天然沸石粉对氯氧镁水泥耐水性影响研究

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (1): 41-47.

所属专题：水泥混凝土

天然沸石粉对氯氧镁水泥耐水性影响研究

孙恩禹¹, 陈啸洋²

1.辽宁科技大学应用技术学院,鞍山 114051;
2.辽宁科技大学化学工程与技术学院,鞍山 114051

收稿日期:2020-08-03 修回日期:2020-11-08 出版日期:2021-01-15 发布日期:2021-02-07
作者简介:孙恩禹(1975—),男,副教授。主要从事镁质胶凝材料及制品的研究。E-mail:sunenyu@126.com

Effect of Natural Zeolite Powder on Water Resistance ofMagnesium Oxychloride Cement

SUN Enyu¹, CHEN Xiaoyang²

1. College of Applied Technology,University of Science and Technology Liaoning,Anshan 114051,China;
2. College of Chemical Engineering and Technology,University of Science and Technology Liaoning,Anshan 114051,China

Received:2020-08-03 Revised:2020-11-08 Online:2021-01-15 Published:2021-02-07

摘要/Abstract

摘要： 氯氧镁水泥(MOC)具有轻质、高强、耐磨等优势,但耐水性差制约了其在建筑行业的发展。为制备高耐水性MOC,以天然沸石粉(NZOP)为掺合料,分析了天然沸石粉对MOC凝结时间、抗压强度、耐水性的影响。同时,利用X射线衍射仪、扫描电镜、压汞仪分析了改性后MOC的相组成、微观形貌和孔结构的变化。此外,利用离子色谱仪检测了MOC浸水后溶液中的Cl^-浓度。结果表明,合适掺量的天然沸石粉可以有效提高MOC的抗压强度和耐水性,缩短MOC的凝结时间。掺入30%(质量分数)天然沸石粉和0.5%(质量分数)磷酸后,MOC的28 d抗压强度和浸水28 d软化系数分别可达75.8 MPa和0.91,氯离子浓度低至9.0 mmol/L。此外,溶液中Cl^-浓度随着MOC软化系数的降低而提高。

关键词: 氯氧镁水泥, 天然沸石粉, 磷酸, 草酸, 耐水性, 微观形貌

Abstract: Magnesium oxychloride cement (MOC) has the advantages of light weight,high strength and high wear resistance,however,its poor water resistance restricts its development in the construction industry.To prepare high water resistance of MOC,natural zeolite powder (NZOP) was used as admixture.The effect of NZOP on the setting time,compressive strength and water resistance of MOC was investigated.Meanwhile,X-ray diffractometer,scanning electron microscope and mercury intrusion porosimetry were used to analyze the change of phase composition,microstructure and pore structure of modified MOC.In addition,the concentration of Cl^- in immersing solution was measured by ion chromatograph.The results show that NZOP effectively improves the compressive strength and water resistance of MOC and reduces the initial and final setting time of MOC.After adding 30% (mass fraction) NZOP and 0.5% (mass fraction) phosphoric acid,the 28 d compressive strength and 28 d softening coefficient of MOC reach up to 75.8 MPa and 0.91,respectively,and the concentration of Cl^- in immersing solution is as low as 9.0 mmol/L.In addition,the concentration of Cl^- in immersing solution increases with the decrease of the softening coefficient of MOC.

Key words: magnesium oxychloride cement, natural zeolite powder, phosphoric acid, oxalic acid, water resistance, microstructure

中图分类号:

TQ172

孙恩禹, 陈啸洋. 天然沸石粉对氯氧镁水泥耐水性影响研究[J]. 硅酸盐通报, 2021, 40(1): 41-47.

SUN Enyu, CHEN Xiaoyang. Effect of Natural Zeolite Powder on Water Resistance ofMagnesium Oxychloride Cement[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(1): 41-47.

