利用铜尾矿作硅质原料制备硅酸盐水泥熟料的研究

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (4): 1273-1279.

利用铜尾矿作硅质原料制备硅酸盐水泥熟料的研究

严峻¹, 聂松¹, 刘松柏¹, 邱廷省²

1.江西省建筑材料工业科学研究设计院,南昌 330001;
2.江西理工大学资源与环境工程学院,赣州 341000

收稿日期:2020-10-10 修回日期:2021-01-11 出版日期:2021-04-15 发布日期:2021-05-11
通讯作者: 刘松柏,教授级高工。E-mail:lsb8811@126.com
作者简介:严峻(1972—),男,高工。主要从事水泥工艺设计、水泥性能和固废资源化方面的研究。E-mail:jxyanjun@126.com
基金资助:
“十三五”国家重点研发计划(2018YFC1903402)

Preparation of Portland Cement Clinkers by Utilizing Copper Tailings as Siliceous Material

YAN Jun¹, NIE Song¹, LIU Songbai¹, QIU Tingsheng²

1. Jiangxi Building Materials Scientific Research and Design Institute, Nanchang 330001, China;
2. School of Resources and Environmental Engineering, Jiangxi University of Science and Technology, Ganzhou 341000, China

Received:2020-10-10 Revised:2021-01-11 Online:2021-04-15 Published:2021-05-11

摘要/Abstract

摘要： 利用铜尾矿作硅质原料,配制了不同率值的硅酸盐水泥生料,在不同温度(1 350 ℃、1 400 ℃和1 450 ℃)下进行煅烧,得到了相应的硅酸盐水泥熟料样品。利用乙二醇-乙醇法测定样品中的游离氧化钙f-CaO研究了水泥生料的易烧性,利用差示扫描量热仪(DSC)测试生料的吸放热峰研究了铜尾矿对水泥矿物形成温度的影响,并通过X射线衍射仪(XRD)和扫描电子显微镜(SEM)分析了熟料的矿物组成和微观结构。结果表明,与砂岩配料相比,采用铜尾矿作硅质原料配料烧制硅酸盐水泥熟料时,液相出现和C₃S开始形成的温度均更低,生料的易烧性更好。熟料石灰饱和系数(KH)低于0.92,1 400 ℃的煅烧温度下即可制备出f-CaO符合标准要求的硅酸盐水泥熟料,C₃S的尺寸约为20 μm,熟料的结构更加致密。

关键词: 铜尾矿, 生料, 硅酸盐水泥熟料, 煅烧温度, 熟料率值, 易烧性

Abstract: Portland cement clinkers with different clinker modulus were prepared by utilizing copper tailings as siliceous material at different calcination temperatures (1 350 ℃, 1 400 ℃ and 1 450 ℃). The sinterability of cement raw meal was investigated by the determination of f-CaO in the sample by ethylene glycol-ethanol method. Effect of copper tailings on mineral formation temperature was researched by differential scanning calorimetry (DSC). Mineral composition and microstructure of clinkers were also analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that, compared with sandstone, when copper tailings are utilized as siliceous material to prepare Portland cement clinkers, the temperature of liquid phase and C₃S formation are lower, and the sinterability of raw meal is improved. f-CaO conforms to the standard requirement of Portland cement clinkers with lime saturation degree (KH) lower than 0.92 sintered well under 1 400 ℃ were prepared。The size of C₃S is about 20 μm, and the structure of clinkers is more compact.

Key words: copper tailing, raw meal, Portland cement clinker, sintering temperature, clinker modulus, sinterability

中图分类号:

TQ172

严峻, 聂松, 刘松柏, 邱廷省. 利用铜尾矿作硅质原料制备硅酸盐水泥熟料的研究[J]. 硅酸盐通报, 2021, 40(4): 1273-1279.

YAN Jun, NIE Song, LIU Songbai, QIU Tingsheng. Preparation of Portland Cement Clinkers by Utilizing Copper Tailings as Siliceous Material[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(4): 1273-1279.

