天然浮石混凝土冻融损伤及寿命预测模型

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (1): 98-105.

所属专题：水泥混凝土

天然浮石混凝土冻融损伤及寿命预测模型

王萧萧^1,2, 刘畅¹, 尹立强^2,3, 闫长旺^2,3, 刘曙光^2,3

1.内蒙古工业大学土木工程学院,呼和浩特 010051;
2.生态型建筑材料与装配式结构内蒙古自治区工程研究中心,呼和浩特 010051;
3.内蒙古工业大学矿业学院,呼和浩特 010051

收稿日期:2020-08-26 修回日期:2020-09-30 出版日期:2021-01-15 发布日期:2021-02-07
通讯作者: 尹立强,博士,讲师。E-mail:yinliqiang0720@126.com
作者简介:王萧萧(1987—),女,博士,副教授。主要从事混凝土耐久性研究。E-mail:wxiaoxiao.good@163.com
基金资助:
国家自然科学基金(51609119);内蒙古自治区高等学校“青年科技英才支持计划”(NJYT-18-B24)

Freeze-Thaw Damage and Life Prediction Model ofNatural Pumice Concrete

WANG Xiaoxiao^1,2, LIU Chang¹, YIN Liqiang^2,3, YAN Changwang^2,3, LIU Shuguang^2,3

1. School of Civil Engineering,Inner Mongolia University of Technology,Hohhot 010051,China;
2. Inner Mongolia EngineeringResearch Center of Ecological Building Materials and Prefabricated Construction,Hohhot 010051,China;
3. School of Mining Technology,Inner Mongolia University of Technology,Hohhot 010051,China

Received:2020-08-26 Revised:2020-09-30 Online:2021-01-15 Published:2021-02-07

摘要/Abstract

摘要： 内蒙古地区天然浮石资源丰富,可作为粗骨料制作轻质混凝土。为了研究天然浮石混凝土冻融损伤规律,配制了五种配合比的试件进行快速冻融试验。通过天然浮石混凝土相对动弹性模量和质量损失变化规律,分析了浮石骨料对混凝土抗冻性的影响。基于静水压力理论和疲劳损伤理论,推导出天然浮石混凝土的材料系数,进而建立了冻融损伤模型和寿命预测模型,并作为实例,考察了内蒙古巴彦淖尔市冬季低温环境下的天然浮石混凝土寿命。结果表明:浮石骨料能减小混凝土静水压力,提高抗冻性;天然浮石混凝土相对动弹性模量计算值与试验值吻合较好;五组天然浮石混凝土寿命预测值分别达到65 a、84 a、112 a、131 a和50 a,满足安全性运行年限。

关键词: 天然浮石混凝土, 冻融损伤, 相对动弹性模量, 寿命预测

Abstract: Inner Mongolia is rich in natural pumice,which can be used as coarse aggregate of lightweight aggregate concrete.In order to study the freeze-thaw damage law of natural pumice concrete (NPC),the freeze-thaw test was carried out on specimens with five kinds of mixing ratios.The relative dynamic elastic modulus and mass loss of NPC were obtained,and then the influence of pumice aggregate on the concrete frost resistance was analyzed.Based on the hydrostatic pressure theory and the fatigue damage theory,the material coefficient of NPC was deduced,the freeze-thaw damage model and life prediction model of NPC were established,and as an example,the life of NPC in Bayannur,Inner Mongolia in winter was calculated.The results show that pumice aggregate reduces the hydrostatic pressure of concrete and improves its frost resistance.The calculated value of relative dynamic modulus of the NPC is in great agreement with the test value.The life expectancy values of five groups of NPC reach 65 a,84 a,112 a,131 a and 50 a,meeting the safety operation life.

Key words: natural pumice concrete, freeze-thaw damage, relative dynamic elastic modulu, life prediction

中图分类号:

TU528.2

王萧萧, 刘畅, 尹立强, 闫长旺, 刘曙光. 天然浮石混凝土冻融损伤及寿命预测模型[J]. 硅酸盐通报, 2021, 40(1): 98-105.

WANG Xiaoxiao, LIU Chang, YIN Liqiang, YAN Changwang, LIU Shuguang. Freeze-Thaw Damage and Life Prediction Model ofNatural Pumice Concrete[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(1): 98-105.