参考文献

[1] WALLING S A,PROVIS J L.Magnesia-based cements:a journey of 150 years,and cements for the future?[J].Chemical Reviews,2016,116(7):4170-4204.
[2] HE P P,POON C S,TSANG D C W.Effect of pulverized fuel ash and CO₂ curing on the water resistance of magnesium oxychloride cement (MOC)[J].Cement and Concrete Research,2017,97:115-122.
[3] 文静,余红发,吴成友,等.氯氧镁水泥水化历程的影响因素及水化动力学[J].硅酸盐学报,2013,41(5):588-596.
WEN J,YU H F,WU C Y,et al.Hydration kinetic and influencing parameters in hydration process of magnesium oxychloride cement[J].Journal of the Chinese Ceramic Society,2013,41(5):588-596 (in Chinese).
[4] 王路明.磷酸/聚合物复合改善氯氧镁水泥耐水性能与机理的研究[J].功能材料,2015,46(13):13066-13069.
WANG L M.Study on the water resistance and mechanism of improving for magnesium oxychloride cement with phosphate and polymer[J].Journal of Functional Materials,2015,46(13):13066-13069 (in Chinese).
[5] 邓德华.磷酸根离子对氯氧镁水泥水化物稳定性的影响[J].建筑材料学报,2002,5(1):9-12.
DENG D H.Effect of the phosphate anion on the stabilization of hydrate in magnesium oxychloride cement[J].Journal of Building Materials,2002,5(1):9-12 (in Chinese).
[6] 张婷婷,孙延杰.硅灰和六偏磷酸钠对氯氧镁水泥耐水性影响的数学建模和微观分析[J].建材技术与应用,2018(2):1-5+11.
ZHANG T T,SUN Y J.Mathematical modeling and microscopic analysis of effect of silica fume and sodium hexametaphosphate on water resistance of magnesium oxychloride cement[J].Research & Application of Building Materials,2018(2):1-5+11 (in Chinese).
[7] 冯超,关博文,张奔,等.减水剂作用下氯氧镁水泥中水分侵蚀行为[J].非金属矿,2019,42(2):41-44.
FENG C,GUAN B W,ZHANG B,et al.Moisture erosion behavior of magnesium oxychloride cement with the action of water reducer[J].Non-Metallic Mines,2019,42(2):41-44 (in Chinese).
[8] CHAU C K,CHAN J,LI Z J.Influences of fly ash on magnesium oxychloride mortar[J].Cement and Concrete Composites,2009,31(4):250-254.
[9] 余红发,李生堂,何庆英,等.MgO-SF-FA-MgCl₂-H₂O胶凝材料体系的长期强度及耐水性研究[J].硅酸盐学报,2000,28(s1):33-37.
YU H F,LI S T,HE Q Y,et al.Research on long-term strength and water-resistance of MgO-sf-fa-MgCl₂-H₂O system cementitious materials[J].Journal of the Chinese Ceramic Society,2000,28(s1):33-37 (in Chinese).
[10] DENG D H.The mechanism for soluble phosphates to improve the water resistance of magnesium oxychloride cement[J].Cement and Concrete Research,2003,33(9):1311-1317.
[11] CHEN X Y,ZHANG T T,BI W L,et al.Effect of tartaric acid and phosphoric acid on the water resistance of magnesium oxychloride (MOC) cement[J].Construction and Building Materials,2019,213:528-536.
[12] 陈啸洋,毕万利,张婷婷,等.柠檬酸对氯氧镁水泥的改性[J].硅酸盐学报,2019,47(7):884-890.
CHEN X Y,BI W L,ZHANG T T,et al.Modification of magnesium oxychloride cement by citric acid[J].Journal of the Chinese Ceramic Society,2019,47(7):884-890 (in Chinese).

[1]	李涛, 张继文, 姜海楼, 杨建明. 高流动性磷酸铵镁水泥硬化浆体耐盐腐蚀性能试验研究[J]. 硅酸盐通报, 2021, 40(3): 750-757.
[2]	谢子茜, 刘桂宾, 张天宇, 李秋义, 王亮. 钾基碱性电解水对粉煤灰混凝土性能的影响[J]. 硅酸盐通报, 2021, 40(3): 943-950.
[3]	劳家荣, 黄忠财, 郭寅川, 陈琳, 申爱琴, 杨景玉. SAP内养生路面混凝土收缩性能及力学性能研究[J]. 硅酸盐通报, 2021, 40(2): 676-682.
[4]	韩超, 杨建明, 单春明, 吴庆, 何富强. 不同溶液长期浸泡下大流动性磷酸钾镁水泥基防腐涂层的性能[J]. 硅酸盐通报, 2021, 40(1): 48-54.
[5]	刁金龙, 于天来, 莫大洪, 郑涛, 郭艳艳, 吕景文. SnO对SnF₂-P₂O₅-WO₃系统玻璃结构和性能的影响[J]. 硅酸盐通报, 2021, 40(1): 266-270.
[6]	薛伶俐;黎红兵;高云龙;李胜伟. 磷酸镁水泥基材料与混凝土粘结性能研究进展[J]. 硅酸盐通报, 2020, 39(9): 2724-2731.
[7]	时军;王晶;史忠祥;戴丽静. 表面活性剂对YMn2O5粉体微观形貌的影响[J]. 硅酸盐通报, 2020, 39(9): 3001-3007.
[8]	夏文静;蒋斌;吴涛;梁家华. 基于正交试验采用多指标矩阵分析改性生土墙体材料热湿配合比[J]. 硅酸盐通报, 2020, 39(6): 1859-1867.
[9]	刘志宁;何富强;卓卫东;王勇. 偏高岭土/粉煤灰-磷酸钾镁水泥体系早期水化研究[J]. 硅酸盐通报, 2020, 39(5): 1397-1402.
[10]	陈伟;刘翔;李秋. 基于外部供应修复剂系统的自修复水泥基材料研究[J]. 硅酸盐通报, 2020, 39(4): 1057-1063.
[11]	纪荣健;王琪;盛敏;杨建明;傅新雨. 含高镁镍渣粉的磷酸钾镁水泥性能试验研究[J]. 硅酸盐通报, 2020, 39(3): 696-702.
[12]	钱达友;杨建明. 水冻融和硫酸盐溶液冻融环境下MKPC砂浆的耐久性评价[J]. 硅酸盐通报, 2020, 39(2): 359-366.
[13]	张世鹏;铁生年. 微硅粉复合氯氧镁水泥制备与性能研究[J]. 硅酸盐通报, 2020, 39(2): 402-408.
[14]	张爱莲;张林春;俞金艳;高小建. 磷酸镁水泥基材料力学性能研究[J]. 硅酸盐通报, 2020, 39(2): 422-427.
[15]	崔宝栋;关岩;毕万利;滕笑语;梁媛媛;陈英;孟宪章. 不同矿物掺料对硫氧镁水泥耐热性能的影响[J]. 硅酸盐通报, 2020, 39(2): 428-434.

天然沸石粉对氯氧镁水泥耐水性影响研究

Effect of Natural Zeolite Powder on Water Resistance ofMagnesium Oxychloride Cement

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价