参考文献

[1] GORDON R B. Production residues in copper technological cycles[J]. Resources, Conservation and Recycling, 2002, 36(2): 87-106.
[2] FU P F, YANG T W, FENG J, et al. Synthesis of mesoporous silica MCM-41 using sodium silicate derived from copper ore tailings with an alkaline molted-salt method[J]. Journal of Industrial and Engineering Chemistry, 2015, 29: 338-343.
[3] 陈甲斌,李瑞军,余良晖.铜矿尾矿资源调查评价方法及其应用[J].自然资源学报,2012,27(8):1373-1381.
CHEN J B, LI R J, YU L H. The way of the survey and assessment of copper tailings resources and their application[J]. Journal of Natural Resources, 2012, 27(8): 1373-1381 (in Chinese).
[4] 兰志强,蓝卓越.铜尾矿资源综合利用研究进展[J].矿产保护与利用,2015(5):51-56.
LAN Z Q, LAN Z Y. The progress of comprehensive utilization of copper tailings resource[J]. Conservation and Utilization of Mineral Resources, 2015(5): 51-56 (in Chinese).
[5] 汪洋,田键,朱艳超.铜尾矿开发利用现状分析[J].环境工程,2015,33(s1):623-627.
WANG Y, TIAN J, ZHU Y C. Research on development and exploitation of copper mine tailing[J]. Environmental Engineering, 2015, 33(s1): 623-627 (in Chinese).
[6] NIKOLIC N, BÖCKER R, NIKOLIC M. Long-term passive restoration following fluvial deposition of sulphidic copper tailings: nature filters out the solutions[J]. Environmental Science and Pollution Research, 2016, 23(14): 13672-13680.
[7] 鲁亚,刘松柏,施麟芸.铜尾矿粉的制备及应用于UHPC中的配合比设计研究[J].新型建筑材料,2020,47(6):33-37.
LU Y, LIU S B, SHI L Y. Preparation of copper tailings powder and its mix ratio design in application of UHPC[J]. New Building Materials, 2020, 47(6): 33-37 (in Chinese).
[8] 周科平,刘福萍,胡建华,等.尾矿库溃坝灾害链及断链减灾控制技术研究[J].灾害学,2013,28(3):24-29.
ZHOU K P, LIU F P, HU J H, et al. Research of tailings dam-break disaster chain and chain-cutting disaster mitigation control technology[J]. Journal of Catastrophology, 2013, 28(3): 24-29 (in Chinese).
[9] ONUAGULUCHI O, EREN Ö. Recycling of copper tailings as an additive in cement mortars[J]. Construction and Building Materials, 2012, 37: 723-727.
[10] 施麟芸,毛佩林,刘松柏,等.CaO-MgO-Al₂O₃-SiO₂系铜尾矿微晶玻璃析晶特征研究[J].硅酸盐通报,2020,39(5):1645-1649.
SHI L Y, MAO P L, LIU S B, et al. Crystallization characteristics of copper tailings glass-ceramics of CaO-MgO-Al₂O₃-SiO₂ system[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(5): 1645-1649 (in Chinese).
[11] THOMAS B S, DAMARE A, GUPTA R C. Strength and durability characteristics of copper tailing concrete[J]. Construction and Building Materials, 2013, 48: 894-900.
[12] ZHANG C S, ZHOU T T, WU Q S, et al. Mechanical performances and microstructures of cement containing copper tailings[J]. Asian Journal of Chemistry, 2014, 26(5): 1371-1375.
[13] LIU S H, WANG L, LI Q L, et al. Hydration properties of Portland cement-copper tailing powder composite binder[J]. Construction and Building Materials, 2020, 251: 118882.
[14] AHMARI S, ZHANG L Y. Production of eco-friendly bricks from copper mine tailings through geopolymerization[J]. Construction and Building Materials, 2012, 29: 323-331.
[15] 奚新国,张长森,周婷婷,等.铜尾渣对水泥生料易烧性及熟料性能的影响[J].建筑材料学报,2014,17(6):1102-1107+1114.
XI X G, ZHANG C S, ZHOU T T, et al. Effect of copper tailings on burn-ability of cement raw meal and performances of clinker[J]. Journal of Building Materials, 2014, 17(6): 1102-1107+1114 (in Chinese).
[16] JIAN S W, GAO W B, LV Y, et al. Potential utilization of copper tailings in the preparation of low heat cement clinker[J]. Construction and Building Materials, 2020, 252: 119130.
[17] QIU G H, LUO Z Y, SHI Z L, et al. Utilization of coal gangue and copper tailings as clay for cement clinker calcinations[J]. Journal of Wuhan University of Technology-Mater Sci Ed, 2011, 26(6): 1205-1210.
[18] KOLOVOS K, TSIVILIS S, KAKALI G. The effect of foreign ions on the reactivity of the CaO-SiO₂-Al₂O₃-Fe₂O₃ system: part II: cations[J]. Cement and Concrete Research, 2002, 32(3): 463-469.