参考文献

[1] HASSANPOUR M,SHAFIGH P,MAHMUD H B.Lightweight aggregate concrete fiber reinforcement:a review[J].Construction and Building Materials,2012,37:452-461.
[2] RASHAD A M.A short manual on natural pumice as a lightweight aggregate[J].Journal of Building Engineering,2019,25:100802.
[3] 王海龙.轻骨料混凝土早期力学性能与抗冻性能的试验研究[D].呼和浩特:内蒙古农业大学,2009.
WANG H L.The study on early mechanics and frost resistance of lightweight aggregate concrete[D].Hohhot:Inner Mongolia Agricultural University,2009 (in Chinese).
[4] HOSSAIN K M A.Properties of volcanic ash and pumice concrete[J].IABSE Report,1990,80:145-150.
[5] HOSSAIN K M A.Blended cement using volcanic ash and pumice[J].Cement and Concrete Research,2003,33(10):1601-1605.
[6] HOSSAIN K M A,LACHEMI M.Development of volcanic ash concrete:strength,durability,and microstructural investigations[J].ACI Materials Journal,2006,103(1):11-17.
[7] LIU K H,YAN J C,ALAM M S,et al.Seismic fragility analysis of deteriorating recycled aggregate concrete bridge columns subjected to freeze-thaw cycles[J].Engineering Structures,2019,187:1-15.
[8] 王海龙,申向东,王萧萧.碳纤维改善浮石混凝土力学特性的试验研究[J].建筑材料学报,2013,16(2):232-236.
WANG H L,SHEN X D,WANG X X.Study of carbon fiber improved pumice concrete mechanical properties[J].Journal of Building Materials,2013,16(2):232-236 (in Chinese).
[9] DONG W,SHEN X D,XUE H J,et al.Research on the freeze-thaw cyclic test and damage model of Aeolian sand lightweight aggregate concrete[J].Construction and Building Materials,2016,123:792-799.
[10] 王萧萧,申向东,王海龙,等.天然浮石混凝土孔溶液结冰规律的研究[J].材料导报,2017,31(6):130-135.
WANG X X,SHEN X D,WANG H L,et al.Research on icing law of pore solution in natural pumice concrete[J].Materials Review,2017,31(6):130-135 (in Chinese).
[11] 洪锦祥,缪昌文,刘加平,等.冻融损伤混凝土力学性能衰减规律[J].建筑材料学报,2012,15(2):173-178.
HONG J X,MIAO C W,LIU J P,et al.Degradation law of mechanical properties of concrete subjected to freeze-thaw cycles[J].Journal of Building Materials,2012,15(2):173-178 (in Chinese).
[12] POLAT R,DEMIRBOGA R,KARAKOC M B,et al.The influence of lightweight aggregate on the physico-mechanical properties of concrete exposed to freeze-thaw cycles[J].Cold Regions Science and Technology,2010,60(1):51-56.
[13] 严佳川,邹超英.冻融循环作用下混凝土材料寿命评估方法[J].哈尔滨工业大学学报,2011,43(6):11-15.
YAN J C,ZOU C Y.Evaluation method for the service life of concrete under the freeze-thaw action[J].Journal of Harbin Institute of Technology,2011,43(6):11-15 (in Chinese).
[14] 李金玉,彭小平,邓正刚,等.混凝土抗冻性的定量化设计[J].混凝土,2000(12):61-65.
LI J Y,PENG X P,DENG Z G,et al.Quantitative design on the frost-resistance of concrete[J].Concrete,2000(12):61-65 (in Chinese).
[15] 董伟,申向东,赵占彪,等.风积沙轻骨料混凝土冻融损伤及寿命预测研究[J].冰川冻土,2015,37(4):1009-1015.
DONG W,SHEN X D,ZHAO Z B,et al.Study of the freezing-thawing damage and life prediction of aeolian lightweight aggregate concrete[J].Journal of Glaciology and Geocryology,2015,37(4):1009-1015 (in Chinese).
[16] WANG X X,WU Y,SHEN X D,et al.An experimental study of a freeze-thaw damage model of natural pumice concrete[J].Powder Technology,2018,339:651-658.
[17] HARIYADI,TAMAI H.Enhancing the performance of porous concrete by utilizing the pumice aggregate[J].Procedia Engineering,2015,125:732-738.
[18] 中华人民共和国住房和城乡建设部.普通混凝土长期性能和耐久性能试验方法标准:GB/T 50082—2009[S].北京:中国建筑工业出版社,2009.
Ministry of Housing and Urban Rural Development of the People’s Republic of China.Standard for test methods of long term performance and durability of ordinary concrete:GB/T 50082—2009[S].Beijing:China Construction Industry Press,2009 (in Chinese).
[19] POWERS T C.A working hypothesis for further studies of frost resistance of concrete[J].ACI Journal Proceedings,1945,41(1):245-272.
[20] POWERS T C.The air requirement of frost-resistance concrete[J].Proceedings of Highway Research Board,1949,29:184-202.
[21] 蔡昊.混凝土抗冻耐久性预测模型[D].北京:清华大学,1998.
CAI H.Prediction model of concrete frost resistance durability[D].Beijing:Tsinghua University,1998 (in Chinese).
[22] 段安.受冻融混凝土本构关系研究和冻融过程数值模拟[D].北京:清华大学,2009.
DUAN A.Research on constitutive relationship of frozen-thawed concrete and mathematical modeling of freeze-thaw process[D].Beijing:Tsinghua University,2009 (in Chinese).
[23] AAS-JAKOBSEN K,Fatigue of Concrete Beams and Columns[M].Trondheim:Institute for Betonkonstruksjoner,1970:148.
[24] CASTILLO E,FERNÁNDEZ-CANTELI A.A general regression model for lifetime evaluation and prediction[J].International Journal of Fracture,2001,107(2):117-137.

