[J]. 硅酸盐通报, 2021, 40(7): 2165-2173.
[3]	李宝玉. 石墨烯/聚乙烯复合改性沥青胶结料的流变性能研究[J]. 硅酸盐通报, 2021, 40(7): 2461-2468.
[4]	张超, 邓智聪, 马蕾, 刘超, 陈宇宁, 汪智斌, 贾子健, 王香港, 贾鲁涛, 陈春, 孙正明, 张亚梅. 3D打印混凝土研究进展及其应用[J]. 硅酸盐通报, 2021, 40(6): 1769-1795.
[5]	金源, 徐嘉宾, 孙登田, 陈明旭, 黄永波, 芦令超, 程新. 纳米二氧化硅对白水泥基3D打印材料结构变形、流变及力学性能的影响[J]. 硅酸盐通报, 2021, 40(6): 1855-1862.
[6]	徐嘉宾, 金源, 赵智慧, 陈明旭, 芦令超, 程新. 氧化铁红颜料对白水泥基3D打印材料流变及可打印性能的影响[J]. 硅酸盐通报, 2021, 40(6): 1863-1869.
[7]	张超, 邓智聪, 汪智斌, 侯泽宇, 贾子健, 王香港, 贾鲁涛, 陈春, 孙正明, 张亚梅, 潘金龙. 纤维对3D打印混凝土打印性能与力学性能的影响[J]. 硅酸盐通报, 2021, 40(6): 1870-1878.
[8]	谢晓杰, 王申. 纳米氧化铝对硅酸盐水泥浆体流变、水化和硬化强度的影响[J]. 硅酸盐通报, 2021, 40(6): 1911-1917.
[9]	韩卓群, 李伶, 刘时浩, 邱坤, 王守兴, 刘福田. 光固化ZrO₂陶瓷料浆的流变性能研究[J]. 硅酸盐通报, 2021, 40(6): 1965-1971.
[10]	黄彦敏, 毛岩鹏, 王旭江, 李敬伟, 王文龙, 马怡荻. 高强石膏3D打印浆体材料的制备与性能研究[J]. 硅酸盐通报, 2021, 40(6): 1979-1986.
[11]	李树鹏, 金祖权, 熊传胜. 钢筋混凝土电化学除氯技术研究现状[J]. 硅酸盐通报, 2021, 40(1): 25-33.
[12]	骆文进, 王丽英. 乳胶粉掺量对纤维素醚改性水泥浆体流变性能的影响[J]. 硅酸盐通报, 2021, 40(1): 71-76.
[13]	胡善海, 钱玉鹏, 江学峰, 王飞, 丁锋, 赵绍林. 蛭石基流延浆料的流变性能研究[J]. 硅酸盐通报, 2021, 40(1): 312-316.
[14]	薛伶俐;黎红兵;高云龙;李胜伟. 磷酸镁水泥基材料与混凝土粘结性能研究进展[J]. 硅酸盐通报, 2020, 39(9): 2724-2731.
[15]	杨建祥;曾三海;郑正旗;贺行洋;苏英;杨进. 超细钢渣粉对硅酸盐水泥浆体流变性能的影响[J]. 硅酸盐通报, 2020, 39(8): 2508-2514.