天然浮石混凝土冻融损伤及寿命预测模型

Freeze-Thaw Damage and Life Prediction Model ofNatural Pumice Concrete

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	魏达, 朱平华, 王新杰, 刘惠, 刘少峰, 贾学军. 再生粗骨料附着砂浆含量对再生混凝土抗冻耐久性的影响[J]. 硅酸盐通报, 2021, 40(3): 765-774.
[2]	徐存东;张鹏;连海东;王燕;李振;谷丰佑. 基于Weibull分布的灌区混凝土建筑物寿命预测[J]. 硅酸盐通报, 2020, 39(5): 1483-1490.
[3]	焦隽隽;朱俊锋. 再生混凝土冻融损伤可靠性分析[J]. 硅酸盐通报, 2020, 39(4): 1145-1152.
[4]	霍俊芳;曹雪;王萧萧;奇雨欣;李海清. 天然浮石混凝土孔结构对其抗压强度影响的研究[J]. 硅酸盐通报, 2020, 39(3): 734-739.
[5]	崔钊玮;刘荣桂;陆春华;王豪杰. 干湿循环与受弯裂缝共同作用下海工砼梁内氯离子侵蚀及耐久性寿命预测[J]. 硅酸盐通报, 2020, 39(2): 344-351.
[6]	乔宏霞;付勇;路承功;郭飞. 基于Wiener退化的混凝土加速试验耐久性研究[J]. 硅酸盐通报, 2020, 39(11): 3496-3502.
[7]	李永靖;潘铖;张淑坤;李东华;关宏涛;张镇山. 循环荷载对煤矸石混凝土损伤试验研究[J]. 硅酸盐通报, 2019, 38(8): 2531-253.
[8]	王伯昕;潘晨;汪飞;王清. 基于Logistic模型的混凝土冻融损伤演化规律[J]. 硅酸盐通报, 2019, 38(8): 2536-254.
[9]	张经双;段雪雷. 冻融循环下不同龄期水泥土损伤特性和能量耗散[J]. 硅酸盐通报, 2019, 38(7): 2144-215.
[10]	潘一鸣;王伯昕;汪飞;王清. 碳酸盐和硫酸盐作用下混凝土宏-细观损伤机理[J]. 硅酸盐通报, 2019, 38(12): 3713-371.
[11]	马俊军;蔺鹏臻. 基于可靠指标的混凝土箱梁桥氯离子扩散效应分析与寿命预测[J]. 硅酸盐通报, 2019, 38(1): 7-13.
[12]	谢智刚;王起才;代金鹏;王振宇;田祥富;薄士威. 全浸泡作用下混凝土抗硫酸盐侵蚀性能试验研究[J]. 硅酸盐通报, 2018, 37(4): 1125-1131.
[13]	徐存东;程昱;高懿伟;田俊姣;张锐. 基于可拓层次分析法的混凝土材料抗冻耐久性影响因素分析[J]. 硅酸盐通报, 2018, 37(4): 1181-1187.
[14]	程阳;孙家瑛;郑明. 弯拉荷载和碳化耦合作用下氯离子扩散试验研究[J]. 硅酸盐通报, 2017, 36(5): 1700-1705.
[15]	乔宏霞;麻红卫;王金磊;路成功. 干燥和浸水环境下基于无损检测方法的镁水泥砼最佳配合比研究[J]. 硅酸盐通报, 2017, 36(4): 1258-1265.